Assessment of compressive strength of cement mortar with glass powder from the early strength  

Wang, Chien-Chih (Department of Civil Engineering and Geomatics, Cheng Shiu University)
Ho, Chun-Ling (College of Civil Engineering, Huaqiao University, Intelligence and Automation in Construction Fujian Province Higher-educational Engineering Research Centre)
Wang, Her-Yung (Department of Civil Engineering, National Kaohsiung University of Science and Technology)
Tang, Chi (Department of Soil and Water Conservation, National Pingtung University of Science and Technology)
Publication Information
Computers and Concrete / v.24, no.2, 2019 , pp. 151-158 More about this Journal
Abstract
The sustainable development principle of replacing natural resources with renewable material is an important research topic. In this study, waste LCD (liquid crystal display) glass powder was used to replace cement (0%, 10%, 20% and 30%) through a volumetric method using three water-binder ratios (0.47, 0.59, and 0.71) to make cement mortar. The compressive strength was tested at the ages of 7, 28, 56 and 91 days. The test results show that the compressive strength increases with age but decreases as the water-binder ratio increases. The compressive strength slightly decreases with an increase in the replacement of LCD glass powder at a curing age of 7 days. However, at a curing age of 91 days, the compressive strength is slightly greater than that for the control group (glass powder is 0%). When the water-binder ratios are 0.47, 0.59 and 0.71, the compressive strength of the various replacements increases by 1.38-1.61 times, 1.56-1.80 times and 1.45-2.20 times, respectively, during the aging process from day 7 to day 91. Furthermore, a prediction model of the compressive strength of a cement mortar with waste LCD glass powder was deduced in this study. According to the comparison between the prediction analysis values and test results, the MAPE (mean absolute percentage error) values of the compressive strength are between 2.79% and 5.29%, and less than 10%. Thus, the analytical model established in this study has a good forecasting accuracy. Therefore, the proposed model can be used as a reliable tool for assessing the design strength of cement mortar from early age test results.
Keywords
cement mortar; LCD glass powder; prediction model;
Citations & Related Records
Times Cited By KSCI : 2  (Citation Analysis)
연도 인용수 순위
1 Al-Mutairi, N., Terro, M. and Al-Khaleefi, A. (2004), "Effect of recycling hospitals ash on the compressive properties of concrete: statistical assessment and predicting model", Build. Environ., 39(5), 557-566. https://doi.org/10.1016/j.buildenv.2003.12.010.   DOI
2 Aliabdo, A.A., Elmoaty, A.E.M.A. and Aboshama, A.Y. (2016), "Utilization of waste glass powder in the production of cement and concrete", Constr. Build. Mater., 124, 866-877. https://doi.org/10.1016/j.conbuildmat.2016.08.016.   DOI
3 Carsana, M., Frassoni, M. and Bertolini, L. (2014), "Comparison of ground waste glass with other supplementary cementitious materials", Cement Concrete Compos., 45, 39-45. https://doi.org/10.1016/j.cemconcomp.2013.09.005.   DOI
4 Chang, H.L. (2005), "An approach to sustainable growth for flat panel display industry in Taiwan", Sustain Ind Dev Bimonthly, 19, 4-13.
5 Chen, T.T., Wang, C.C., Hsiung, B.B.C. and Wang, H.Y. (2017), "Seven-day test result assessment of the developed strength in composite cement mortar with slag", Constr. Build. Mater., 152, 587-597. https://doi.org/10.1016/j.conbuildmat.2017.07.001.   DOI
6 Fang, S.F. (2006), "The effect of the lightweight aggregate concrete properties from Sediment at high temperature", Master Thesis, National Kaohsiung University of Applied Sciences, Kaohsiung, Taiwan.
