Low-cycle fatigue behaviors of 316L austenitic stainless steel in high temperature water: Effects of pre-soaking, dissolved oxygen, and boric acid & lithium hydroxide  

Xiong, Yida (Graduate School of Engineering, Tohoku University)
Watanabe, Yutaka (Graduate School of Engineering, Tohoku University)
Shibayama, Yuki (Institute for Materials Research, Tohoku University)
Zhong, Xiangyu (Frontier Research Initiative, New Industry Creation Hatchery Center, Tohoku University)
Mary, Nicolas (ELyTMaX UMI 3757, CNRS - Universite de Lyon - Tohoku University, International Joint Unit, Tohoku University)
Publication Information
Nuclear Engineering and Technology / v.54, no.9, 2022 , pp. 3215-3224 More about this Journal
Abstract
Latest studies found that for 316LN austenitic stainless steel (ASS), its LCF life decreased noticeably in high temperature water containing a great amount of dissolved oxygen (DO) (2 ppm DO), compared with that in the water containing 50 or 100 ppb DO. This finding is different from previous studies about ASSs. This study confirmed that the 316L had similar behavior to 316LN. The LCF life of 316L in water containing 1000 ppb DO water was considerably shorter than that in the water containing 50 ppb DO. Addition of boric acid & lithium hydroxide and pre-soaking did not display noticeable effects on the LCF life of this material in the water with 1000 ppb DO, indicating the discrepancy between the latest studies and previous studies was not caused by the boric acid & lithium hydroxide and pre-soaking. This study also confirmed that similar to 316LN, when a certain amount of DO was added into the water, the amount of hydrogen absorbed into the material decreased significantly compared with that when the DO was less than 5 ppb.
Keywords
Corrosion fatigue; Stainless steels; Water chemistry; Nuclear materials;
Citations & Related Records
연도 인용수 순위
  • Reference
1 K. Garbett, An Evaluation of Enriched Boric Acid in European PWRs, EPRI 1003124, Palo Alto, CA, 2001.
2 A. Zoppi, Cristiana Lofrumento, Emilio Mario Castellucci, Mariz Grazia Migliorini, The Raman spectrum of hematite: possible indicator for a compositional or firing distinction among Terra Sigillata wares, Ann. Chim. 95 (2005) 239-246, https://doi.org/10.1002/adic.200590026.   DOI
3 C. Faidy, T. Le Courtois, E. de Fraguier, J.-A. Leduff, A. Lefrancois, J. Dechelotte, Thermal fatigue in French RHR system, in: Int. Conf. On Fatigue of Reactor Components, Napa, California, July 31-August 2, 2000.
4 Us NRC, Regulatory Guide 1.207, 2007.
5 O. Chopra, Gary L. Stevens, Effect of LWR Coolant Environments on Fatigue Life of Reactor Materials Final Report, NUREG/CR-6909, Rev. 1, USNRC, Washington, DC, 2018.
6 Y. Xiong, Y. Watanabe, Y. Shibayama, N. Mary, X. Zhong, Low-cycle fatigue behaviors of 316LN austenitic stainless steel in borated and lithiated high temperature water with different levels of dissolved oxygen, Corrosion Sci. 176 (2020), https://doi.org/10.1016/j.corsci.2020.109048.   DOI
7 Y. Xiong, Y. Watanabe, Y. Shibayama, N. Mary, Effects of 100 ppb dissolved oxygen on low-cycle fatigue behaviors of 316LN austenitic stainless steel in borated and lithiated high temperature water and mechanism behind these effects, Corrosion Sci. 168 (2020), https://doi.org/10.1016/j.corsci.2020.108567.   DOI
8 B.D. Hosterman, Raman Spectroscopic Study of Solid Solution Spinel Oxides, Dissertations, University of Nevada, Las Vegas, 2011.
9 P.R. Graves, C. Johnston, J.J. Campaniello, Raman scattering in spinel structure ferrites, Mater. Res. Bull. 23 (1988) 1651-1660, https://doi.org/10.1016/0025-5408(88)90255-3.   DOI
10 T. Fujii, Water quality and corrosion of metals, J. Surf. Finish. Soc. Jpn. 51 (2000) 134-140, https://doi.org/10.4139/sfj.51.134.   DOI
11 T. Miyazawa, T. Terachi, S. Uchida, T. Satoh, T. Tsukada, Y. Satoh, Y. Wada, H. Hosokawa, Effects of hydrogen peroxide on corrosion of stainless steel, (V) characterization of oxide film with multilateral surface analyses, J. Nucl. Sci. Technol. 43 (2006) 884-895, https://doi.org/10.1080/18811248.2006.9711173.   DOI
12 A. Turnbull, Modeling of the chemistry and electrochemistry in cracks-a review, Corrosion 57 (2001) 175-189, https://doi.org/10.5006/1.3290342.   DOI
13 P.L. Andresen, Emerging issues and fundamental processes in environmental cracking in hot water, Corrosion 64 (2008) 439-464, https://doi.org/10.5006/1.3278483.   DOI
14 Y. Xiong, Y. Watanabe, Y. Shibayama, X. Zhong, N. Mary, Low-cycle fatigue behaviors of 316L austenitic stainless steels with different surface finishing in simulated pressurized water reactor primary water and an oxygenated, borated, lithiated high temperature water, Corrosion Sci. 190 (2021), https://doi.org/10.1016/j.corsci.2021.109709.   DOI
15 O.K. Chopra, Mechanisms and Estimation of Fatigue Crack Initiation in Austenitic Stainless Steels in LWR Environments, NUREG/CR-6787, Argonne National Laboratory, Argonne, IL, August 2002. ANL-01/25.
