• 한국전기전자재료학회논문지
• /
• 제19권11호
• /
• pp.1025-1028
• /
• 2006

Dense $0.95(Na_{0.5}K_{0.5})NbO_3-0.05LiTaO_3$ (NKN-5LT) ceramics were developed by conventional sintering process. Sintering temperature was lowered by adding $Na_2CO_3$ as a sintering aid. The electrical properties of NKN-5LT ceramics were investigated as a function of $Na_2CO_3$ concentration. When the sample sintered at $1000^{\circ}C$ for 4 h with the addition of 1 mol% $Na_2CO_3$, electro-mechanical coupling factor $(k_p)$ and piezoelectric coefficient $(d_{33})$ of NKN-5LT ceramics were found to reach the highest values of 0.43 and 190 pC/N, respectively.

• 대한화학회지
• /
• 제36권1호
• /
• pp.107-112
• /
• 1992

rose bengal(RB)과 NaI를 각각 감응제 및 초감응제로 사용하여 광전기 화학쎌 ITO/$SnO_2$/RB, NaI, $NaClO_4$/Pt로부터 얻은 광전류는 광조사시간의 경과에 따라 비교적 서서히 감소하였다. RB 염료 용액을 광조사하여 분광학적인 방법으로 분석한 결과, 들뜬 RB 분자는 분자내에 있는 요오드에 의해 삼중항 상태, $^3RB^*$로 바뀌고 iodide를 산화시킨 후 환원된 상태가 되어 $SnO_2$ 반도체에 전자를 주입하는 것으로 확인되었다. NaI 대신 $I_2$가 포함되면 $^3RB^*$ 상태에서 전자를 주입하고 염료는 빠르게 분해되므로 광전류는 급격히 감소하였다.

• 한국표면공학회지
• /
• 제54권2호
• /
• pp.96-101
• /
• 2021

NaNbO₃:Eu³⁺ phosphor thin films were grown on quartz substrates by radio-frequency magnetron sputtering at a growth temperature of 100 ℃, with subsequent annealing at temperatures of 800, 900, and 1000 ℃. The effects of annealing temperature on the structural, morphological, and optical properties of the thin films were investigated. The NaNbO₃:Eu³⁺ sputtering target was synthesized by a solid-state reaction of raw materials Na₂CO₃, Nb₂O₅, and Eu₂O₃. The X-ray diffraction patterns exhibited that the thin films had two mixed phases of NaNbO₃ and Eu₂O₃. Surface morphologies were investigated by using field emission-scanning electron microscopy and indicated that the grains of the thin film annealed at 1000 ℃ showed irregular shapes with an average size of approximately 300 nm. The excitation spectra of Eu³⁺-doped NaNbO₃ thin film consisted of a strong charge transfer band centered at 304 nm in the range of 240-350 nm and two weak peaks at 395 and 462 nm, respectively, resulting from the ⁷F₀→⁵L₆ and ⁷F₀→⁵H₂ transitions of Eu³⁺ ions. The emission spectra under excitation at 304 nm exhibited an intense red band centered at 614 nm and two weak bands at 592 and 681 nm. As the annealing temperature increased from 800 ℃ to 1000 ℃, the intensities of all the emission bands and the band gap energies gradually increased. These results indicate that the higher annealing temperature enhance the luminescent properties of NaNbO₃:Eu³⁺ thin films.

• 한국세라믹학회지
• /
• 제49권3호
• /
• pp.241-246
• /
• 2012

Physical properties of plasma electrolytic oxidized layers of 8 different kinds of Al alloys, A-1100, A-2024, A-5052, A-6061, A-6063, A-7075, ACD-7B and ACD-12 were investigated. The electrolyte for plasma electrolytic oxidation was mixture of distilled water, $Na_2P_2O_7$, KOH and some metal salts. Growth rate of oxide layer was slower in $Na_2P_2O_7$ electrolyte system than in $Na_2SiO_3$ system, and Ra50 surface roughness of oxidized layer was below $1.2{\mu}m$. Surface hardness in $Na_2P_2O_7$ electrolyte system is higher than in $Na_2SiO_3$ system, and roughness was lower in $Na_2P_2O_7$ electrolyte system than in $Na_2SiO_3$ system.

