• 한국세라믹학회지
• /
• 제27권6호
• /
• pp.755-762
• /
• 1990

The tungsten paste was printed on the surface of 92% alumina sheet which was made by type casting process. The printed tungsten was bonded on the Al2O3 by co-firing in reducing atmosphere. During the co-firing, the binder burn-out was easier in wet H2 atmosphere than in dry H2, which affected sintered density. In practically, the use of wet H2 above 100$0^{\circ}C$ was beneficial for density of alumina and bond strength. This phenomena occured more distinctly when atmosphere varied from dry H2 to wet H2 than varied dew point in wet H2. In wet H2, the improvement in bonding strength can be attributed to good glass migration into the metal layer due to inhibition of the tungsten particle growth, with increase of alumina density, at the temperatrue higher than 100$0^{\circ}C$.

• 한국세라믹학회지
• /
• 제40권10호
• /
• pp.1005-1014
• /
• 2003

알칼리 자극제의 종류에 따른 고로수쇄슬래그의 수화 및 물리적 특성을 조사하였다 활성화제는 $Na_2$SiO$_3$, $Na_2$CO$_3$, NaOH, $Na_2$SO$_4$를 사용하였고, $Na_2$SiO$_3$, $Na_2$CO$_3$, $Na_2$SO$_4$는 $Na_2$O, NaOH는 $\frac{1}{2}$$Na_2$O로 환산하여 1, 3, 5, 7 wt%를 첨가한 후 W/S=0.5로 실험을 실시하였다. 또한, 압축강도 실험은 OPC에 대해 각각 30 wt% 첨가하여 실험을 하였다. 활성화제의 종류에 따라 주요 수화생성물은 C-S-H, $C_4$AH$_{13}$, AFt, Al(OH)$_3$ 등이었으며, $Na_2$CO$_3$의 경우가 가장 큰 슬래그의 수화율을 보였다. $Na_2$SO$_4$를 사용하였을 때 압축강도가 가장 크게 나타났다.

• Transactions on Electrical and Electronic Materials
• /
• 제7권2호
• /
• pp.72-75
• /
• 2006

Ferroelectric PZT heterolayered thick films were fabricated by the alkoxide-based sol-gel method. PZT(Zr/Ti=60/40) paste was made and alternately screen-printed on the $Al_2O_3$ substrates. We have introduced a press-treatment to obtain a good densification of screen printed films. The porosity of the thick films was decreased with increasing the applied pressure and the thick films pressed at $0.6ton/cm^2$ showed the dense microstructure and thickness of about $76{\mu}m$. The relative dielectric constant increased with increasing the applied pressure. The remanent polarization and coercive field increased with increasing applied pressure and the values for the PZT thick films pressed at $0.6ton/cm^2$ were $16.6{\mu}C/cm^2$, 76.9 kV/cm, respectively.

• 한국세라믹학회지
• /
• 제47권5호
• /
• pp.381-386
• /
• 2010

Some basic properties of inorganic coatings hardened by the room temperature reaction with alkalies were examined. The coating paste was prepared from the powders in the system $Al_2O_3-SiO_2$-CaO using blast furnace slag, fly ash and amorphous ceramic fiber after mixing with a solution of sodium hydroxide and water glass. The mineralogical and morphological examinations were performed for the coatings prepared at room temperature and after heating to $1200^{\circ}C$ respectively. The binding force of the coating hardened at room temperature was caused by the formation of fairly dense matrix mainly composed of oyelite-containing amorphous phase formed by the reaction between blast furnace slag and alkali solution. At the temperature, fly ash and ceramic fiber was not reacted but imbedded in the binding phase, giving the fluidity to the paste and reinforcing the coating respectively. During heating up to $1200^{\circ}C$, instead of a break in the coating, anorthite and gehlenite was crystallized out by the reaction among the binding phase and unreacted components in ternary system. The crystallization of these minerals revealed to be a reason that the coating maintains dense morphology after heating. The maintenance of binding force after heat treatment is seemed to be also caused by the formation of welldispersed fiber-like mineral phase which is originated from the shape of the amorphous ceramic fiber used as a raw materials.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 추계학술대회 논문집 Vol.18
• /
• pp.200-201
• /
• 2005

