• 한국세라믹학회지
• /
• 제23권3호
• /
• pp.1-8
• /
• 1986

The preparation and electrical conductivity of $\beta$-$Al_2O_3$ are investigated as a function of $Na_2O$ content from the-oretical composition of $\beta$-$Al_2O_3$ to that of $\beta$"-$Al_2O_3$. $\beta$-$Al_2O_3$ $\beta$"$Al_2O_3$$\alpha$-Al2O3 and ${\gamma}$-NaAlO2 phases appear in the calcined powder at 125$0^{\circ}C$ for 2 hours. The majoity phase is $\beta$-$Al_2O_3$ in sintered specimens at 155$0^{\circ}C$ and 1$650^{\circ}C$ for 30 mins respectively and ${\gamma}$-4NaAlO_2$ phase also exists when Na2O content is over 10.39w/o ${\gamma}$-4NaAlO_2$ phase does not affect the grain growth of $\beta$-$Al_2O_3$ in sintering at 155$0^{\circ}C$ but acts as a reactive liquid for the abnormal grain growth of $\beta$-$Al_2O_3$in sintering at 1$650^{\circ}C$ The electrical conduction of $\beta$-$Al_2O_3$is predominated by 4Na^+$ ion. Contribution of ionic con-ductivity to total conductivity is gradually decreased with increasing temperature at given oxygen pressure and to -tal conductivity is increased by positive hole due to interstitial oxygen with increasing oxygen pressure.

• 센서학회지
• /
• 제7권3호
• /
• pp.218-224
• /
• 1998

ZnO 분말과 $Al_{2}O_{3}$ 분말을 1 : 1의 mole 비로 ball milling 시킨 후, 압착하여 펠렛을 제작하였다. 소성시 분위기를 진공으로 유지하기 위하여 각각 $3{\times}10^{-5}$ Torr의 진공도로 석영관에 봉입한 다음 $900^{\circ}C{\sim}1200^{\circ}C$로 소성하였다. 실험결과, $900^{\circ}C{\sim}1100^{\circ}C$까지는 ZnO, $Al_{2}O_{3}$ 및 $ZnAl_{2}O_{4}$의 혼합구조를 보이다가 $1200^{\circ}C$에서 (311), (220)면등의 주된 피크를 갖는 다결정으로 성장하여 $ZnAl_{2}O_{4}$ 삼원화합물의 구조가 확인되었고, 전자현미경촬영에 의해 화합물의 결정화된 입자들이 관찰되었다. 광흡수측정에 의해 에너지 밴드갭은 약 4.53 eV로 계산되었으며, PL 스펙트럼은 소결온도의 상승에 따라 단파장영역으로 이동하여, $1200^{\circ}C$에서 430nm부근에서 발광피크를 보였다.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2013년도 춘계학술대회 논문집
• /
• pp.114-115
• /
• 2013

$Ti_3AlC_2$ was corroded between 800 and $1100^{\circ}C$ in an Ar-0.2% $SO_2$ gas atmosphere according to the equation: $Ti_3AlC_2+O_2{\rightarrow}rutile-TiO_2+{\alpha}-Al_2O_3$ + (CO or $CO_2$). The scales that formed on the $Ti_3AlC_2$ were thin and rich in ${\alpha}-Al_2O_3$, whose growth rate was exceedingly slow. The $TiO_2$ was present either as the outermost surface scale or a mixture inside the ${\alpha}-Al_2O_3$-rich scale. In the $Ti_3AlC_2$, the activity and diffusivity of Ti were low, whereas those of Al were high. This was the main reason for the superior corrosion resistance of $Ti_3AlC_2$ over TiAl.

• 한국세라믹학회지
• /
• 제35권2호
• /
• pp.129-136
• /
• 1998

The effects of MgO on the resistance to corrosion and oxidation of Al2O3-SiC-C refractory have been in-vestigated. The resistance to oxidation was improved as the amount of MgO increased. The resistance to corrosion was enhanced until 2 wt% MgO content but degraded over that content. From the dependence of temperatuer on the oxidation resistance oxidation was suppressed by the microstructural densification caused by spinel formation over 1200~130$0^{\circ}C$and the formation MgO-Al2O3-SiO2 liguid-phase over 130$0^{\circ}C$ The weight loss of specimens containing MgO with various purity at range of 95 to 99% and par-ticle size of -0.045 mm to -0.074 mm was examined. The oxidation resistance was not changed signficantly with the particle size and purity of MgO powders.

