• 한국세라믹학회지
• /
• 제38권11호
• /
• pp.1015-1022
• /
• 2001

본 연구에서는 용융염법에 의한 Ba-ferrite의 생성기구와 그 자기적특성에 대해 조사하였다. 출발원료 중 BaC $O_3$만이 용융염내에서 용해도를 가졌으며, 이는 용융염내에서는 Ba-ferrite의 생성이 용해된 $Ba^{2+}$가 F $e_2$ $O_3$나 $\delta$-FeOOH의 표면으로 확산하여 표면반응을 통해 일어나는 것으로 보인다. 한편, 출발물질($\delta$-FeOOH와 F $e_2$ $O_3$)에 따라 생성된 Ba-ferrite가 합성되는 온도는 더 낮은 온도에서 생성됨을 알 수 있었다.

• 한국전기전자재료학회논문지
• /
• 제37권3호
• /
• pp.292-296
• /
• 2024

In this study, Iron (III) oxide-hydroxide (δ-FeOOH) was successfully synthesized using hydrogen peroxide (H₂O₂) as an oxidizing agent. The synthesis of δ-FeOOH was carried out by controlling the amount of H₂O₂, and pure δ-FeOOH was successfully synthesized in ranges from 0.2 mL to 0.6 mL of H₂O₂. The size of the synthesized δ-FeOOH particles was compared by controlling the amount of oxidant H₂O₂. The average particle size of the synthesized pure δ-FeOOH particles increased from 875.1 nm to 897.2 nm as the amount of H₂O₂ was increased. The optical properties of δ-FeOOH synthesized under these specific conditions were investigated. All δ-FeOOH showed a similar trend of increasing and decreasing light absorption from 800 nm to 400 nm, although there was a slight difference in the amount of light absorption, with the largest amount of light absorption at 410 nm. The band gap energy of δ-FeOOH through the Tauc plot method was about 2.1~2.2 eV when H₂O₂ was 0.2~1.4mL. With a sufficient small particle size, simple control of that particle size, and a small band gap energy enough to absorb light in the visible spectrum, δ-FeOOH could be useful in a variety of applications, including photoelectrochemistry and battery electrodes.

• 한국세라믹학회지
• /
• 제19권3호
• /
• pp.223-228
• /
• 1982

For the preparation of ferroxidure BaO.5.5 $Fe_2O_3$ with high coercive force, the green and calcined coprecipitates, which were obtained by neutralizing the mixed salt solution $FeCl_2-BaCl_2$ and $FeCl_3-BaCl_2$ with alkali solution $NaOH-Na_2CO_3$, were investigated about the thermal reaction, crystal growth, and the magnetic properties of the sintered specimens. The very single-domain crystallites of Ba-ferrite with high coercive force are formed from the coprecipitate of amorphous $Fe(OH)_3$ and amorphous $BaCO_3$ at lower temperature than that of subnucleus crystalline $\delta$-FeOOH and amorphous $BaCO_3$.

• 한국환경보건학회지
• /
• 제21권2호
• /
• pp.68-74
• /
• 1995

The optimum conditions was synthesized for the formation of Magnetite ($Fe_3O_4$) by air bubbling with the suspensions obtained by mixing Ferrous sulfate ($FeSO_4\cdot 7H_2O$) and Sodium Hydroxide (NaOH) solution in various values equivalent ratio($R=2NaOH/FeSO_4$) were studied. The changes of the structure were measured with XRD, $EM and BET. Equivalent ratio R: 0.65 was synthesized Goethite ($\alpha$-FeOOH), which becomes Maghemite ($\gamma=Fe_2O_3$) by dehydration, reduction and oxidation process. At the equivalent ratio over 1 (R>1), Magnetite ($Fe_3O_4$) was synthesized directly. The oxygen-deficient Magnetite ($Fe_3O_{4-\delta}$), which is obtained by flowing $H_2$ gas(100 ml/min) through the synthesis Magnetite at 350$\circ$C for 4 hr. By using it, was researched the decomposition reaction of $CO_2$. $CO_2$ was decomposed nearly 100% in 45 minutes by the oxygen-deficient Magnetite.