PFerroelectric PZT heterolayered thick films were fabricated by the alkoxide-based sol-gel method. PZT(40/60) and PZT(60/40) paste were made and alternately screen-printed on the $Al_2O_3$ substrates. We have introduced a press-treatment to obtain a good densification of screen printed films. The porosity of the thick films were decreased with increasing the applied pressure and the thick films pressed at 0.6 ton/$cm^2$ showed the dense microstructure and thickness of about 76${\mu}m$. The remanent polarization and coercive field increased with increasing applied pressure and the values for the PZT thick films pressed at 0.6 ton/$cm^2$ were 17.04${\mu}Ccm^2$, 78.09 kV/cm, respectively.

• 센서학회지
• /
• 제18권3호
• /
• pp.202-206
• /
• 2009

Flat type catalytic combustible hydrogen sensors were fabricated using platinum micro-heaters and sensing material pastes. The platinum micro-heater was formed on an alumina substrate by sputtering method. The paste for the sensing materials was prepared using ${\gamma}-Al_2O_3$ 30 wt%, $SnO_2$ 35 wt%, and Pd/Pt 30 wt% and coated on the platinum micro-heater. The sensing performances were tested for the prepared sensors with different substrate sizes. The micro catalytic combustible hydrogen sensors showed quick response time, high reliability, and good selectivity against various gases(CO, $C_3H_8,\;CH_4$) at low operating temperature of $156^{\circ}\C$.

• Advances in concrete construction
• /
• 제3권1호
• /
• pp.71-90
• /
• 2015

In order to investigate the feasibility and advantage of tuff used as pozzolan in cement-based composite, the representative specimens of tuff were collected, and their chemical compositions, proportion of vitreous phase, mineral species, and rock structure were measured by chemical composition analysis, petrographic analysis, and XRD. Pozzolanic activity strength index of tuff was tested by the ratio of the compression strength of the tuff/cement mortar to that of a control cement mortar. Pozzolanic reaction degree, and the contents of CH and bond water in the tuff/cement paste were determined by selective hydrochloric acid dissolution, and DSC-TG, respectively. The tuffs were demonstrated to be qualified supplementary binding material in cement-based composite according to relevant standards. The tuffs possessed abundant $SiO_2+Al_2O_3$ on chemical composition and plentiful content of amorphous phase on rock texture. The pozzolanic reaction degrees of the tuffs in the tuff/cement pastes were gradually increased with prolongation of curing time. The consistency of CH consumption and pozzolanic reaction degree was revealed. Variation of the pozzolanic reaction degree was enhanced with the bond water content and relationship between them appeared to satisfy an approximating linear law. The fitting linear regression equation can be applied to mutual conversion between pozzolanic reaction degree and bond water content.

• 한국세라믹학회지
• /
• 제24권1호
• /
• pp.77-85
• /
• 1987

Hardened cement paste is mainly affected by corrosion of sulphate and chlorine ions in sea water. In this investigation, many specimens were made with the cement clinker minerals such as C3S, C3A, C4AF and their mixture according to cement composition added various blending materials. After the specimens were immersed in 4% MgSO4 and MgCl2 solutions, the product of reaction, the microstructure of specimen and Ca+2 ion leached in the solution were studied. The formation of Ca(OH)2 in the specimen of C3S is reduced relatively by adding pozzolanic admixtures. The chlorine ion is easily diffuse into the C3S specimen and produced CaCl2 compound, and it makes the specimen porous by leaching out itself into the solution. The specimen of C3A, C4AF are broken down by expanding reaction of ettringite and gypsum compound produced in the MgSO4 solution. At a later period, the ettringite is transformed into gypsum and 5MgO.2Al2O3·15H2O. The C3A in the MgCl2 solution combines chlorine ion to form Friedel's salt and prevents the diffusion reaction of chlorine ion into the specimen. Granulated slag shows inferior effect on the resistance of the specimen in MgSO4 solution by forming ettringite and gypsum, but good result in MgCl2 solution. Pozzolanic materials, on the whole, offer noticable effect on the resistance of the specimen in both solutions.

