Effect of the Concentration of Suspension and Electrolyte on Zeta Potential

It was investigated that effect of suspension and electrolyte concentrations on zeta potential of alumini suspension and Iso-Electric Point(I.E.P.). The alumina powders in 0.1∼l $\mu\textrm{m}$ particle size distribution, and the electrolyte NH$_4$NO$_3$ were used for preparing the suspension and electrophoresis method was used for measuring zeta potential in this work. As the concentration of suspension was increased, zeta potential and the I.E.P. were increased, respectively. On the other hand, as the electrolyte concentration was increased, the I.E.P. was decreased. As a result of this work, the best condition for measuring zeta potential was the 0.01 wt% and 10 mM of the suspension and the electrolyte concentration, respectively.

현탁액과 전해질의 농도가 제타전위에 미치는 영향

알루미나 분말과 전해질의 농도가 제타전위 및 등전점에 미치는 영향에 대하여 고찰하였다. 0.1~l $\mu\textrm{m}$의 입도 범위를 지닌 알루미나 분말시료와 NH$_4$NO$_3$를 사용하여 실험을 수행하였으며, 전기영동법을 이용하여 제타전위를 측정하였다. 현탁액 내의 시료량이 증가할수록 제타전위와 등전점은 큰 값을 나타내었으며, 현탁액의 농도가 0.0l wt%일 때 제타전위 측정에 가장 적합한 것으로 나타났다. 또한 전해질 농도가 증가할 경우, 제타전위의 값은 다소 증가하는 경향을 보였으나 큰 변화는 없었고, 등전점 값은 오히려 조금 감소하였다. 제타전위 측정에 가장 적합한 전해질 농도는 10 mM인 것으로 나타났으며, 전해질의 종류에 따라서 제타전위와 등전점의 값이 조금 변하는 경향이 있으나 큰 차이를 발생시키지는 않는 것으로 확인되었다.