Fracture Behavior of Oxide Scales and Influence of Oxide Scales on the Strength of Materials

An Fe-25Cr steel was oxidized in Ar atmosphere at 973K with and without applying external stress of 30∼35 MPa. A 0.1$\mu\textrm{m}$ thick $Cr_2O_3$ scales formed during pre-treatment in Ar atmosphere. Initiation of cracking on the oxide scales took place at grain boundaries during the end of second creep stage, in which cracks were found nearly perpendicular to the tensile directions. On the contrary, a scale developed in $N_2$-0.1%$SO_2$ displaced a poor adherence on the metal substrate. In this sample, a fast grown of scales was observed during creep deformation, and the strength of materials was much lower than in Ar. The creep strain rate of $1.5{\times}10^{-7}/s$ and $5.8{\times}10^{-7}/s$ was determined in Ar and in $N_2$-0.1%$SO_2$ under 30MPa, respectively.

산화피막의 파괴거동 및 산화피막이 소지금속의 기계적 강도에 미치는 영향