• 한국세라믹학회지
• /
• 제28권1호
• /
• pp.11-18
• /
• 1991

A precipitation method, one of the most effective liquid phase reaction methods, was adopted in order to prepare high-tech Al2O3/ZrO2 composite ceramics, and the effects of stress-induced phase transformation of ZrO2 on thermal shock behavior of Al2O3-ZrO2 ceramics were investigated. Al2(SO4)3.18H2O, ZrOCl2.8H2O and YCl3.6H2O were used as starting materials and NH4OH as a precipitation agent. Metal hydroxides were obtained by single precipitation(process A) and co-precipitation(process B) method at the condition of pH=7, and the composition of Al2O3-ZrO2 composites was fixed as Al2O3-15v/o ZrO2(+3m/o Y2O3). Critical temperature difference showing rapid strength degradation by thermal shock showed higher value in Al2O3/ZrO2 composites(process A : 20$0^{\circ}C$, process B : 215$^{\circ}C$) than in Al2O3(175$^{\circ}C$). The improvement of thermal shock property for Al2O3/ZrO2 composites was mainly due to the increase of strength at room temperature by adding ZrO2. The strength degradation was more severe for the sample with higher strength at room temperature. Crack initiation energies by thermal shock showed higher values in Al2O3/ZrO2 composites than in Al2O3 ceramics due to increase of fracture toughness by ZrO2.

• 한국재료학회지
• /
• 제4권2호
• /
• pp.159-165
• /
• 1994

순수한 알루미늄을 양극산화한 $AI_2O_3/AI$ 소자 및 그 위에$SnO_2$를 증착, 소자를 제작하여 그들의 전기적인 특성을 여러 습도 분위기 중에서 조사하였다. 단위습도당의 표면저항 변화는 $AI_2O_3/AI$ 소자에서는 $1.40 \times 10^{-2}\Omega$ /RH이었다. 두 소자는 습도에 따른 표면저항 변화중에서 hysteresis현상을 나타내고 있지만, $SnO_2-AI_2O_3/Al$ 소자쪽이 더 작은 hysteresis현상을 나타내었다. $SnO_2-AI_2O_3/Al$ 소자에 있어서 표면저항에 대한 온도의존성은 40-$60^{\circ}C$에서 $2.50 \times 10^{-2} \Omega /^{\circ}C$인것에비해 0~$20^{\circ}C$에서는 $0.56 \times 10^{-2} \Omega /^{\circ}C$와 같이 적기 때문에 $SnO_2-AI_2O_3/Al$ 소자는 실온영역에서 습도센서로 쓸 수 있다고 결론할 수 있다.

• 한국자기학회지
• /
• 제16권6호
• /
• pp.283-286
• /
• 2006

고밀도 자기기록용 Ba-페라이트/$SiO_{2}$ 자성박막에서 계면확산 장벽으로써 ${\alpha}-Al_{2}O_{3}$ 버퍼층의 역할을 연구하였다. 열처리동안 $1900{\AA}$의 두께를 가진 비정질 Ba-페라이트/$SiO_{2}$ 박막에서 계면확산은 약 $700^{\circ}C$에서 일어나기 시작하였다. 열처리온도를 $800^{\circ}C$까지 증가시켰을 때, 계면확산은 자기특성을 저하시킬 정도로 급격히 진행되었다. 고온에서의 계면확산을 억제하기 위하여, $110{\AA}$ 두께의 ${\alpha}-Al_{2}O_{3}$ 버퍼층을 Ba-페라이트/$SiO_{2}$ 박막의 계면에 증착하여 사용하였다. Ba-페라이트/${\alpha}-Al_{2}O_{3}/SiO_{2}$ 박막에서는 $800^{\circ}C$의 고온까지 열처리하여도 계면확산이 심각하게 일어나지는 않았다. ${\alpha}-Al_{2}O_{3}$ 버퍼층에 의하여 계면확산이 억제되기 때문에 Ba-페라이트 자성박막의 포화자속밀도와 보자력이 향상되었다. 따라서 Ba-페라이트/$SiO_{2}$ 박막의 계면에서 ${\alpha}-Al_{2}O_{3}$ 버퍼층은 $SiO_{2}$ 기판 성분의 계면확산 장벽으로 사용될 수 있다.

