• Journal of the Korean Ceramic Society
• /
• v.33 no.2
• /
• pp.143-148
• /
• 1996

• Journal of the Korean Chemical Society
• /
• v.30 no.5
• /
• pp.415-422
• /
• 1986

The metal-support interaction of copper oxide supported on ${\gamma}$-alumina and silica was studied by X-ray diffraction (XRD) and temperature-programmed reduction(TPR). It was found that XRD pattern of CuO can not be observed up to 5.0wt % copper content for CuO/${\gamma}-Al_2O_3$ while CuO/$SiO_2$ sample shows the CuO pattern even at 2.5wt% copper content. $H_2-$TPR of CuO/${\gamma}-Al_2O_3$ system shows four major peaks at 145${\circ}C$, 185${\circ}C$, 210${\circ}C$, and 250${\circ}C$. In the case of CuO/$SiO_2$, a large peak at 250${\circ}C$ was appeared accompanying a small peak at 425${\circ}C$. Comparing the TPR peaks with that of copper aluminate which was prepared from the calcination of CuO/${\gamma}-Al_2O_3$ at 1000${\circ}C$, the peaks at around 145${\circ}C$, 200${\circ}C$ (185${\circ}C$ and 210${\circ}C$), and 250${\circ}C$ were corresponded to $Cu^+$ ion in CuO interacting ${\gamma}-Al_2O_3$, $Cu^+$ ions in defect sites of ${\gamma}-Al_2O_3$ and $Cu^{2+}$ ion in the bulk CuO layer, respectively. From the results, it was concluded that there is considerable metal-support interaction in CuO on ${\gamma}-Al_2O_3$ and the interaction results in a stabilization of $Cu^+$ ion in the system.

• Applied Chemistry for Engineering
• /
• v.35 no.1
• /
• pp.1-7
• /
• 2024

Mn-M/Al₂O₃ (M = Cu, Fe, Co, and Ce) catalysts were prepared for simultaneous oxidation of NO, CO, and CH₄, and their oxidation activities were compared. The Mn-Cu/ Al₂O₃ catalyst with the best simultaneous oxidation activity was characterized by XRD, Raman, XPS, and O₂-TPD analysis. The result of XRD indicated that Mn and Cu existed as complex oxides in the Mn-Cu/Al₂O₃ catalyst. Raman and XPS results showed that electron transfer between Mn ions and Cu ions occurred during the formation of the Mn-O-Cu bond in the Mn-Cu/Al₂O₃ catalyst. The XPS O 1s and O₂-TPD analyses showed that the Mn-Cu/Al₂O₃ catalyst has more adsorbed oxygen species with high mobility than the Mn/Al₂O₃ catalyst. The high simultaneous oxidation activity of the Mn-Cu/Al₂O₃ catalyst is attributed to these results. Gas-phase NO promotes the oxidation reactions of CO and CH₄ in the Mn-Cu/Al₂O₃ catalyst while suppressing the NO oxidation reaction. These results were presumed to be because the oxidized NO was used as an oxidizing agent for CO and CH₄. On the other hand, the oxidation reactions of CO and CH₄ competed on the Mn-Cu/Al₂O₃ catalyst, but the effect was not noticeable because the catalyst activation temperature was different.

• Journal of Powder Materials
• /
• v.7 no.3
• /
• pp.149-153
• /
• 2000

In this study, the fabrication of $Al_2O_3$/5vol.%Cu nanocomposite and its mechanical property were discussed. The nanocomposite powders were produced by high energy ball milling of $Al_2O_3$ and Cu elemental powders. The ball-milled powders were sintered with Pulse Electric Current Sintering (PECS) facility. The relative densities of specimens sintered at $1200^{\circ}C$ and $1250^{\circ}C$ after soaking process at $900^{\circ}C$ were 96% and over 97%, respectively. The sintered microstructures were composed of $Al_2O_3$ matrix and the nano-sized Cu particles distributed on grain boundaries of $Al_2O_3$ matrix. The nanocomposite exhibited the enhanced fracture toughness compared with general monolithic $Al_2O_3$. The toughness increase was explained by the crack deflection and bridging by dispersed Cu particles.

• Environmental Engineering Research
• /
• v.10 no.3
• /
• pp.131-137
• /
• 2005

The catalytic activity of precious metals(Rh, Pd, Pt) and nickel catalysts supported on ${\gamma}-Al_2O_3\;and\;CeO_2$ in the partial combustion of methane(PCM) to syngas was investigated based on the product distribution in a fixed bed now reactor under atmospheric condition and also on analysis results by SEM, XPS, TPD, BET, and XRD. The activity of the catalysts based on the syngas yield increased in the sequence $Rh(5)/CeO_2{\geq}Ni(5)/CeO_2>>Rh(5)/Al_2O_3>Pd(5)/Al_2O_3>Ni(5)/Al_2O_3$. Compared to the precious catalysts, the syngas yield and stability of the $Ni(5)/CeO_2$ catalyst were almost similar to $(5)/CeO_2$ catalyst, and superior to these of any other catalysts. The syngas yield of $Ni(5)/CeO_2$ catalyst was 90.66% at 1023 K. It could be suggested to be the redox cycle of the successive reaction and formation of active site, $Ni^{2-}$ and the lattice oxygen, $O^{2-}$ produced due to reduction of $Ce^{4-}$ to $Ce^{3-}$.