• 한국세라믹학회지
• /
• 제37권4호
• /
• pp.368-375
• /
• 2000

Fracture toughness of particulate composites of Al2O3/SiC, Al2O3/ZrO2 and Al2O3/ZrO2/SiC was analysed theoretically. According to the suggested particle bridging model for obtaining the R-curve height, the crack extension resistance for the long crack was linearly proportional to the residual calmping stress at the interface between the second phase and the matrix. It was also a function of the particle size and the content. It was confirmed that the rising R-curve behavior of Al2O3 containing 30 vol% SiC particles of 3${\mu}{\textrm}{m}$ was owing to the strong crack bridging by SiC particles. For Al2O3/ZrO2/SiC composites, the tensional stress from the 3${\mu}{\textrm}{m}$ SiC particles was large enough to activate the spontaneous transformation of the ZrO2. The crack extension resistance due to the particle bridging mechanism did not seem to be affected much by the coupled toughening, but its resultant toughness increase could be significantly smaller due to the dependency on the matrix toughness.

• 한국결정성장학회지
• /
• 제16권4호
• /
• pp.172-179
• /
• 2006

[ $Al_2O_3-MoO_3$ ]의 혼합물을 환원소성하면 $MoO_3$만 $900^{\circ}C$에서 Mo로 환원되고 $1300^{\circ}C$까지 $Al_2O_3$와 Mo간의 화합물은 형성되지 않았다. $Al_2O_3-MoO_3-MnO_2$, 혼합물의 경우, $900^{\circ}C$에서 먼저 $MnO_2$가 $MoO_3$와 반응하여 중간화합물 $Mn_2Mo_3O_8$를 형성하였다가. $1100^{\circ}C$와 $1300^{\circ}C$에서 $Mn_2Mo_3O_8$ 화합물은 사라지고 새로운 화합물 $MnAl_2O_4$가 생성되었다. $Al_2O_3$와 $MoO_3,\;MnO_2$의 혼합분말 중 Mo만이 선택적으로 환원되는 selective reduction process에 의해 $Al_2O_3/Mo/MnO_2$ 복합재를 제조하였다. $Al_2O_3/Mo$ 복합재의 경우 Mo의 함량이 증가함에도 불구하고 Mo입자가 $Al_2O_3$ matrix의 입성장을 억제하여 평균입경의 변화는 거의 없었다. 파괴강도는 $Al_2O_3$ matrix의 입성장 억제 현상 때문에 Mo의 함량이 증가함에 따라 증가하였다. 경도는 Mo의 낮은 경도값 때문에 약간 감소하였으나 반면에 파괴인성은 증가하였다. $Al_2O_3/Mo/MnO_2$ 복합재의 경우 $MnO_2$는 matrix의 입성장을 촉진시켰고, Mo와 $MnO_2$의 함량이 증가함에 따라 $MnO_2$의 입성장효과 때문에 오히려 낮은 파괴강도를 보였다. 경도는 입계에 존재하는 coalesced Mo 입자들과 matrix의 입성장 때문에 더욱 감소하였으나 반면에 파괴인성은 더욱 증가하는 경 향을 보였다.

• 한국세라믹학회지
• /
• 제33권7호
• /
• pp.832-838
• /
• 1996

Thermite reaction products of MgO and Al were added to MgO-C refractory to improve the properties of corrosion against the attack of slag, oxidation and mechanical spalling. Corrosion rate of MgO-C-MgAl2O4 spinel refractory at the ratio of 3.3(CaO/SiO2) slag was smaller than that of MgO-C and MgO-C-Al refractory. The excellent corrosion resistance of the MgO-C-MgAl2O4 spinel refractory against the slag attack was appeared by Al and MgAl2O4 spinel with high melting point and corrosion resistance and the high thermal conductivity and low thermal expansion of AIN. Hot M.O.R at 140$0^{\circ}C$ and the resistance of oxidation weight loss at 90$0^{\circ}C$ were 210kg/cm2 and -12% respectively.

