• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2001년도 춘계학술대회 논문집
• /
• pp.807-810
• /
• 2001

Fatigue crack growth tests were carried out using high manganese cast steel under constant amplitude loading. Crystal grain size of the material is about 1000$\mu\textrm{m}$. For this material, the fatigue crack growth mechanism of high manganese steel was clarified from results such as observation of crack growth path and fracture surface. $\Delta$$K_{th}$ is about 8MPa$\surd$m which is quiet large as compared to the general structural steels and the crack growth rate is lower than the general structural steels especilly in the low $\Delta$K regsion. The reason of this behavior is crack closure due to fracture surface roughness.

• 한국해양공학회지
• /
• 제15권2호
• /
• pp.105-110
• /
• 2001

The fatigue crack propagation behavior of the SA516/70 steel which is used for pressure vessels was examined experimentally at room temperature, 150$^{\circ}C $, 250$^{\circ}C $ and 370$^{\circ}C $ with stress ratio of R=0.1 and 0.3. The fatigue crack propagation rate da/dN related with the stress intensity factor range $\Delta K$ was influenced by the stress ratio within the stable growth of fatigue crack(Region II) with an increase in $\Delta K$. The resistance to the fatigue crack growth at high temperature is higher in comparison with that at room temperature, and the resistance attributed to the extent of plasticity-induced by compressive residual stress according to the cyclic loads. Fractographic examinations reveal that the differences of the fatigue crack growth characteristics between room and high temperature are mainly explained by the crack closure and oxide-induced by high temperature.

• 한국안전학회지
• /
• 제9권1호
• /
• pp.161-164
• /
• 1994

Computer aided unloading elastic compliance method was employed to measure the closure and the length of short cracks. The most significant factor that influences the fatigue growth behavior of short cracks is the crack closure Phenomenon. dc/dN-$\Delta$ $K_{eff}$ relationships of short cracks are found to coincide well with the corresponding long crack relationships. Non-propagating behavior of short cracks at notch root can be predicted from the crack opening SIF of short cracks, $K_{op}$ , and the growth equation of long cracks in Region I and II.n Region I and II.I.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2004년도 추계학술대회
• /
• pp.208-213
• /
• 2004

Methods for estimation of the effective stress intensity factor range (${\Delta}K_{eff}$) are evaluated for narrow and wide band random loading crack growth test data of 2024-T351 aluminum alloy. Three methods of determining $K_{op}$, visual measurement, ASTM offset compliance method, and the neural network method proposed by Kang and Song, and three methods of estimating ${\Delta}K_{eff}$, conventional, the 2/PI0 and 2/PI methods proposed by Donald and Paris, are compared in a quantitative manner by using the results of fatigue crack growth life prediction under random loading. For all $K_{op}$ determination methods discussed, the 2/PI0 and 2/PI methods of estimating ${\Delta}K_{eff}$ provide better results than conventional method for narrow and wide band random loading data.

• 한국정밀공학회지
• /
• 제9권1호
• /
• pp.106-117
• /
• 1992

In this study, the propagation behaviour and the closure phenomena of physically small surface cracks were investigated by the techinque of the Kikukawa-unloading elastic compliance method using a back face strain gage. The surface cracks initiated and propagated from notched specimens under constant amplitude bending load. The crack shape (aspect ratio) with approximately semi-circular at the early stage was changed to semi-elliptical as the cracks grew larger. The crack depth (a) could be expressed uniquenly by the crack length (c). The dependence of the crack propagation rate on the stress ratio R was strongly related in the lower ${\Delta}K$ range. The deceleration of the surface crack propagation rate was prominent in lower R during the crack length was small. When the propagation rate was rearranged with the effective stress intensity factor range ${\Delta}$K_{eff} the dependence of the crack propagation rate on the stress ratio R was found to be diminshed. These were caused by the crack closure phenomena that was most prominent at the lower propagation rate. The mechanism of crack closure phenomena was dominated by the plasticity-induced mechanism.

• 대한기계학회논문집
• /
• 제12권2호
• /
• pp.271-277
• /
• 1988

본 연구에서는 항공기, 압력용기 및 지상운송차량 등에 고강도와 용접성이 요구되는 고강도 알류미늄합금 7017T651, 7020T651 및 5083 H115에 대해 균열진전 하한계특성 및 안정 균열진전 하한계특성에 미치는 영향을 고찰 하고자 한다.

