• Korean Journal of Materials Research
• /
• v.9 no.1
• /
• pp.35-41
• /
• 1999

In this study we investigated the effects of process variables on the bond strength, and its dependency upon the interfacial chemistry when the joined $ZrO_2$ toughened $Na\beta$"-alumina to $\alpha$-alumina using B$_2$$O_3$-$SiO_2$-Al$_2$$O_3$-CaO glass sealant. We observed that bond strength is mainly determined by the strength of the glass, which, in turn, depends on the glass composition established after joining reaction. Joining at $950^{\circ}C$ for 15min yielded the highest average bond strength of 66MPa. Different types of interfacial reaction seem to occur at each interface. After joining at $950^{\circ}C$ for 15min we found that Ca and Si diffuse much deeper(~15$\mu\textrm{m}$) into the $\beta$"-alumina composite than into the $\alpha$-alumina(<1$\mu\textrm{m}$) as a result of ion exchange reaction and more effective grain boundary diffusion. Thermal expansion coefficient of the glass was found to have changed more closely to those of the $\beta$"-alumina composite and $\alpha$-alumina, which put the glass under a slight compressive stress.ressive stress.

• Journal of Powder Materials
• /
• v.5 no.3
• /
• pp.210-219
• /
• 1998

The W-Cu composite powders were synthesized from W and Cu elemental powders by ball-milling process, and their microstructural changes and sintering behaviors were evaluated. The ball milling process was carried out in a 3-dimensional mixer (Turbula mixer) using zirconic ($ZrO_2$) ball and alumina ($Al_2O_3$) vial up to 300 hrs. The ball-milled W-Cu powders revealed nearly spherical shape. Microstructure of the composite powders showed onion-like structure which consists of W and Cu shells due to the moving characteristic of Turbula mixer. The W and Cu elements in the composite powders milled for 300 hrs were homogeneously distributed, and W grain size in the ball-milled powder was smaller than 0.5 $\mu\textrm{m}$. Fe impurity introduced during ball milling process was very low as of 0.001 wt%. The relative sintered density of ball-milled W-Cu specimens reached about 94% after sintering at $1100^{\circ}C$.

• Korean Journal of Materials Research
• /
• v.31 no.10
• /
• pp.546-551
• /
• 2021

To improve ferroelectric properties of PZT, many studies have attempted to fabricate dense PZT films. The AD process has an advantage for forming dense ceramic films at room temperature without any additional heat treatment in low vacuum. Thick films coated by AD have a higher dielectric breakdown strength due to their higher density than those coated using conventional methods. To improve the breakdown strength, glass (SiO₂-Al₂O₃-Y₂O₃, SAY) is mixed with PZT powder at various volume ratios (PZT-xSAY, x = 0, 5, 10 vol%) and coating films are produced on silicon wafers by AD method. Depending on the ratio of PZT to glass, dielectric breakdown strength and energy storage efficiency characteristics change. Mechanical impact in the AD process makes the SAY glass more viscous and fills the film densely. Compared to pure PZT film, PZT-SAY film shows an 87.5 % increase in breakdown strength and a 35.3 % increase in energy storage efficiency.

• Korean Chemical Engineering Research
• /
• v.43 no.4
• /
• pp.503-510
• /
• 2005

In this research, composite alumina was prepared to add the various promoters by sol-gel method and examined its thermal stability. After sintering at $1,200^{\circ}C$, the thermal stability resulted in following order, $Si{\fallingdotseq}La$ > Ti > $Ba{\fallingdotseq}Ce$ > Y > $Zr{\fallingdotseq}Mg$, in accordance with adding the promoters. Especially in case of silica-added alumina, a phase transformation temperature to ${\alpha}$-alumina increased about $150^{\circ}C$ and after sintering at $1,200^{\circ}C$, it showed to maintain in ${\gamma}$-form and ${\delta}$-form alumina phase. Also it showed an increase of surface area from $3m^2/g$ to $71m^2/g$ compared with pure ${\alpha}$-alumina. In the case of silicaadded alumina, the characterization change of this alumina particle resulted in a delay of phase transformation because Si-O-Al bond was increased when sintered at high temperature. In case of lanthanum-added alumina, there was a sintering delay phenomenon in inter-particles as $LaAlO_3$ structure existed. The existence of lanthanum structure was confirmed by XRD and XPS analysis. It appeared on the alumina surface as $La_2O_3$ structure when it was sintered under $1,000^{\circ}C$, as the perovskite structure of $LaAlO_3$ at above $1,000^{\circ}C$ and as the magneto-plumbite structure of $LaAl_{11}O_{18}$ at above $1,300^{\circ}C$.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2004.08a
• /
• pp.552-554
• /
• 2004

Barrier ribs of plasma display panel (PDP) are glass matrix composite reinforced with alumina particles. Mechanical properties of the ribs are very crucial for the improvement in reliability of the panel as the ribs might fracture during transportation and service. In this study, therefore, the effects of filler type and content on the mechanical properties of the ribs were investigated. The fillers used include $Al_2O_3$, $TiO_2$, $ZrO_2$ and fused silica. The content of the filler was changed from 0 to 40 vol.%. The mechanical properties of the ribs measured were hardness, Young's modulus, fracture toughness, and 3-point bending modulus. The fracture toughness evaluated by micro-Vicker's indentation of the composites, in general, was measured to increase with the content of the filler until the sintered density does not decrease significantly. The improvement, however, was dependent on the type of filler employed.

