• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2009년도 하계학술대회 논문집
• /
• pp.183-183
• /
• 2009

본 연구에선 ITO에 사용되는 Indium의 양을 줄이기 위해 ITO와 유사한 성질을 보이는 조성인 Indium - Zinc - Tin Turnary compound를 연구하였다. 각 조성은 Indium - Zinc - Tin Turnary compound를 기본으로 하여 Zinc site에 이종원소인 Al2O3와 Ga2O3를 doping함에 따라 변화되는 전기적 특성을 살며보았다. 분석에 사용한 Ceramic pellet은 일반적인 Ceramic process를 거쳐 제작되었다. 각 조성의 전기적 특성은 TCR meter와 Hall effect analyser를 이용하여 측정하였고, X-ray diffraction measurements(XRD), Scanning Electron microscope(SEM)를 이용하여 결정학적 특성을 분석하였다.

• Restorative Dentistry and Endodontics
• /
• 제6권1호
• /
• pp.115-122
• /
• 1980

The corrosion of silver amalgam is regarded as one of major causes in the failures of dental amalgam restorations. To evaluate the corrosion resistance of dental amalgam alloys, electrochemical tests such as potential and polarization measurement were used widely. But these commonly used methods have not provided the sufficient informations on relative resistance of amalgam to corrosion. In this experiment, the corrosion currents were measured using electronic potentiostat to compare some commercial dental amalgam alloys. All alloys were triturated in a amalgamator and condensed into a mold described in A.D.A. Specification No. 1 to produce cylinder form specimens of 4mm diameter by 5mm long. After specimen kept for 1 week at $37^{\circ}C$, each specimen was embedded in epoxy resin. The surfaces of specimens were then polished with a emery paper, diamond dust, and $Al_2O_3$. These specimens were immersed in artifical saliva kept at $37^{\circ}C$, and currents of each specimen were measured for 24 hours at 0.0volt (SCE). The author obtained conclusions as follows: 1. High copper amalgam showed superior resistance against corrosion to conventional amalgam, but a pellet form of high copper amalgam seemed to be susceptible to corrosion. 2. In lathe-cut alloys, fine-cut had superior resistance against corrosion to regular-cut. 3. Non-zinc conventional amalgam alloys were more resistant to corrosion than that of zinc containing conventional amalgam alloys. 4. In both of high copper and conventional amalgams, predispensed forms tended to have better resisitance to corrosion than that of pellet forms.

• 한국전기전자재료학회논문지
• /
• 제17권5호
• /
• pp.467-475
• /
• 2004

ZnO epilayer were synthesized by the pulsed laser deposition(PLD) process on $Al_2$ $O_3$substrate after irradiating the surface of the ZnO sintered pellet by the ArF(193 nm) excimer laser. The epilayers of ZnO were achieved on sapphire(A $l_2$ $O_3$) substrate at a temperature of 400 $^{\circ}C$. The crystalline structure of epilayer was investigated by the photoluminescence and double crystal X-ray diffraction(DCXD). The carrier density and mobility of ZnO epilayer measured with Hall effect by van der Pauw method are 8.27${\times}$$10^{16}$$cm^{-3}$ and 299 $\textrm{cm}^2$/Vㆍs at 293 K, respectively. The temperature dependence of the energy band gap of the ZnO obtained from the absorption spectra was well described by the Varshni's relation, $E_{g}$(T)= 3.3973 eV - (2.69 ${\times}$ 10$_{-4}$ eV/K) $T^2$(T＋463k). After the as-grown ZnO epilayer was annealed in Zn atmospheres, oxygen and vaccum the origin of point defects of ZnO atmospheres has been investigated by the photoluminescence(PL) at 10 K. The native defects of $V_{Zn}$ , $V_{o}$ , Z $n_{int}$, and $O_{int}$ obtained by PL measurements were classified as a donors or accepters type. In addition, we concluded that the heat-treatment in the oxygen atmosphere converted ZnO thin films to an optical p-type. Also, we confirmed that vacuum in ZnO/A $l_2$ $O_3$did not form the native defects because vacuum in ZnO thin films existed in the form of stable bonds.s.s.s.