• 대한기계학회논문집
• /
• 제16권9호
• /
• pp.1605-1614
• /
• 1992

본 연구에서는 고장력 7075-T73 알루미늄합금에 대하여 변동하중의 기보파형 인 단일과대하중과 고-저(high-low) 블럭하중하의 지연거동에 미치는 과대하중비 %O.L., 기준응력확대계수범위 .DELTA. $K_{b}$ 및 무차원 균열깊이 a/W의 영향을 규명하였 으며, 또한 Wheeler모델의 수정에 의한 예측피로수명을 실험치와 함께 검토하였다.다.

• 한국안전학회지
• /
• 제7권1호
• /
• pp.20-29
• /
• 1992

Effects of strain hardening exponents on the retardation behavior of fatigue crack propagation are experimentally investigated. The retardation of fatigue crack propagation seems to be induced by the crack closure at crack tip. The phenomenon of crack closure becomes remarkable with the increment of strain hardening exponent and magnitude of percent peak load. The ratio of crack growth increment(a$\_$d//w$\_$d/) is influenced by a single overloading (a$\_$d/) and estimated plastic zone size (W$\_$d/=2r$\_$y/) is increased according with the increasing of strain ha.dening exponents. The number of retarded crack growth cycles were (N$\_$d/) decreased as the baseline stress intensity factor .ange( K$\_$b/) was increased. Within the limitation of these experimental results obtained under the single overload, an empirical relation between crack retardation ratio (Nd/N＊), strain hardening exponent (n) and percent peak load (％PL) has been proposed as; Nd/N＊＝ exp [PL $.$ PL$.$A(n)＋B(n) ] where, A(n)＝${\alpha}$n＋${\beta}$, B(n)＝${\gamma}$n＋$\delta$, PL＝％PL/100 and ${\alpha}$＝0.78, ${\beta}$＝0.54, ${\gamma}$＝0.58 and $\delta$＝-0.01, It is interesting to note that all these constants are identical for materials such as aluminum(A3203), steel(S4SC), steel(SS41) and stainless steel(SUS316) used in this experimental study.

• 한국기계가공학회지
• /
• 제3권4호
• /
• pp.88-94
• /
• 2004

High manganese steel was maintained stability of Non-Magnetics performance. Fatigue tests were carried out under constant stress amplitude, using a non-magnetic high manganese steel. The fatigue crack growth mechanism of the high manganese steel was clarified from results such as observation of crack growth path and fracture surface. The result of getting this study was shown as following: 1) Remarkably ${\Delta}Kth$ of the high manganese steel is big with about 3 times of the general steel product. 2) In the low ${\Delta}K$ value region, da/dN is dependent on Kmax, and in the high ${\Delta}K$ value region, it is dependent on ${\Delta}Keff$. The reason of this behavior is crack closure due to fracture surface roughness and fretting oxide. 3) It seems to ease the stress concentration of crack tip crack growth behavior in the ${\Delta}Kth$ vicinity by the generation of the secondary crack.

• 한국해양공학회지
• /
• 제2권2호
• /
• pp.61-70
• /
• 1988

In order to consider the concept of the fitness for purpose'in fatigue design of offshore structure, fracture mechanics is applied to evaluate initial or weld defects. Generally, linear elastic fracture mechanics has been applied to tstimate initial fatigue crack propagation rate as well as long fatigue crack propagation rate. But, initial fatigue crack propagation rate in elasto-plastic notch field may not be characterized by application of stress intensity factor range .DELTA. K, because plastic effect due to stress concentration of notch may contribute to initial crack propagation. Therefore, to introduce the plastic effect into fatigue crack driving force, in this studty, the evaluating method of J-integral range .DELTA. J, was developed by willson was modified for application to notch field. In calculation of .DELTA. J obtained from the modified J-integral, stress gradient and crack closure behavior in the notch field were considered. The initial crack propagation rates in the notch fields of mild steels and high tensile strength steels were correlated to .DELTA. J. As the result, it was cleared that the present .DELTA. J is applicable to charachterize the fatigue crack propagation rates in both the elastic and elasto-plastic notch fields.