Study of the Al-coating on the STS 316L Stainless Steel by Pulse Plating in the Molten Salts at Room Temperature  

정세진 (영남대학교 재료금속공학부)
조계현 (영남대학교 재료금속공학부)
Publication Information
Journal of the Korean institute of surface engineering / v.35, no.1, 2002 , pp. 17-32 More about this Journal
Abstract
Electroplating methods by molten salts and non-aqueous melts were employed for aluminium coating on STS 316L stainless steel. After coated with Ni or non-coated surface on stainless steel, Al pulse plating was carried out in two different types of electrolytes at room temperature. The Al layer from $AlCl_3$-TMPAC melts could not obtain appreciable thickness for engineering application due to chemical reactions between deposits and moisture of air. However, The Al coating by pulse plating in the Ethylbenzene-Toluene-$AlBr_3$ systems was found to be solid coating layer with a few $\mu\textrm{m}$ scale. The conductivity of Ethylbenzene-Toluene-$AlBr_3$ electrolyte was as functions of time and agitation. By seven days exposure after mixing of the electrolyte, Al-deposited layer shows uniform and near by pore-free with high current density (higher than 30mA/$\textrm{cm}^2$). The roughness and imperfection of coating layer were decreased with a increasing agitation speed. It was found that the optimum condition for the Al pulse plating on the 316L stainless steel was a 400mA peak current, duty cycle, $t_{on}$ $t_{ off}$=3ms/1ms, and a current density of 30mA/$\textrm{cm}^2$.
Keywords
Citations & Related Records
연도 인용수 순위
  • Reference
1 Leo J. M. J. Blomen and Michael N. Mugerwa ; 'Fuel Cell Systems' Plenum Press, New York and London. (1993)
2 G. Pelleier and G. A. Capuano, J. Electrochem. Soc., 136, (1989) 1082   DOI   ScienceOn
3 S. Bizabalimana and G. A. Capuano, Can. Metal. Q., 26, (1987) 13   DOI
4 C. L. Hussey, X. Xu, J. Electrochem. Soc., 138, (1991) 1886   DOI
5 P. W. R., Hussey C. L., Stafford G. R., J. Electrochem. Soc., 143 (1996) 461
6 G. E. McManis, A. N. Fletcher, D. E. Bliss and M. H. Miles, J. Electroanal. Chem., 190, 171 (1985)   DOI   ScienceOn
7 李熙雄, 금속표면처리, 13, (1980) 244
8 Kyehyun Cho, to be published
9 G. A. Capuano, W. G. Davenport, J. Electrochem. Soc., (1984) 131
10 廉熙澤, 李柱性 ; '鑛金.表面處理' 文運堂 (1994) 171
11 G. A. Capuano, J. Electrochem. Soc., 138, (1991) 484   DOI
12 United States Patent 4,222,827
13 S. U. Choi, W. C. Frith and H. C. Brown, J. Electrochem. Soc., 113, (1966) 4128
14 조남웅, 장세기 , 전재호, 신정철, 한국표면공학회지, 31, (1998) 3
15 T. P. Moffat, J. Electrochem. Soc., 141, (1994) L115   DOI
16 G. A. Capuano and W. G. Davenport, Plating, March, (1973) 251
17 K. Schumann and H. H. Perkampus, J. Electrochem. Soc., 33A, (1977) 417
18 A. J. Appleby, F. R. Foulkes ; 'Fuel Cell Handbook' Van Nostrand Reinhold, New York. (1989)
19 J. S. Wilkes, J. A. Levisky, R. A. Wilson and C. L. Hussey, Inorg. Chem., 21, (1982) 1236   DOI
20 United States Patent 4,849,060
21 S. U. Choi and H. C. Brown, J. Am. Chem. Soc., 88, (1966) 903   DOI
22 G. A. Capuano, Can. Metal. Q., 27, (1988) 155   DOI
23 C. Koltia, Z. Loizos and N. Spyrellies, Surf. Coat. Technol., 45, (1991) 155   DOI   ScienceOn
24 T. Takenaka, A. Hoshikawa, M. Kawakami, Toyohashi University of Technology, Toyohshi 441, Japan
25 Jean-Claude Puippe, Frank Leaman ; 'The ory and Practice of Pulse Plating', American Electroplaters and Surface Finishers Society
26 Yuguang Zhao and T. J. Noot, Electrochemi Acta., 42, (1997) 3
27 T. P. Moffat, G. R. Stafford, and D. E. Hall, J. Electrochem. Soc., 140, (1993) 2779   DOI   ScienceOn
28 R. T. Carlin, W. Crawford, and M. Bersch, J. Electrochem. Soc, 139, (1992) 2720   DOI
29 K. Schumann and H. H. Perkampus, Spectrochim. Acta., 32A, (1978) 1651
30 S. U. Choi and H. C. Brown, J. Ameri. Chem. Soc., 140, (1993) 903
31 X. H. Xu and C. L. Hussey, University of Mississippi, MS 38677, 445
32 G. A. Capuano and W. G. Davenport, J. Electrochem. Soc., 118, (1971) 1688   DOI
33 L. Legrand, A. Tranchant, and R. Messia, J. Electrochem. Soc., 141, (1994) 378   DOI   ScienceOn