• 조명전기설비학회논문지
• /
• 제22권12호
• /
• pp.142-149
• /
• 2008

본 논문은 비열평형 플라즈마와 촉매를 이용하여 트리클로로에틸렌의 효과적인 분해방법을 제안하였다. 이를 위하여 이산화망간과 알루미나 펠렛을 플라즈마 리액터 내부에 충진한 리액터를 설계하였다. 이산화망간 충진 리백터를 이용할 경우에는 산소를 포함한 가스중의 방전에 의해 발생된 오존이 촉매 표면에서 분해되는 동안에 발생된 산소원자 라디칼에 의하여 TCE의 분해율이 향상됨을 알 수 있었다. 그리고 알루미나를 충진한 경우에는 TCE DCAC로 산화되었으며, COx 및 $Cl_2$와 같은 저분자상으로 많이 분해되지 않았다. 그러나 알루미나 충진 리액터에 의한 플라즈마 처리된 가스를 리액터 후단에 설치한 이산화망간 촉매를 통과시킴에 의하여 분해율이 매우 향상됨을 알 수 있었다. 따라서, 플라즈마 프로세스에 이산화망간을 응용함에 의하여 오존 분해에 따른 촉매 표면의 산소원자 라디칼에 의하여 TCE 및 분해 생성물(DCAC)를 효율적으로 분해하는 것이 가능하다.

• 청정기술
• /
• 제23권3호
• /
• pp.286-293
• /
• 2017

본 연구는 악취가스 물질(바이오가스의 불순물)의 하나인 $H_2S$를 제거하기 위한 흡착제의 성능을 향상시키기 위해 수행하였다. 기본 담체로서 4가지 물질($Fe_2O_3$, $Ca(OH)_2$, 분말 활성탄, $Al(OH)_3)$을 혼합 사용하여 pellet 형태의 흡착제를 제조하였다. 또한, 4가지 물질의 $H_2S$ 흡착에 미치는 영향을 평가한 결과, $Fe_2O_3$와 분말활성탄은 $H_2S$ 흡착성능이 각각 1.5, 2배로 증가하는 것으로 나타났으며 $Ca(OH)_2$와 $Al(OH)_2$는 $H_2S$ 흡착성능에는 영향이 없는 것으로 나타났다. 또한 4가지 물질을 기본혼합 담체로 한 후, 활성물질로 KI, KOH, $K_2CO_3$를 선정하여 각각 5 wt% 첨가한 후에 $H_2S$ 흡착성능을 시험한 결과 $K_2CO_3$를 첨가한 흡착제가 가장 성능이 우수한 것으로 나타났다. 또한 $K_2CO_3$를 5 ~ 30 wt%까지 변화시키면서 흡착성능을 확인한 결과, $K_2CO_3$ 함량이 20 wt%까지는 함량과 비례하여 $H_2S$ 흡착성능이 증가하는 것을 확인할 수 있었으나 30 wt%에서는 $H_2S$ 흡착성능 급격히 떨어지는 것을 확인하였다. 또한 $K_2CO_3$ 첨가 함량에 따른 $H_2S$ 흡착성능을 바탕으로 Thomas model을 이용하여 모델링을 실시한 결과에서도 $K_2CO_3$ 함량이 20 wt%까지는 실험값과 모사값이 잘 일치하고 있음을 보여주었다. 이러한 결과들을 바탕으로, 본 연구에서 확인된 활성물질의 종류와 활성물질의 함량을 흡착제 제조에 이용한다면 $H_2S$ 흡착제의 흡착성능 개선뿐만 아니라 흡착제의 사용수명 증대를 기대할 수 있었다.

• 한국건축시공학회지
• /
• 제23권6호
• /
• pp.663-671
• /
• 2023

본 연구에서는 목질계 바이오매스(Bio-SRF, 우드펠릿)를 연료로 사용하는 발전소 3곳에서 배출된 4종의 목질계 플라이애시(FA)의 재활용성을 실험적으로 검토하였다. FA의 물리 분석(입형, 입도분포, 분말도, 밀도)과 화학 분석(화학조성, 중금속 함량)을 수행하였고, KS L 5405에 준하여 혼입률 5~20%의 모르타르 시험체를 제작하고 플로우와 압축강도를 측정하였다. 4종의 FA는 입경 약 20~30㎛, 밀도 약 2.3~2.5g/cm³, 분말도 2,600~4,900cm²/g, SiO₂, Al₂O₃, Fe₂O₃, CaO 성분이 약 50~90%를 차지하고 있으며, 염소와 SiO₂ 함량을 배제하고 KS L 5405의 FA 2, 3형과 유사한 특성을 보였다. 모르타르 혼입 평가 결과, 펠릿 연소 FA는 5~20% 혼입 범위에서 모르타르 압축강도는 34~47MPa로 측정되었다. 목질계 연료 100%를 연소한 FA는 혼화재 대체재로서 재활용성이 높다고 평가된다.