• 한국세라믹학회지
• /
• 제29권3호
• /
• pp.223-231
• /
• 1992

CaO and ZnO were added to Al2O3-SiO2 binary system respectively as flux, then ZrO2 and TiO2 were applied as nucleating agent to these CaO-Al2O3-SiO2 and ZnO-Al2O3-SiO2 ternary system glass. The transparency could not be kept in CaO-Al2O3-SiO2 system glass, whereas the transparent glass-ceramics were prepared in ZnO-Al2O3-SiO2 system glass containing ZrO2 as the nucleating agent. At this time the optimum heating temperatures for the nucleation and the crystal growth were 78$0^{\circ}C$ and 97$0^{\circ}C$. The sizes of the precipitated crystals in the transparent glass-ceramics were below 0.1 ${\mu}{\textrm}{m}$, and their light transmissibilities were more than 80%.

• 한국세라믹학회지
• /
• 제19권3호
• /
• pp.179-186
• /
• 1982

This research is to aim at the study of sintering mechanism through the observation of microstructure by scanning electron microscopy, after the mixture of 30wt% $Al_2O_3$ (White Alundum) powder is fired in air at the temperature range of 1350~150$0^{\circ}C$ in order to sinter $Al_2O_3$-Al through the oxidation of Al powder. The results obtained in this experiment are as follows: 1. While the compressive strength of $Al_2O_3$(WA) body fired at $1450^{\circ}C$ for 5hrs in air is 150kg/$\textrm{cm}^2$, that of Al-$Al_2O_3$ body fired at 135$0^{\circ}C$, $1400^{\circ}C$ for 5hrs in air is 1100kg/$\textrm{cm}^2$, 1600kg/$\textrm{cm}^2$ respectively, and the higher the firing temperature, the more the compressive strength increases. These results from the sintering effect between $Al_2O_3$(WA) grains and surrounding Al-oxidation layer. 2. While the compressive strength of Al2O3(WA) body fired at 150$0^{\circ}C$ for 5hrs in air is 250kg/$\textrm{cm}^2$, the compressive strength of Al-$Al_2O_3$body fired under the same condition is 2050kg/$\textrm{cm}^2$ and water absorption 9.0%, porosity 23.3%, bulk density 2.60gr/$cm^3$. It is assumed that these results come from not only the grain growth of oxidized Al grains but also the increase of bonding strength between $Al_2O_3$(WA) grains.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2008년도 추계학술대회 논문집 Vol.21
• /
• pp.195-195
• /
• 2008

CAS계 유리에 $CaCO_3-Al_2O_3$ 혼합물 및 화합물을 10, 30 wt% 첨가하여 저온 소걸 및 마이크로파 유전 특성을 고찰하였다. CAS계 유리의 연화온도는 $841^{\circ}C$ 이며, CAS계 유리에 $CaCO_3$ 와 30 wt%의 $CaCO_3-Al_2O_3$ 혼합물을 melting되며, 10 wt%의 $CaCO_3$, $Al_2O_3$, $1CaCO_3-1Al_2O_3$ 혼합물 및 $CaAl_2O_4$ 화합물를 10 wt% 첨가하였을 때 $900^{\circ}C$ 이하에서 소걸이 가능하였다. 복합체의 XRD 상 분석 결과, CaCO3를 첨가하였을 때에는 모든 조성이 비정질을 나타내었고, $Al_2O_3$와 $1CaCO_3-1Al_2O_3$ 혼합물은 $Al_2O_3$ 결정상이 생성되었고, $CaAl_2O_4$ 화합물은 $CaAl_2Si_2O_8$의 hexagonal와 anorthite 결정상이 생성되었다. 따라서 CAS-10 (A, C-A, CA) 복합체는 $900^{\circ}C$에서 각각 유전율 ($\varepsilon_r$) 6.4, 6.9, 5.15 와 품질계수 ($Q^*f$) 2,400, 1,500, 3,000의 마이크로파 유전 특성을 나타내어 LTCC 기판 재료로 사용이 가능하며, 특히 $CaAl_2O_4$ 화합물을 사용하였을 때 가장 우수한 유전 특성을 나타내는 것을 확인하였다.

