• Korean Journal of Materials Research
• /
• v.9 no.6
• /
• pp.609-614
• /
• 1999

The effect of the amount of $SiO_2$dopant on the behavior of $AlO_2$$O_3$-composite formation by melt oxdation of Al-alloy was examined in this paper. The $SiO_2$powder was spread on the top surface of the Al-1Mg-3-Si-5Zn-1Cu alloy in th alumina crucible. The selected amount of each powder was 0.03, 0.10, 0.16g/$\textrm{cm}^2$. The oxidation behavior was determined by observing the weight gain after the heat treatment for 10 hours at 1373K. The macroscopic structure of formed oxide layer was examined by an optical microscope. The top surface and the cross-section of the grown oxide layer were investigated by SEM and analysed by EDX. The $SiO_2$ powder was determined to enhance oxidation by thermit reaction with Al which reduced the growth incubation period of the oxidation layer. As the amount of the $SiO_2$dopant increased, the growth rate decreased due to the precipitated Si which blocked the Al-alloy channel in the composite materials. However, more uniform layer was obtained due to the occurrance of the enhanced oxidation reaction in the whole alloy surface compared to the case of addition of less amount of dopant.

• Journal of the Korean Ceramic Society
• /
• v.32 no.4
• /
• pp.482-488
• /
• 1995

The phase transformation temperature from $\theta$- to $\alpha$-alumina was lowered from 1214$^{\circ}C$ to 114$0^{\circ}C$ in DSC by treating ${\gamma}$-alumina obtained by calcination of boehmite at $700^{\circ}C$ for 2hrswith $\alpha$-Al2O3 seeds (d50=0.36${\mu}{\textrm}{m}$) and 3wt% of the alumina sol. $\alpha$-Al2O3 seeds seemed to lower to the transformation temperature and the alumina sol suppressed the high temperature agglormeration. The effect was increased as the amount of the sol was increased, which was supported by TEM and particle size distribution. For an example, spherical ${\gamma}$-alumina powder with d50=0.54${\mu}{\textrm}{m}$ was prepared by treating the ${\gamma}$-alumina with 9 wt% of the alumina sol and 3wt% of the $\alpha$-Al2O3. It sintered to 99% of the theoretical density at 150$0^{\circ}C$ for 2hrs. and it had relatively homogeneous microstructure with 2~3${\mu}{\textrm}{m}$ sized grains.

• Journal of the Korean Ceramic Society
• /
• v.31 no.9
• /
• pp.975-980
• /
• 1994

The thermal properties of cordierite (2MgO.2Al2O3.5SiO2)+30 wt% clay+ Xwt% MnO2 of infrared radiator have been investigated as a function of MnO2 additives (X=0,0.1,0.25,0.5,1.0,1.5,2.0,2.5). The thermal expansion coefficient was decreased with increasing amounts of MnO2 additives. Otherwise, the spectral emissivity was increased in the below 4.5 ${\mu}{\textrm}{m}$ wavelength. Also, the infrared radiator of cordierite system which spectral emissivity was approximately 1.0 can be attainable at from 4.5 ${\mu}{\textrm}{m}$ to 8 ${\mu}{\textrm}{m}$ wavelength. The spectral emissivity was decreased from 8 ${\mu}{\textrm}{m}$ to 14 ${\mu}{\textrm}{m}$ above X=2.5.

• Journal of the Mineralogical Society of Korea
• /
• v.8 no.1
• /
• pp.29-36
• /
• 1995

연옥은 구성광물의 조직, 결합양상 및 화학조성 등에 의해 일반적인 투각섬석과 구분되며, 색, 경도 및 인성 등에 의해 등급과 가치가 달라진다. 본 연구에서는 춘천산 연옥을 대상으로 연옥의 물리적 특성(조직, 경도 및 인성) 등의 연구가 수행되었다. 춘천산 연옥은 구성광물인 투각섬석의 조직, 입도 및 공생광물(불순물)의 특성에 따라 세 가지 유형(유형 I, 유형 II, 유형 III)으로 구분된다. 유형 I은 치밀한 극미립의 초미정질(<5$\mu\textrm{m}$) 투감섬석의 치밀한 집합체로서 구성되며, 유형 II와 유형 III은 미정질(10~30$\mu\textrm{m}$) 및 세립 (>50$\mu\textrm{m}$)의 투각섬석 집합체로서 투휘석, 활석, 녹니석 및 사문석 등이 미량으로 함유된다.연옥을 구성하는 세 유형의 투각섬석의 화학조성은 Fe, Al 성분이 유형 III에서 가장 높은 함량(1.07~1.88wt.% FeO, 1.3~2.59wt.% Al2O3)을 나타내며, 유형 II(0.22~0.37wt.% FeO, 0.66~0.77wt.% Al2O3), 유형 I (0.20~0.24wt.% FeO, 0.05~0.12wt.% Al2O3)의 순으로 감소함을 보이고, SiO2 성분은 유형 I (59.13~59.67 wt.%), 유형 II(58.02~59.40wt.%), 유형 III (57.34~58.63 wt.%)순으로 함량이 낮아짐을 알 수 있다.연옥의 미경도(VHN=311~659)와 파괴인성치(2.38$\times$105~5.62$\times$105 dyne.cm-3/2)는 유형 I, 유형 II, 유형 III의 순으로 낮아진다. 이러한 결과는 조직 및 집합구조의 특성과 밀접한 관계를 갖고 있음을 반영한다.