• Journal of the Korean Ceramic Society
• /
• v.37 no.11
• /
• pp.1058-1064
• /
• 2000

연속슬립캐스팅 및 상압소결법으로 $Al_2$O$_3$/ZrO$_2$적층복합체를 제조하였으며, 적층복합체에서 ZrO$_2$층을 단사정, 정방정 및 입방정으로 각각 달리 적층하여 균열생성 및 전파 거동에 미치는 ZrO$_2$상의 영향을 고찰하였다. 균열 생성은 냉각시 $Al_2$O$_3$층과 ZrO$_2$층 간의 열팽창 계수의 차이에 의한 열적불일치응력이 가장 큰 요인으로 작용하였다. 적층체 내에 존재하는 균열은 tetra-ZrO$_2$의 경우 적층두께 조절로 가능하였으며, cubic-ZrO$_2$의 경우는 냉각속도 조절로 균열밀도로 크게 낮출 수 있었다. $Al_2$O$_3$/ZrO$_2$적층체를 구성하는 세가지 ZrO$_2$상(mono, tetra, cubic)들 중에서 cubic-ZrO$_2$가 포함된 적층체의 경우 $Al_2$O$_3$와 ZrO$_2$계면에 형성된 잔류압축응력으로 인한 균열굴절 효과를 얻을 수 있었다.

• Journal of Korea Foundry Society
• /
• v.22 no.2
• /
• pp.75-81
• /
• 2002

The main objectives were to investigate the suitability of CaO crucible for melting TiAl alloys and to develop investment mold for investment casting of TiAl alloys. TiAl alloy specimen were prepared by plasma arc furnace under argon atmosphere. After melting of TiAl alloy using CaO crucible, the results showed that there is little contamination of oxygen in the TiAl bulk. Conventional vacuum induction furnaces can be readily adaptable to produce cast parts of TiAl without high skilled techniques. The determination of optical metallography and microhardness profiles in investment cast TiAl alloy rods has allowed the gradation of the relative thermal stability of the oxides examined. The molds used for the present study were $ZrO_2$, $Al_2O_3$, CaO stabilized $ZrO_2$ and $ZrSiO_4$. Even although high temperature of mold preheating, $Al_2O_3$ mold is a promising mold material for investment casting of TiAl alloys in terms of thermal stability, cost and handling strength. It is important to take thermal stability and preheating temperature of mold into consideration for investment casting of TiAl alloys.

• Resources Recycling
• /
• v.29 no.6
• /
• pp.65-72
• /
• 2020

Black dross is a dark gray dross generated during the aluminum recycling process that uses flux, and contains NaCl, KCl, Al2O3, MgO, etc. Black dross is separated into soluble substances (NaCl, KCl) and insoluble substances (Al2O4, MgO) through the dissolution process. Soluble materials can be reused as salt flux, and Al2O3 and MgO can be upcycled to various ceramic materials through the synthesis process. In this study, Mayenite was synthesized using Al2O3 and MgO recovered from black dross, and the synthesis was performed according to the mixing ratio and reaction temperature. It was confirmed that when Mayenite was synthesized using black dross (spinel) and CaCO3, precursors were changed to Mg0.4Al2.4O4 and CaO at 700 ℃, and to Ca12Al14O33 (Mayenite) after 800 ℃. In the mixing conditions experiment, it was confirmed that the Mayenite XRD peak increased with increase of the CaCO3 content, and the Mg0.4Al2.4O4 XRD peak decreased. As a result of the BET analysis of the synthesized powder, the surface area decreased as the fine particles were grown and agglomerated in the process of generating mayenite.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.226-226
• /
• 2003

The Commercial LiCoO$_2$ particles, which were 7.7${\mu}{\textrm}{m}$ in average diameter, were coated with $Al_2$O$_3$ by a gas suspension spray coating method. The coating amount of $Al_2$O$_3$ on the surface of LiCoO$_2$ was varied from 0.1 to 2 wt.% and compared their electrochemical characteristics with those of bare LiCoO$_2$. $Al_2$O$_3$ coating on the surface of LiCoO$_2$ increased surface area and electrical conductivity, and showed the better cycle and thermal stability even at the higher voltage. The observed optimum A1$_2$O$_3$ coating amount that exhibited the highest capacity retention was 0.2 wt.%.

• Journal of the Korean Ceramic Society
• /
• v.50 no.6
• /
• pp.439-445
• /
• 2013

Both an unreinforced $Al_2O_3$/Al matrix and a ${\alpha}-Al_2O_3$ particulate reinforced composite have been produced by the oxidation of an Al surface doped with NaOH in the absence of any other dopant. Fabrication of the matrix was initiated by the formation of $NaAlO_2$, which provides a favorable surface structure for the matrix formation by breaking the protective $Al_2O_3$ layer on Al. During the matrix growth, the external surface of the growth front was covered with a very thin sodium-rich oxide. A cyclic formation process of the sodium-rich oxide on the growth surface was proposed for the sodium-induced directed metal oxidation process. This process involves dissolution of the sodium-rich oxide, motion of Na to the growth front, and re-formation of the oxide on the surface. Near-net-shape composites were fabricated by infiltrating an $Al_2O_3$/Al matrix into a ${\alpha}-Al_2O_3$ particulate preform, without growth barrier materials. The infiltration distance increased almost linearly in the NaOH-doped preform.