Experimental Study on Corrosion Characteristics of 1.25Cr-0.5Mo in the 1st-mathanator reactor for Synthetic Natural Gas according to Gas Compositions  

Kim, Jin-Hyun (Department of Automobiles, Chosun College University of Science & Technology)
Cho, Honghyun (Department of Mechanical engineering, Chosun University)
Publication Information
Journal of the Korea Academia-Industrial cooperation Society / v.17, no.5, 2016 , pp. 709-716 More about this Journal
Abstract
Recently, the operating conditions of the various mechanical structures have become more severe and the running time has become longer as the development of plant equipment increases with the introduction of high technology. Thus, the reliability of the system and its accessories is becoming a problem. Normally, synthetic natural gas (SNG) plants use 1.25Cr-0.5Mo or 2.25Cr-1Mo heat resistant steel according to the operating conditions. In this study, a lab-scale reactor was set up using 1.25Cr-0.5Mo steel, in order to carry out corrosion tests for producing synthetic natural gas. The corrosive characteristics were investigated under 1st-methanator operating conditions and fundamental data about the durability and reliability were obtained by using the experimental test. The analysis of results obtained on the durability of the reactor under emission and injection compositions showed that the hydrogen embrittlement caused by hydrogen and the oxidation corrosion caused by H2O had the most effect on the durability of 1.25Cr-0.5Mo steel in the SNG reactor. However, the hydrogen embrittlement and oxidation corrosion occurred simultaneously under emission conditions, so that the corrosion of the material increased suddenly after a long operating time. Besides, the corrosion of the 1.25Cr-0.5Mo steel under the injection composition was faster than that under the emission composition.
Keywords
Synthetic natural gas(SNG); 1.25Cr-0.5Mo; $1^{st}$-Methanator; Composition; Corrosion;
Citations & Related Records
Times Cited By KSCI : 3  (Citation Analysis)
연도 인용수 순위
1 H. J. Kim, H. S. Ryoo, "Ways to Improve Reliability against Stress-Relief Cracking in Weld Metal", Trans. of KMSE, Vol.25, No.2, pp. 3-5, 2007.
2 H. J. Sung, M. S. Ju, J. G. Ju, Y. Y. Kim, "Characteristics of Electro Slag Strip overlaied weldments on the 1.25Cr-0.5Mo Steel", KWJS Conference, Vol. 45, pp. 65-66, 2005.
3 D. H. Lee, J. J. Pack, "Effect of Welding Heat Input and PWHT Cooling Rate on Mechanical Properties of Welded Region at SAW of 1.25Cr-0.5Mo Steel for Pressure Vessel", KWJS Vol.22, No.5 pp. 26-31, 2004.
4 H. W. Lee, H. T. Yang, S. T. Kim, "The Characteristics of the Hydrogen Embrittlement for the Cr-Mo Steels in Use of Pressure Vessel", Trans. of KSME A, Vol.26, No. 6, pp. 1107-1113, 2002.   DOI
5 K. D. Park, J. H. Kim, H. K. Yoon, W. J. Park, "Evaluation on High Temperature Fracture Toughness of Pressure Vessel SA516/70 Steel", ISSN, 1225-0767, pp. 99-104, 2001
6 J. H. Yun, B. S. Lee, Y. J. Oh, J. W. Kim, J. H. Hong, "Effects of temperature and loading rate about fracture resistance of SA518-Gr.70, Nuclear Reactor Coolant pipe", KMS Conference, 1998.
7 Y. D. Yoo, S. H. Kim, Y. S. Yun, G. T. Jin, "Conversion Technology from Coal to Synthetic Natural Gas", Korean Industrial Chemistry News, Vol. 12, No.3, pp. 38-57, 2009.
8 H. T. Yang, S. T. Kim, "A Study on the Mechanical Properties and Microstructural Change by the Thermal Embrittlement of Cr-Mo Steel", Proceeding of the KAMES 2002 Joint Symposium, Vol. 2002, No. 11, pp. 65-70, 2002.
9 G. G. Hancock, H. H. Johnson, Transactions of Metallurgical Society of AIME, 236, pp. 513-514, 1966
10 C. A. Zapffe, C. E. Sims, "Hydrogen Embrittlement, internal stress and defects in steel", Trans. AIME, 145, pp. 225-226. 1941.
11 A. S. Tetelman, Hydrogen in Metals, ASM 17, 1974
12 H. T. Yang, S. T. Kim, "A Study on the Mechanical strength change by thermal aging of 2.25Cr-1Mo steel", Transactions of the Korean Society of Mechanical Engineers A Vol.24 No. 7, 1771-1778, 2000.   DOI
13 S. G. Lee, M. H. Chung, S. K. Oh, J. K. Song, "Creep property Assessment and Creep Life Estimation for High-Remperature Tube Material(2.25Cr1Mo Steel) in Power Plants by LMP", JOET, Vol. 12, No.2, pp. 65-70, 1998.
14 C. F. Barth, E. A. Steigerwald, A. R. Troiano, "Hydrogen Permeability and Delayed Failure of Polarized Martensitic Steels", Corrosion, 25(9), pp. 353-358, 1969.   DOI
15 B. E. Wilde, "Mechanism of Cracking of High Strength Martensitic Stainless Steels in Sodium Chloride Solution", Corrosion, 27(8), pp. 326-333, 1971.   DOI
16 I. C. Choi, K. M. Lee, "Combustion Characteristics of Dual Swirl Combustor according to Hydrogen Content in Simulated SNG Fuel", KOSCO SYMPOSIUM, pp. 111-113, 2014.
17 M. J. Kim, S. W. Chung, J. E. Lee, D. B.Lee, "The Society Of Air-Conditioning And Refrigerating Engineers Of Korea", SAREK SYMPOSIUM, pp. 780-784, 2014.
18 T. W. Kang, K. S. Yoon, M. S. Yang, J. K. Kim, S. H. Kim, "Synthetic natural gas(SNG) production facility construction projects for the pre-feasibility study", Yooshin technical article, Vol. 19, No.4, pp. 34-47, 2012.