16 O.K. Chopra, Effects of LWR Coolant Environments on Fatigue Design Curves of Austenitic Stainless Steels, NUREG/CR-5704, Argonne National Laboratory, Argonne, IL, 1999. ANL-98/31.
17 K. Kussmaul, J. Jansky, R. Rintamaa, M. Kemppainen, K. Torronen, On the mechanism of environmental cracking introduced by cyclic thermal loading, in: IAEA Specialists' Meeting, Corrosion and Stress Corrosion of Steel Pressure Boundary Components and Steam Turbines, VTT Symp, vol. 43, Espoo, Finland, 1983.
18 Y. Xiong, Y. Watanabe, Y. Shibayama, Effects of dissolved hydrogen on lowcycle fatigue behaviors and hydrogen uptake of 316LN austenitic stainless steel in simulated pressurized water reactor primary water, Int. J. Fatig. 134 (2020), https://doi.org/10.1016/j.ijfatigue.2019.105457.   DOI
19 A. PH Surtees, G. T Swindles, I. P Savov, I. J Scowen, H. Gm Edwards, T. Munshi, Raman Spectroscopy for the discrimination of tephras from the Hekla eruptions of 1510 and 1947, Holocene 26 (2016) 432-438, https://doi.org/10.1177/0959683615609744.   DOI
20 S. Watanabe, M. Yamanaka, A. Sakai, K. Sawada, T. Iwasa, Laser Raman spectroscopic study on magnetite formation in magnetotactic bacteria, J. Japan Inst. Metals 73 (2009) 334-339, https://doi.org/10.2320/jinstmet.73.334.   DOI
21 J. Wang, J. Wang, E. Han, Influence of conductivity on corrosion behavior of 304 stainless steel in high temperature aqueous environment, J. Mater. Sci. Technol. 32 (2016) 333-340, https://doi.org/10.1016/j.jmst.2015.12.008.   DOI
22 X. Wu, Y. Katada, Inclusion-involved fatigue cracking in high temperature water, Mater, Corrosion 56 (2005) 305-311, https://doi.org/10.1002/maco.200403845.   DOI
23 Q. Peng, G. Li, T. Shoji, The crack tip solution chemistry in sensitized stainless steel in simulated boiling water reactor water studied using a microsampling technique, J. Nucl. Sci. Technol. 40 (2003) 397-404, https://doi.org/10.1080/18811248.2003.9715371.   DOI
24 Korea Atomic Energy Research Institute, Study on Chemical and Volume Control System Design Improvement of PWR to USE the Enriched Boric Acid, KAEPI RR-1591, Taejon, Korea, 1995.
25 H.K. Birnbaum, P. Sofronis, Hydrogen-enhanced localized plasticityda mechanism for hydrogen-related fracture, Mater. Sci. Eng. 176 (1994) 191-202, https://doi.org/10.1016/0921-5093(94)90975-X.   DOI
26 Electric Power Research Institute, Enriched Boric Acid for PWR Application, EPRI NP-6458, Palo Alto, CA, USA, 1992.
27 X. Wu, Y. Katada, Role of inclusions and carbide bands in corrosion fatigue of pressure vessel steel in high-temperature water, Corrosion 60 (2004) 1045-1057, https://doi.org/10.5006/1.3299218.   DOI
28 O.K. Chopra, Mechanism of fatigue crack initiation in austenitic stainless steels in LWR environments, in: Trans. 17th Int. Conf. Struct. Mech. React. Technol. (SMiRT 17), 2002, pp. D03-D04.
29 D.A. Jones, Principles and Prevention of Corrosion, Macmillan Publishing Company, New York, 1996.
30 A. Turnbull, Modelling of crack chemistry in sensitized stainless steel in boiling water reactor environments, Corrosion Sci. 39 (1997) 789-805, https://doi.org/10.1016/S0010-938X(97)89342-0.   DOI
31 M.C. Song, K.J. Lee, in: Proceedings of the Symposium on Technologies for the Management of Radioactive Waste from Nuclear Power Plants and Back End Nuclear Fuel Cycle Activities, 1999. IAEA-SM-357/75.
32 M.L. Martin, J.A. Fenske, G.S. Liu, P. Sofronis, I.M. Robertson, On the formation and nature of quasi-cleavage fracture surfaces in hydrogen embrittled steels, Acta Mater. 59 (2011) 1601-1606, https://doi.org/10.1016/j.actamat.2010.11.024.   DOI
33 O.K. Chorpra, W.J. Shack, Environmental Effects on Fatigue Crack Initiation in Piping and Pressure Vessel Steels, NUREG/CR, 2001, p. 6717.
34 J.E. Maslar, W.S. Hurst, W.J. Bowers, J.H. Hendricks, M.I. Aquino, In situ Raman spectroscopic investigation of aqueous iron corrosion at elevated temperatures and pressures, J. Electrochem. Soc. 147 (2000) 2532-2542, https://doi.org/10.1149/1.1393565.   DOI