• Composites Research
• /
• 제12권3호
• /
• pp.36-44
• /
• 1999

In-situ process에 의한 $Al_2O_{3p}/Al$기 복합재료 제조시, Mg의 첨가형태와 함량, 공정온도 및 유지시간이 응용Al의 침투거동과 미세조직 및 경도에 미치는 영향을 조사하였다. Mg분말과 $Al_2O_3$입자의 혼합분말에 순 Al을 침투시켜 복합재를 제조하는 경우, 침투율에 영향을 주는 가장 유력한 변수는 Mg분말의 함량이며, Mg의 활발한 반응으로 $700^{\circ}C$의 낮은 온도에서도 침투가 가능했다. 한편 Al-Mg합금을 $Al_2O_3$입자에 침투시켜 복합재를 제조하는 경우 Mg함량과 공정온도에 관계없이 거의 동일한 침투율을 나타냈으며 침투 가능한 공정온도는 $800^{\circ}C$이었다. Mg과 $Al_2O_3$의 혼합분말로 제조한 복합재가 Al-Mg합금으로 제조한 복합재 보다 월등히 높은 경도를 나타냈으나, 과도한 계면방응에 의한 불균일한 강화상의 분산으로 경도의 산포도는 컸다.

• 시멘트
• /
• 통권51호
• /
• pp.20-30
• /
• 1973

1) electron-microprobe를 응용하여 $CaO-SiO_2-Al_2O_3$ 계에서 생성한 $C_2S$, $C_3S$ 에 존재하는 sulfate의 solid, solution을 정량적으로 구할 수 있었으며 이 결과로 $C_2S$ 에 $Al_2O_3$, $SO_3$ 등이 solid soln 등으로 침적되고 이들이 $C_3S$의 생성을 억제한다는 mechanism이 확인되었다. 2) phase equilibrium(상평형)에 의하면 $Na_2SO_4$, $K_2SO_4$는 mineralizer로서 작용하며 $C_3S$ 의 생성을 돕는다. 그러나 $K_2SO_4$ 와 $Al_2SO_3$ 가 결합상태로 존재할 경우는 1,400 $^{\circ}C$에서 광범위한 liquid를 생성하며 quenching하면 glass질과 $\beta-C_2S$ 만이 얻어지고 $C_3S$ 는 생성되지 않는다. 또 이를 1,250 $^{\circ}C$ 까지 서냉하면 $C_2S$ 와 Ca, K, Al, S, 등을 함유한 새로운 물질이 생성된다. 3) $CaO-SiO_2-Al_2O_3-Fe_2O_3$ 계에서 $C_3S$ 의 생성에 미치는 $Na_2SO_4$, $K_2SO_4$ 의 영향을 실험실적으로 검토한 결과 complex interaction이 확인되었으며 $Na_2SO_4$ 는 어떤 경우에는 mineralizing effect를 상실한다는 재미 있는 사실이 발견되었다.

• 한국세라믹학회지
• /
• 제31권12호
• /
• pp.1475-1482
• /
• 1994

Compositionally triphasic boehmite-silica-zirconia composite gels were prepared by a multiphasic sol-gel route. Phase-formation characteristics and densification behavior of the gel compacts were examined with and without $\alpha$-Al2O3 seeding. In the unseeded triphasic gels, both $\alpha$-Al2O3 and mullite crystallize simultaneously at 130$0^{\circ}C$. On the other hand, the $\alpha$-Al2O3 seeding selectively induces the formation of corundum phase ($\alpha$-Al2O3) at a significantly lower temperature (~110$0^{\circ}C$) and facilitates an epitaxial growth of $\alpha$-Al2O3 between 1100~130$0^{\circ}C$. The densification of alumina-mullite-zirconia composite (derived from the triphasic gels) was also enhanced by the $\alpha$-Al2O3 seeding, and this was attributed to the delayed crystallization of mullite in the $\alpha$-Al2O3 seeded gel.

• 한국세라믹학회지
• /
• 제31권10호
• /
• pp.1169-1175
• /
• 1994

Five Al2O3/SiC/metal composites with four different particle sizes of green SiC abrasive grains are grown by the directed oxidation of an commercially available Al-alloy. Oxidation was conducted in air at 100$0^{\circ}C$, 96 hours long. Slip casted SiC-fillers were placed on the alloy or SiC powder deposited up to the required layer thickness. Their microstructures are described and measurements of density, elastic constants, frexural strength, fracture toughness and work of fracture are reported. The results are compared with those of commercial dense sintered Al2O3. The properties of produced materials have a strong relationship to not only the properties of Al2O3, SiC, Al and Si but also to the phase share and phase distribution. The composite materials are dense (0.5% porosity), tough (KIC = 3.4~6.4 MPa{{{{ SQRT { m} }}), strong ({{{{ sigma }}B = 170~345 MPa) and reasonably shrinkage free producible. The reinforcements is attained mainly through the plastic deformation of ductile metal phase.