• Advances in materials Research
• /
• 제13권3호
• /
• pp.161-171
• /
• 2024

This study aimed to investigate the effect of physicochemical properties and mix ratios of iron ore (oxide feed): coke (reductant) on the carbothermic reductions of iron ore. Coke size was fixed at ≤63 ㎛ while iron ore size varied between 150-63 ㎛ and ≤63 ㎛ respectively. Mix ratios were changed from 100:0 (reference) to 80:20 and 60:40 while the temperature, heating rate and soaking duration in muffle furnace were fixed at 1100 ℃, 10 ℃/min and 1 hour. Particle size analyzer, XRF, CHNS and XRD analyses were used for determination of raw feed characteristics. The occurrence of phase transformations from various forms of iron oxides to iron during the carbothermal reductions were identified through XRD profiles and supported with weight loss (%). XRF analysis proved that iron ore is of high grade with 93.4% of Fe₂O₃ content. Other oxides present in minor amounts are 2% Al₂O₃ and 1.8% SiO₂ with negligible amounts of other compounds such as MnO, K₂O and CuO. Composite pellet with finer size iron particles (≤63 ㎛) and higher carbon content of 60:40 exhibited 45.13% weight lost compared to 32.30% and 3.88% respectively for 80:20 and 100:0 ratios. It is evident that reduction reactions can only occur with the presence of coke, the carbon supply. The small weight loss of 3.88% at 100:0 ratio occurs due to the removal of moisture and volatiles and oxidations of iron ore. Higher carbon supply at 60:40 leads into better heat and mass transfer and diffusivity during carbothermic reductions. Overall, finer particle size and higher carbon supply improves reactivity and gas-solid interactions resulting in increased reductions and phase transformations.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 추계학술대회 논문집
• /
• pp.279-279
• /
• 2007

비휘발성 메모리 Fe-RAM은 빠른 정보처리 속도와 전원공급이 차단되었을 때도 계속 정보를 유지할 수 있는 비휘발성 특징과 더불어 저전압, 저전력 구동의 장점이 있어서, 차세대 메모리로 많은 주목을 받고 있다. FeRAM에 사용되는 강유전체는 주로 Pb(Zr,Ti)$O_3$가 적용되었는데, 최근에는 비납계 강유전체의 연구도 활발히 이루어지고 있다. 이러한 비납계 강유전체 중에서 가장 특성이 우수한 물질은 $(Bi,La)_4Ti_3O_{12}$ (BLT) 이다. 그런데 BLT는 결정 방향에 따른 강한 이방성의 강유전 특성을 나타내기 때문에 BLT 박막을 이용하여 Fe-RAM 소자 등을 제작하기 위해서는 결정의 방향성을 세심하게 제어하는 것이 매우 중요하다. 지금까지 연구된 BLT 박막의 방향성 조절결과를 보면, BLT 박막을 스핀 코팅 법 (spin coating method)으로 증착하고, 핵생성 열처리 단계를 조절하여 무작위 방향성을 갖는 박막을 제조하는 방법이 일반적이었다. 그런데 이러한 스핀 코팅법에서의 핵생성 단계의 제어는 공정 조건 확보가 너무 어려운 단점이 있다. 이러한 어려움을 극복할 수 있는 대안은 스퍼터링 증착법(sputtering deposition method), PLD (pulsed laser deposition)법 등과 같은 PVD (physical vapor deposition) 법의 증착방법을 적용하는 것이다. PVD 법으로 증착하는 경우에는 이미 박막 내에 무수한 결정핵이 존재하기 때문에 핵생성 단계가 필요가 없게 된다. PVD 증착법의 적용을 위해서는 타겟의 제조 및 평가 실험이 선행되어야 한다. 그런데 벌크 BLT 재료의 소결공정 조건과 전기적 특성에 관한 연구 결과는 거의 발표가 되지 않고 있다. 본 실험에서는 $Bi_2O_3,\;TiO_2,\;La_2O_3,\;Nb_2O_5\;and\;Al_2O_3$ 분말들을 이용하여 최적의 조성을 구하기 위하여 $Nb^{+5}$ 와 $Al^{+3}$을 $Ti^{+4}$ 자리에 소량 치환시켜 제조하였다. 혼합된 분말을 하소 후 pellet 형태로 성형하여 소결을 실시하였다. 시편을 1mm 두께로 연마하고, 양면에 silver 전극을 인쇄하여 전기적 특성을 측정하였다. 측정결과 $Ti^{+4}$ 자리에 $Nb^{+5}$를 치환하여 제조한 시편에서 $2P_r{\sim}31\;{\mu}c/cm^2$정도의 매우 우수한 특성을 얻었다.