• 한국전기전자재료학회논문지
• /
• 제24권7호
• /
• pp.589-593
• /
• 2011

[ $SnO_2$ ]nano powders were prepared by solution reduction method using tin chloride($SnCl_2{\cdot}2H_2O$), hydrazine($N_2H_4$) and NaOH. The $SnO_2$ thick films for gas sensors were fabricated by screen printing method on alumina substrates and annealed at $300^{\circ}C$ in air, respectively. XRD patterns of the $SnO_2$ nano powders showed the tetragonal structure with (110) dominant orientation. The particle size of $SnO_2$ nano powders at the ratio of $SnCl_2:N_2H_4$+NaOH= 1:6 was about 60 nm. The sensing characteristics were investigated by measuring the electrical resistance of each sensor in a test box. Sensitivity of $SnO_2$ gas sensor to 5 ppm $CH_4$gas and 5 ppm $CH_3CH_2CH_3$ gas was investigated for various $SnCl_2:N_2H_4$+NaOH proportion. The highest sensitivity to $CH_4$ gas and $CH_3CH_2CH_3$ gas of $SnO_2$ sensors was observed at the $SnCl_2:N_2H_4$+NaOH= 1:8 and $SnCl_2:N_2H_4$+NaOH= 1:6, respectively. Response and recovery times of $SnO_2$ gas sensors prepared by $SnCl_2:N_2H_4$+NaOH= 1:6 was about 40 s and 30 s, respectively.

• 한국세라믹학회지
• /
• 제16권3호
• /
• pp.135-141
• /
• 1979

This study seeks to find optimum conditions for the heating schedule of the Diopside-Devitrite system, to find the amounts and the kinds of nucleus which effect the crystal growth and forming nucleus. Generally, crystallization in the glass depends on the number of nucleus growing in the internal system and the rate of crystal growth. In order to obtain homogeneous polystalline phae, Diopside as MgO source and $ZrO_2$.$P_2O_5$, $TiO_2$, NaF, $CaF_2$ as nucleating agents were added to the $Na_2O$.CaO.$6SiO_2$ glass. The results obtained were Summarized as follows. 1) Optimum Batch Composition of base glass is 76.82 wt.% $SiO_2$, 5.84 wt.% CaO, 4.54 wt.% MgO and 9.80 wt.% $Na_2O$. 2) Best heating schedule.140$0^{\circ}C$(Melting)coolinglongrightarrow95$0^{\circ}C$reheatinglongrightarrow$1100^{\circ}C$coolinglongrightarrowRoom Temp. 3) The optimum amounts of $ZrO_2$.$P_2O_5$, $TiO_2$ and $CaF_2$ are 3wt.% and that of NaF is 4 wt.% as a nucleating agents.

• Bulletin of the Korean Chemical Society
• /
• 제28권10호
• /
• pp.1675-1682
• /
• 2007

Large colorless single crystals of faujasite-type zeolite with diameters up to 200 μm have been synthesized from gels with the composition of 3.58SiO2:2.08NaAlO2:7.59NaOH:455H2O:5.06TEA:1.23TCl. Two of these, colorless octahedron about 200 μm in cross-section have been treated with aqueous 0.1 M TlC2H3O2 and KNO3 in order to prepare Tl+- and K+-exchanged faujasite-type zeolites, respectively, and then determined the Si/Al ratio of the zeolite framework. The crystal structures of |Tl71|[Si121Al71O384]-FAU and |K53Na18|[Si121Al71O384]-FAU per unit cell, a = 24.9463(2) and 24.9211(16) A, respectively, dehydrated at 673 K and 1 × 10-6 Torr, have been determined by single-crystal X-ray diffraction techniques in the cubic space group Fd m at 294 K. The two single-crystal structures were refined using all intensities to the final error indices (using only the 905 and 429 reflections for which Fo > 4σ(Fo)) R1/R2 = 0.059/0.153 and 0.066/0.290, respectively. In the structure of fully Tl+-exchanged faujasite-type zeolite, 71 Tl+ ions per unit cell are located at four different crystallographic sites. Twenty-nine Tl+ ions fill site I' in the sodalite cavities on 3-fold axes opposite double 6-rings (Tl-O = 2.631(12) A and O-Tl-O = 93.8(4)o). Another 31 Tl+ ions fill site II opposite single 6-rings in the supercage (Tl-O = 2.782(12) A and O-Tl-O = 87.9(4)o). About 3 Tl+ ions are found at site III in the supercage (Tl-O = 2.91(6) and 3.44(3) A), and the remaining 8 occupy another site III (Tl-O = 2.49(5) and 3.06(3) A). In the structure of partially K+-exchanged faujasite-type zeolite, 53 K+ ions per unit cell are found at five different crystallographic sites and 18 Na+ ions per unit cell are found at two different crystallographic sites. The 4 K+ ions are located at site I, the center of the hexagonal prism (K-O = 2.796(8) A and O-K-O = 89.0(3)o). The 10 K+ ions are found at site I' in the sodalite cavity (K-O = 2.570(19) A and O-KO = 99.4(9)o). Twenty-two K+ ions are found at site II in the supercage (K-O = 2.711(9) A and O-K-O = 94.7(3)o). The 5 K+ ions are found at site III deep in the supercage (K-O = 2.90(5) and 3.36(3) A), and 12 K+ ions are found at another site III' (K-O = 2.55(3) and 2.968(18) A). Twelve Na+ ions also lie at site I' (Na-O = 2.292(10) and O-Na-O = 117.5(5)o). The 6 Na+ ions are found at site II in the supercage (Na-O = 2.390(17) A and O-Na-O = 113.1(11)o). The Si/Al ratio of synthetic faujasite-type zeolite is 1.70 determined by the occupations of cations, 71, in two single-crystal structures.

