Glass-alumina Composites Prepared by Melt Infi1tration: III. In-vitro Fatigue Behavior

Hertzian cyclic fatigue properties of the alumina-glass dental ceramics were evaluated in exact in vitro environment at contact loads from 200 N to 1000 N and up to 10$\^$6/ cycles to investigate the indentation damage and strength degradation. At 200 N, no strength degradation and crack generation was observed up to 10$\^$6/ contact cycles. As load increased from 200 N to 1000 N, the drastic reduction in strength was found when the damage transition from ring to radial crack occurred. The extent of strength degradation was more pronounced in vitro environments probably due to chemical reaction of artificial saliva with glass phase through radial cracks introduced during large numbers of contacts.

용융침투법으로 제조한 유리-알루미나 복합체: III. In-vitro 피로거동

인공치관용 알루미나-유리 복합체를 유사 구강분위기인 인공타액 하에서 200-1000 N의 하중 조건으로 $10^{6}$ 횟수까지 헤르찌안 반복하중 피로특성을 조사하였다. 200 N의 하중에서 $10^{6}$까지 반복피로 실험결과, 강도 저하 및 균열 현상은 관찰되지 않았다. 하중이 1000 N으로 증가함에 따라 링 균열에서 방사상 균열로 전이되었을 때 급격한 강도 저하 현상이 발생하였다. 강도 저하 현상은 유사 구강 분위기하에서 반복 하중 접촉 시 발생한 방사상 균열을 통해 침투한 인공타액과 유리상의 화학적 반응으로 더욱 가속화 되었다.