• Journal of the Korean Ceramic Society
• /
• v.37 no.4
• /
• pp.359-367
• /
• 2000

Particulate composites of Al2O3/SiC, Al2O3/ZrO2 and Al2O3/ZrO2/SiC have been fabricated to investigate their R-curve behaviors and toughening mechanisms. Al2O3 containing 30 vol% SiC particles of 3${\mu}{\textrm}{m}$ showed rising R-curve behavior owing to the strong crack bridging by SiC particles. The fracture toughness reached 9.1 MPa {{{{ SQRT {m} }} at the crack length of 1000${\mu}{\textrm}{m}$. On the other hand, ZrO2-toughened Al2O3 had a high flat R-curve since it rose steeply in the short crack region due to the well known transformation toughening. For Al2O3/ZrO2/SiC composites, the R-curve behavior was similar to that of Al2O3/SiC but with slightly higher toughness. The SiC particles in this composite decreased the amount of transformable tetragonal phase to reduce the effect of transformation toughening by 50%. It was also found that the fracture toughness of this composite with two different toughening mechanisms was markedly lower than that estimated by the simple addition of two contributions.

• Journal of the Korean Ceramic Society
• /
• v.28 no.4
• /
• pp.338-346
• /
• 1991

The alumina-titania composite powders coated with Al2O3 were prepared by the method of hydrolysis-deposition of mixed aluminium salt solution of Al2(SO)4-Al(NO3)3-Urea. The effects of coating-process parameters on the characteristics of coated composite powders were also investigated. As the content of TiO2 dispersed in deionized water increased, the coated composite powders were found to be more uniform in size and unagglomerated. When TiO2 powders were coated for 30 min, the optimum TiO2 content in the coating process was 400 mg/ι. The size of TiO2 particle was increased approximately from 0.7${\mu}{\textrm}{m}$ to 1.0${\mu}{\textrm}{m}$ through coating of Al2O3. The IEP of coated composite powders was pH=8.3 identical to the value of aluminium hydroxides and the zeta-potential showed nearly similar values each other. When heat treating coated composite powders at 130$0^{\circ}C$, only two phases of TiO2(rutile) and Al2TiO5 were observed. These results showed that the suface of TiO2 could be uniformly coated with the aluminium hydroxide.

• Korean Journal of Materials Research
• /
• v.7 no.8
• /
• pp.707-713
• /
• 1997

HVPE(hydride vapor phase epitaxy)법으로 (111)MgAI$_{2}$ $O_{4}$기판위에 GaN 후막을 성장하였다. GaN를 성장하기 전에 기판에 표면을 GaCI로 처리한 수 성장하였을 때 이중 X선 회절 피크의 반치폭이 710 arcsec로서 N $H_{3}$로 처리한 후 성장한 GaN에 비하여 작았으며, 무색 투명의 경면상태가 얻어\ulcorner다. 113$0^{\circ}C$의 온도에서 성장한 GaN 의 광루미네센스(PL)특성과 동일하게 나타났다. 10K의 온도에서 측정된 PL 스펙트럼은 자유여기자와 속박여기자의 재결합천이에 의한 피크들과 Mg과 관련된 도너-억셉터 쌍 사이의 재결합 및 이의 1LO, 2LO, 3LO 및 4 LO 포논복제에 의한 피크들이 나타났다. 성장된 GaN는 n형의 전도성을나타내었으며, 캐리어 이동도와 농도는 각각 21.3$\textrm{cm}^2$/V ㆍsec와 4.2 x $10^{18}$$cm^{-3}$이었다.