• 대한치과보철학회지
• /
• 제35권1호
• /
• pp.221-243
• /
• 1997

The objective of this study was to characterize the mechanical properties of $Y_{2}O_{3}$-containing glass infiltrated ceramic core material, which was made by pressureless powder packing method. A pure alumina powder with a grain size of about $4{\mu}m$ was packed without pressure is silicon mold to form a bar shaped sample, and applied PVA solution as a binder. Samples were sinterd at $1350^{\circ}C$ for 1 hour. After cooling, $Y_{2}O_{3}$-containing glass($SiO_{2},\;Y_{2}O_{3},\;B_{2}O_{3},\;Al_{2}O_{3}$, ect) was infiltrated to the sinterd samples at $1300^{\circ}C$ for 2 hours and cooled. Six different proportions $Y_{2}O_{3}$ of were used to know the effect of the mismatch of the thermal expansion coefficient between alumina powder and glass. The samples were ground to $3{\times}3{\times}30$ mm size and polished with $1{\mu}m$ diamond paste. Flexural strength, fracture toughness, hardness and other physical properties were obtained, and the fractured surface was examined with SEM and EPMA. Ten samples of each group were tested and compared with In-Ceram(tm) core materials of same size made in dental laboratory. The results were as follows : 1. The flexural strengths of group 1 and 3 were significantly not different with that of In-Ceram, but other experimental groups were lower than In-Ceram. 2. The shrinkage rate of samples was 0.42% after first firing, and 0.45% after glass infiltration. Total shrinkage rate was 0.87%. 3. After first firing, porosity rate of experimental groups was 50%, compared with 22.25% of In-Ceram. After glass infiltration, porosity rate of experimental groups was 2%, and 1% in In-Ceram. 4. There was no statistical difference in hardness between two materials tested, but in fracture toughness, group 2 and 3 were higher than In-Ceram. 5. The thermal expansion coefficients of experimental groups were varied to $4.51-5.35{\times}10^{-6}/^{\circ}C$ according to glass composition, also the flexural strengths of samples were varied. 6. In a view of SEM, many microparticles about $0.5{\mu}m$ diameter and $4{\mu}m$ diameter were observed in In-Ceram. But in experimental group, the size of most particles was about $4{\mu}m$, and a little microparticles was observed. The results obtained in this study showed that the mismatch of the thermal expansion coefficients between alumina powder and infiltrated glass affect the flexural strength of alumin/glass composite. The $Y_{2}O_{3}$-containing glass infiltrated ceramic core made by powder packing method will takes less time and cost with sufficient flexural strength similar to all ceramic crown made with slip casting technique.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2013년도 춘계 학술논문 발표대회
• /
• pp.313-314
• /
• 2013

The study carried out the experiment with presenting as the fundamental data for developing non-cement by using red mud generated in blast furnace slag and bauxite generated in the process of manufacturing the pig iron process of manufacturing Al(OH)₃/Al₂O from as the binding material using the accelerator of NaOH. After fixing the thing and the NaOH adding the blast furnace slag and NaOH 10, 20, 30 (%) with 10, 20, 30 (%) substituted the red mud in the blast furnace slag and the experimental method carried out the experiment. And it measured the flexural strength and compressive strength and took a photograph EDS analysis and SEM. Consequently, the compressive strength was improved as the addition rate of the NaOH was high and the compressive strength according to the replacement ratio of the red mud was degraded. This is determined that film of the blast furnace slag is destroyed and it makes the hydration reaction condition and the intensity is revealed.