Synthesis of Alumina Nano Particles by PAA Gel Method from Kaolin

Non-aggregated nanoscale $\alpha$-Al$_2$O$_3$ powders were prepared successfully by polyacrylamine (PAA) gel method. The method was very simple and polymer network inhibited the aggregate of $\alpha$-Al$_2$O$_3$ powders. In this investigation, nanoparticles of $\alpha$-Al$_2$O$_3$ with a diameter of about 8-15 nm were fabricated by calcining the gel precusors with various concentrations of aluminum sulfate, acrylamide and N,N'-methylene-bis-acrylamide (BIS) in air at 110$0^{\circ}C$ for 2 h. The molar ratio of aluminum sulfate to acrylamide did not have any influence on the size of particles. On the other hand, as the molar ratio of BIS to acrylamide increased, the size of nanoparticles decreased.

카올린으로부터 PAA Gel법에 의한 알루미나 나노 입자의 합성

Polyacrylamide(PAA) 겔법은 매우 간단한 중합법이며, 고분자 망상구조가 $\alpha$-Al$_2$O$_3$ 분말의 응집을 억제하므로 미 응집된 나노 크기의 $\alpha$-Al$_2$O$_3$ 분말은 polyacrylamide(PAA) 겔법을 통하여 성공적으로 합성되었다 본 연구에서는 황산알루미늄, acrylamide 및 N,N'-methylene-bis-acrylamide(BIS)의 여러 농도에서 합성된 겔 전구체를 공기 중에서 110$0^{\circ}C$, 2시간동안 하소시켜서 약 8-l5 nm의 직경을 가진 나노 $\alpha$-Al$_2$O$_3$ 입자들을 제조할 수 있었다. Acrylamide에 대한 황산알루미늄의 몰비를 증가시켰을 때는 나노 입자들의 크기는 변하지 않았지만, acrylamide에 대한 BIS의 몰비를 증가시켰을 때는 나노입자들의 크기는 작아지는 경향을 나타내었다.