• 약학회지
• /
• 제30권1호
• /
• pp.31-41
• /
• 1986

Sarcolemmal membrane fraction from canine ventricle was isolated from the discarded pellet after the first homogenization in the isolation procedure of sarcoplasmic reticulum (Method 1) and the protein yield, purity, and sidedness of this preparation were compared to those of sarcolemmal fraction prepared by method of Lee et al. (Method 2) and a slight modification of original protocol of Jones et al. (Method 3). Method 1 differed from Method 2 essentially only in that vigorous homogenization was carried out by omnimixer and homogenization medium containing 30mM Tris-maleate was used in the first step. The sarcolemmal fraction was enriched from 45 to 50 and 29-fold in [$^3H$] ouabain, [$^3H$] DHA, [$^3H$] QNB binding and $Na^+$, $K^+$-ATPase activity, respectively, compared to homogenate. Total $Na^+$, $K^+$-ATPase activity of highly sarcolemma enriched fraction was 144.6$\pm$16.4$\mu\textrm{mol}$ Pi/mg protein/hr, which was about 85%, of total ATPase activity, and the yield of the preparation was 15.7 mg protein per 100g of starting ventricular tissue. The sarcolemmal preparation supported $^{45}Ca^{2+}$-uptake in the presence of ATP but this uptake was not dependent on oxalate. Sarcolemmal $Na^+$, $K^+$-ATPase activity and detectable [$^3H$] ouabain binding were increased about 32% and 35%, respectively, by pretreatment of sarcolemmal fraction with optimal concentration of sodium dodecylsulfate (0.3-0.4mg/mg protein), suggesting that this preparation contained about 24% of sealed rightside-out vesicles, 26% of sealed inside-out vesicles, and 5001o of freely permeable (leaky) form. This procedure showed the highest protein yield and leaky population, compared to Method 2 and 3. On the other hand, sarcolemmal fraction prepared by Method 2 and 3 showed low value in protein yield but comtained high population of inside-out (46%) and rightside-out (49%) vesicles, respectively, compared to present procedure (Method 1). The results indicate that vigorous homogenization decreases the population of sealed sarcolemmal vesicles but increases the sarcolemmal protein yield per gram tissue and that this procedure is available for further purification of sarcolemmal fraction and for the receptor binding study of sarcolemma.

• 한국응용과학기술학회지
• /
• 제31권4호
• /
• pp.731-739
• /
• 2014

투명 전도성 산화물로서 알루미늄과 붕소가 함께 도핑된 아연산화물(AZOB)이 $900^{\circ}C$에서 분무 열분해법에 의해 제조되었다. 얻어진 마이크론 크기의 AZOB 분말은 알루미늄, 붕소 및 아연의 수용액으로부터 얻어진다. 분무 열분해로 얻어진 마이크론 크기의 AZOB 분말은 $700^{\circ}C$에서 두 시간동안의 후 소성 과정과 24 시간 동안의 볼 밀링을 통해 나노 크기의 AZOB으로 변환된다. AZOB을 구성하는 일차 입자의 크기를 Debye-Scherrer 식에 의해 계산하였고 압축된 AZOB 펠렛의 표면 저항을 측정하였다.