• Journal of the Korean Vacuum Society
• /
• v.11 no.1
• /
• pp.35-42
• /
• 2002

We fabricate thermally stable and low resistance Ru ohmic contacts to $n-ZnO:Al(3\times10^{18}\textrm{cm}^{-3})$, grown by specially designed dual target sputtering system. It is shown that the as-deposited Ru contact produces a specific contact resistance of $2.1{\times}10^{-3}{\Omega}\textrm{cm}^2$. Annealing of the Ru contacts leads to the improvement of current-voltage characteristics. For example, annealing of the contact at $700^{\circ}C$ for 1 min produces a contact resistance of $3.2{\times}10^{-5}}{\Omega}\textrm{cm}^2$. furthermore, the metallisation scheme is found to be thermally stable: the surface of the contact is fairly smooth with a rms roughness of 1.4 nm upon annealing at $700^{\circ}C$. These results strongly indicate that the Ru contact represents a suitable metallisation scheme for fabrication of high-performance ZnO-based optical devices and high-temperature devices. In addition, possible mechanisms are suggested to describe the annealing temperature dependence of the specific contact resistance.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1996.05a
• /
• pp.68-71
• /
• 1996

In the study, the thermal and optical properties of SiO$_2$-PbO-K$_2$O-Al$_2$O$_3$ g1asses were investigated. According to Ga$_2$O$_3$ addictions, the properties of bulk glass, transition temperature and softening temperature were increased, whereas thermal expansion coefficient was decreased; In the optical properties, refractive index was increased, and IR cut-off wavelength was enlarged from 4.64$\mu\textrm{m}$ to 5.22$\mu\textrm{m}$. But, the optical loss of fiber was decreased.

• Proceedings of the Korea Crystallographic Association Conference
• /
• 1999.04a
• /
• pp.1-1
• /
• 1999

부유대용융법에 의하여 불순이온의 종류와 각 이온의 주입 농도를 달리하는 Rutile 단결정을 성장하였다. 성장된 결정으로부터 제조한 박편시료를 이용하여 결정결함과 광투과도에 미치는 각 불순이온의 영향을 조사하였다. 결정성장용 주원료로 99.99%의 TiO2를 사용하고, 불순이온 주입을 위한 원료로서 99.99%의 Al2O3, H3BO3, Ga2O3, Sc2O3, V2O5, Fe2O3, ZrO2, Er2O3, Cr2O3를 각각 사용하였다. 불순이온의 종류에 따르는 영향을 조사하기 위하여 TiO2 99.8 atomic%-불순이온 0.2atomic%의 조성이 되도록 각 이온별로 원료를 정밀하게 평량하고 균일 혼합하였다. 불순 이온의 첨가량에 따르는 영향을 조사하기 위하여 Al2O3는 각각 pure, 0.2, 0.4, 0.6 atomic%를, Cr2O3는 pure, 0.003, 0.05, 0.2 atomic%를 각각 치환하여 원료를 조합하였다. 균일 혼합된 원료를 직경 8mm의 고무 튜브에 넣고 CIP(Cold Isostatic Press0에서 2000kg/$\textrm{cm}^2$의 압력으로 성형한 후 150$0^{\circ}C$에서 1시간 소결함으로서 결정성장용 다결정 원료를 합성하였다. 합성된 다결정을 double ellipsoidal mirror 내에 설치하고,halogen lamp로 가열하여 원료의 한쪽 끝을 용융한 다음, 20rpm의 회전속도, 3-5mm/hr의 성장속도로 하는 유속 1$\ell$/min의 O2 분위기속에서 부유대용융법에 의하여 결정을 성장하였다. 성장된 결정을 성장축에 수직한 방향으로 각각 절단, 연삭, 연마한 박편을 이용하여 편광하에서 low-angle grain boundaries 및 기타의 결정결함을 관찰하였으며, 0.3$\mu\textrm{m}$~0.8$\mu\textrm{m}$ 범위 및 0.6$\mu\textrm{m}$~3.4$\mu\textrm{m}$ 범위에서의 투과 및 흡수 스펙트럼을 측정하였다. 결정 성장 결과 B3+, Er3+, Cr3+ 이온은 Ti4+ 이온과 이온의 크기 차이가 심하여 결정의 정상적인 성장을 방해하는 물성을 나타냈고, V5+, Cr3+ 이온은 흑색의 결정, Fe3+ 이온은 적갈색의 결정으로 성장되었다. Al3+, Zr4+, Al3+의 순서로 투과도가 높아지는 것이 관찰되었다. 불순이온의 농도에 따른 영향으로서 Al3+ 이온의 경우 주입농도가 높아질수록 low angle boundary와 oxygen deficiency가 감소하였고, 투과율은 조금 감소하거나 큰 차이가 없는 것으로 나타났다. 반면에 Cr3+ 이온을 주입한 경우 0.003 atomic%에서 최적의 물성을 보였으며, 주입농도가 높아질수록 결정성장이 어려워지고 광의 투과도가 급격히 저하되었다.