A study on preparation of activated carbon from waste tire

In this study we investigated the manufacturing method for the activated carbon using the char from the pyrolysis of waste tire. The physical activation method using the steam in the fixed-bed quartz reactor was used for preparation of activated carbon. The primary experiment parameters are the activation temperature, activation time, heating rate, and the injection quantity of active agent. From the results of pore distribution of activated carbon, the micropore which was made in $850^{\circ}C$ of activation temperature, $5^{\circ}C$/min of heating rate, and 3 hours of activation time was developed in biggest quantity, and mesopore and macropore were developed in the biggest quantity too. The optimum conditions for producing the activated carbon using the pyrolysis residue were $850^{\circ}C$ of activation temperature, 3 hours of activation time, $5^{\circ}C$/min of heating rate, and 3 g $H_2O/char-g{\cdot}hr$ of active agent through this study. The produced activated carbon in these conditions showed that the potentiality of utilization as activated carbon because the BET specific surface area was $517.6m^2/g$ and total pore volume was $0.648cm^3/g$.

폐타이어로부터 활성탄 제조에 관한 연구

본 연구에서는 폐타이어 열분해 잔류물(char)을 이용하여 활성탄을 제조하기 위한 연구를 수행하였다. 활성탄 제조는 고정층 석영관 반응기에서 수증기를 이용한 물리적 활성화 방법을 사용하였으며, 주요한 실험 변수는 활성화 온도, 활성화 시간, 승온속도 및 활성화제의 주입량 등이다. 활성탄 제조 후 세공분포를 분석한 결과, 활성화 온도 $850^{\circ}C$, 승온속도 $5^{\circ}C$/min, 활성화 시간 3 hr의 조건에서 제조한 활성탄이 미세세공(micropore), 중간세공(mesopore) 및 거대세공(macropore)이 가장 많이 발달함을 알 수 있었다. 본 연구결과, 폐타이어 열분해 잔류물을 이용한 활성탄 제조의 최적 조건은 활성화 온도 $850^{\circ}C$, 활성화 시간 3 hr, 승온속도 $5^{\circ}C$/min, 활성화제 공급량 3 g $H_2O/char-g{\cdot}hr$ 등으로 조사되었다. 이 조건에서 제조한 활성탄의 BET 비표면적은 $517.6m^2/g$, 총 세공부피 $0.648cm^3/g$으로 나타나 활성탄으로서의 사용 가능성을 확인할 수 있었다.