• 한국세라믹학회지
• /
• 제28권8호
• /
• pp.625-625
• /
• 1991

2wt% Al2O3와 10wt% Al2O3를 첨가하여 2000℃와 2050℃에서 가압소결된 SiC를 37 mol% NaCl과 63 mol% Na2SO4 Salt에 의해 60분까지 hot corrosion을 시켰다. 부식은 SiC표면에 형성된 SiO2층이 Na2O 이온에 의한 basic dissolution에 이해 일어남이 관찰되었고 10wt%의 Al2O3가 함유된 시편은 입계에 Al2O3를 함유한 입계상의 존재로 2wt% Al2O3가 함유된 시편보다 낮은 corrosion rate를 나타냈다. SiC와 산화물층 사이에서 gas bubble의 형성이 관찰되었고 이 gas bubble이 산화물층을 심하게 파괴하기 전까지 corrosion rate은 linear하게 변했다. 부식 양상은 개기공과 입계에서 pitting corrosion에 의해 시작되었다.

• 대한화학회지
• /
• 제30권5호
• /
• pp.415-422
• /
• 1986

${\gamma}-Al_2O_3$와 $SiO_2$에 입혀진 CuO계에서 지지체와 금속과의 상호 작용을 X선 회절법과 승온 환원법으로 연구했다. CuO/${\gamma}-Al_2O_3$계의 CuO X선 회절 피크는 구리의 농도가 약 5.0wt % 이상일 때 관찰될 수 있었으며 CuO/$SiO_2$계에서는 2.5wt%의 구리 함량에서도 볼 수 있었다. CuO/${\gamma}-Al_2O_3$의 수소에 의한 승온 환원 실험에서는 145${\circ}C$, 185${\circ}C$, 210${\circ}C$, 그리고 250${\circ}C$부근에서 네개의 주 피크가 나타났으며 CuO/$SiO_2$의 경우는 425${\circ}C$에서의 작은 피크와 함께 250${\circ}C$에서 큰 피크가 나타났었다. 1000${\circ}C$에서 소성시킨 CuO/${\gamma}-Al_2O_3$의 Cu$Al_2O_4$에 대한 승온 환원 피크들과 145${\circ}C$, 200${\circ}C$ (185${\circ}C$, 210${\circ}C$), 250${\circ}C$ 부근의 피크들을 비교해 보면 그들은 각각 ${\gamma}-Al_2O_3$와 상호작용하는 CuO격자에 있는 $Cu^+$이온, ${\gamma}-Al_2O_3$의 결함 자리들에 존재하는 $Cu^+$이온, 그리고 입자가 큰 CuO층에 있는 $Cu^{2+}$이온에 대응시킬 수 있었다. 이러한 결과들로 부터 CuO/${\gamma}-Al_2O_3$계에서는 지지체와 금속간에 상당한 상호작용이 있으며 이 상호 작용이 CuO/${\gamma}-Al_2O_3$계의 $Cu^{2+}$이온을 안정화 시킴을 알 수 있었다.

• 한국결정성장학회지
• /
• 제7권4호
• /
• pp.610-618
• /
• 1997

반응용침법으로 제조된 $Al_2O_3$/Al 복합재료는 900-$1200^{\circ}C$의 온도범위에서 $Al_2O_3$ 분말성형체에 용융Al을 침투시켜 제조하였다. 용융침투는 각 온도에서 잠복기를 거친후 발생하였으며, 복합재료의 성장속도는 시간에 따라 선형적으로 비례하였다. 제조된 복합재료의 주성분은 $Al_2$O$_3$와 Al이었고 소량의 Si이 탐지되었다. 복합재료의 상대밀도는 $Al_2O_3$ 입자크기가 증가함에 따라 증가하였고 용융 침투온도가 높을수록 감소하였다.