• Journal of the Korean Ceramic Society
• /
• v.37 no.2
• /
• pp.174-180
• /
• 2000

Y-TZP/mullite composites were prepared by the infiltration of Y-TZP precursor into partially reaction-sintered mullite. The addition of Y-TZP(~7.2 wt%) increased the bend strength(207 MPa), fracture toughness(4.6MPa.m1/2) and Vickers microhardness(853kg/$\textrm{mm}^2$) of the uninfiltrated mullite sintered at 162$0^{\circ}C$ for 10h by more than 75, 70 and 105%, respectively. Residual alumina-rich glass was observed at a mullite/mullite junction, due to the mullitization reaction of silica melt with crystalline $\alpha$-Al2O3 during a final sintering. Although ZrO2 inclusions improved the final sintered density of mullite they did not effectively prevent its grain growth.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.20 no.10
• /
• pp.3234-3242
• /
• 1996

This paper describes experimental results of modified small punch( MSP) test conducted to evaluate the fracure characteristics and mechanical properties of plasma sparayed zirconia ($ZrO_2$ stabilized with 8wt. % $Y_20_3$ : YSZ) NiCrAlY composite. The mixing ratios of YSZ/NiCrAlY were 0/100, 25/75, 50/50, 100/0 v.%. Test temperatures ranged from 293K to 1473K. This study is directed at development of thermal barrrier coating(TBC) system with superior heat resistance and mechanical properties. The microstructure and fracture process of the composite were examined by SEM and AE method. The mechanical properties of 100% YSZ were nearly independent of the temperatures tested in this study. In contrast, the NiCrAlY-containing composites showed a significant decrease of the mechanical properties above 1273K, showing a ductile- brittle transition behavior up to the temperature. Furthermore, it can seen that 25% YSZ/75% NiCrAlY composite gave the highest fracure strength and fracture energy among the mixing ratio tested over the temperature range.

• Journal of Welding and Joining
• /
• v.7 no.2
• /
• pp.25-34
• /
• 1989

The purpose of this work is to coat ZrO$_{2}$ - 8Y$_{2}$O$_{3}$ ceramic on the Al cast alloy(AC-8A) by using the plasma spray method. Two types of coatings which were composed of two and three layer coating were examined. Each coating powder was analyzed for shape and size distribution and X-ray diffraction pattern. For the coated layers, microstructural analysis and performance estimation which was composed of static thermal test, thermal cyclic test and thermal shock test were conducted.

• Korean Journal of Materials Research
• /
• v.17 no.1
• /
• pp.18-24
• /
• 2007

Mullite-PSZ composite was prepared by sol-gel method using $Al(sec-OC_4H_9)_3,\;Si(OC_2H_5)_4,\;ZrOCl_2\;8H_2O\;and\;Y_2O_3$. The sinterability ana mechanical properties of powder compacts sintered at $1,650^{\circ}C$ for 4 hrs were investigated for various PSZ contents. In result Al-Si spinel formed at $980^{\circ}C$ from amorphous dried gel, and zirconia as well as mullite crystal formed above $1,200^{\circ}C$. The sintered body was densified to $97{\sim}98%$ except the specimen containing 25vol% PSZ which showed the relative density of about 95% obtained by sintering at $1,650^{\circ}C$ for 4 h. The flexural strength of the sintered body was a maximum value of 290 MPa in 20 vol% PSZ, which was also considerably larger than the value of 200 MPa without PSZ. The value of the fracture toughness increased linearly with increase of PSZ content and showed a maximum value of $4.3MPam^{1/2}$ in 25 vol% PSZ, Namely this value was remarkably larger than the $value(2.6MPam^{1/2})$ of pure mullite without PSZ.

• Journal of the Korean Ceramic Society
• /
• v.38 no.9
• /
• pp.834-838
• /
• 2001

Attempts were made to improve mechanical properties of zirconia-based electrolyte by preparing yttria-stabilized cubic zirconia/alumina composite. It was performed by precipitating Yag precursor in aqueous m-zirconia slurry. The powder was separated and then followed by heat treatment with expecting yttria to react with m-$ZrO_2$ to give yttria stabilized zirconia and alumina to be dispersed homogeneously. When 17.8wt% Yag(6.3mol% $Y_2O_3$) was used, fracture toughness and strength were substantially improved from 1.44MPa${\cdot}m^{1/2}$ and 270Mpa for YZ8Y to 3.62MPa${\cdot}m^{1/2}$ and 447MPa respectively, but electrical conductivity at $^{\circ}$C in air was decreased from 0.126 to 0.057${\Omega}^{-1}cm^{-1}$. It seemed due to the presence of small amount of tetragonal zirconia. But when 21.58wt% Yag(8.0mol% $Y_2O_3$) was added, fracture toughness of 2.93MPa${\cdot}m^{1/2}$ and flexural strength of 388MPa were obtained with electrical conductivity of ${\Omega}^{-1}cm^{-1}$.