• Korean Chemical Engineering Research
• /
• 제44권5호
• /
• pp.535-539
• /
• 2006

가연성 폐기물 가스화반응으로 생성되는 합성가스내의 $CO_2$ 제거반응에서 $Li_2ZrO_3$와 알칼리염 첨가제의 효과를 열중량 분석기를 이용하여 그 특성을 연구하였다. $Li_2ZrO_3$는 고체상태의 $ZrO_2$와 $Li_2CO_3$를 합성하여 제조하였고, 반응성향상을 위하여 $K_2CO_3$, $Na_2CO_3$, NaCl, LiCl 등의 알칼리염을 첨가한 후 열처리하여 사용하였다. 첨가한 알칼리염에 따른 반응성 향상은 $K_2CO_3>NaCl>LiCl>Na_2CO_3$ 순으로 나타났고 이는 $Li_2CO_3$의 partial melting에 기인한 것으로 사료된다. 반응 시료의 SEM 분석 결과 용융상태의 존재를 확인할 수 있었고, XRD를 통해 첨가된 알칼리염들의 화학적 성분 변화는 일어나지 않는 것으로 확인되었다. NaCl을 사용한 경우 반응 초기에 60분 정도의 유도시간이 발생하였으며, $Na_2CO_3$가 첨가된 경우 $700{\sim}750^{\circ}C$에서도 $Li_2ZrO_3$의 $CO_2$ 제거반응에 의해 생성된 $Li_2CO_3$의 분해가 유도되지 않아 반응성 감소현상이 나타나지 않았다.

• 한국자기학회지
• /
• 제5권5호
• /
• pp.735-739
• /
• 1995

An experiment was carried out to investigate the effect of $Na_{2}O$ additive on the magnetic and physical properties of $SrZn_{2}-W$ type hexagonal ferrite. The specimens were prepared by the conventional manufacturing methods without atmosphere control. It was found that the magnetic properties of SrO.2ZnO.$8Fe_{2}O_{3}$ are considerably improved on adding 1.5wt% $Na_{2}O$. Theoptimum condition of making magnet with suitable properties are as follows : chemical analysis composition : $Sr^{2+}_{0.852}Zn^{2+}_{1.721}Na^{+}_{0.301}Fe^{2+}_{0.723}Fe^{3+}_{15.703}O_{27}$ ; semisintering condition : $1300^{\circ}C\;{\times}\;1h$ in air ; sintering condition : $1250^{\circ}C\;{\times}\;0.5h\;T_{c}=371^{\circ}C,\;H_{A}=1091.5kA/m,\;K_{A}=2.13{\times}10^{5}J/m^{3}\;and\;n_{B}=31.8\mu\textrm{B}$.

• 한국결정성장학회지
• /
• 제26권4호
• /
• pp.159-163
• /
• 2016

본 연구에서는 간단 고상합성법(solid state reaction method)을 이용하여 $Yb^{3+}$, $Er^{3+}$ 이온이 동시도핑된 $NaGd(MoO4)_2$ ($NaGd(MoO_4)_2:Yb^{3+}/Er^{3+}$)를 성공적으로 합성하였으며, 결정구조 및 광학적 특성을 면밀히 분석하였다. 980nm의 근적외선 레이저를 합성된 NaGd(MoO4)2 파우더에 조사하였을 때 $NaGd(MoO_4)_2:Yb^{3+}/Er^{3+}$ 분말은 540 및 550 nm 부근에서 강한 녹색 발광과 함께 650 및 670 nm 부근에서의 매우약한 적색 발광을 하였으며 이러한 업컨버젼 발광 현상은 $Er^{3+}$ 이온 내의 infra 4f transition에 의한 현상임을 확인할 수 있었다. 또한, $Yb^{3+}$ 및 $Er^{3+}$ 이온의 최적 도핑 농도는 각각 (10.0/10.0 mol%)로 확인되었으며, 그에 따른 upconversion 발광 메커니즘에 대하여 상세히 논의하였다.