7 Federico, L.M. and Chidiac, S.E. (2009), "Waste glass as a supplementary cementations material in concrete- Critical review of treatment methods", Cement Concrete Compos., 31, 606-610. https://doi.org/10.1016/j.cemconcomp.2009.02.001.   DOI
8 Islam, G.M.S., Rahman, M.H. and Kazi, N. (2017), "Waste glass powder as partial replacement of cement for sustainable concrete practice", Int. J. Sustain. Built Environ, 6, 37-44. https://doi.org/10.1016/j.ijsbe.2016.10.005.   DOI
9 Kim, J., Yi, C. and Zi, G. (2015), "Waste glass sludge as a partial cement replacement in mortar", Constr. Build. Mater., 75, 242-246. https://doi.org/10.1016/j.conbuildmat.2014.11.007.   DOI
10 Kim, S.K., Kang, S.T., Kim, J.K. and Jang, I.Y. (2017), "Effects of particle size and cement replacement of LCD glass powder in concrete", Adv. Mater. Sci. Eng., 2017, Article ID 3928047, 12. https://doi.org/10.1155/2017/3928047.
11 Lewis, C.D. (1982), Industrial and Business Forecasting Method, Butterworth Scientific Publishers, London. https://doi.org/10.1002/for.3980020210.
12 Lin, K.L. (2007), "The effect of heating temperature of thin film transistor-liquid crystal display (TFT-LCD) electric-optical waste glass substitute partial clay as eco-brick", J. Clean. Prod., 15, 1755-1759. https://doi.org/10.1016/j.jclepro.2006.04.002.   DOI
13 Cheng, C.H. (2002), "TFT-LCD discussion on the status of waste disposal in manufacturing industry", Center for Environmental Safety, Industrial Technology Research Institute.
14 Matos, A.M. and Sousa-Coutinho, J. (2012), "Durability of mortar using waste glass powder as cement replacement", Constr. Build. Mater., 36, 205-215. https://doi.org/10.1016/j.conbuildmat.2012.04.027.   DOI
15 Omran, A. and Tagnit-Hamou, A. (2016), "Performance of glasspowder concrete in field applications", Constr. Build. Mater., 109, 84-95. https://doi.org/10.1016/j.conbuildmat.2016.02.006.   DOI
16 Schwarz, N., Cam, H. and Neithalath, N. (2008), "Influence of a fine glass powder on the durability characteristics of concrete and its comparison to fly ash", Cement Concrete Compos., 30, 486-496. https://doi.org/10.1016/j.cemconcomp.2008.02.001.   DOI
17 Rahma, A., Naber, N.E. and Ismail, S.I. (2017), "Effect of glass powder on the compression strength and the workability of concrete", Cogent Eng., 4, 1-12. https://doi.org/10.1080/23311916.2017.1373415.   DOI
18 Roland, M., Werner, B. and Brigitte, S.H. (2004), "Safety of recovery of LCDs in compliance with WEEE", Berlin.
19 Sakale, R., Singh, S. and Jain, S. (2016), "Experimental investigation on strength of glass powder replacement by cement in concrete with different dosages", Int. J. Sci. Tech. Eng., 2(8), 76-86.
20 Shayan, A. and Xu, A. (2004), "Value-added utilization of waste glass in concrete", Cement Concrete Res., 34, 81-89. https://doi.org/10.1016/S0008-8846(03)00251-5.   DOI
21 Shi, C., Wu, Y., Riefler, C. and Wang, H. (2005), "Characteristics and pozzolanic reactivity of glass powders", Cement Concrete Res., 35(5), 987-993. https://doi.org/10.1016/j.cemconres.2004.05.015.   DOI
22 Taha, B. and Nounu, G. (2008), "Properties of concrete contains mixed colors waste recycled glass as sand and cement replacement", Constr. Build. Mater., 22(5), 713-720. https://doi.org/10.1016/j.conbuildmat.2007.01.019.   DOI
23 Terro, M.J. (2006), "Properties of concrete made with recycled crushed glass, at elevated temperatures", Build. Environ., 41, 633-639. https://doi.org/10.1016/j.buildenv.2005.02.018.   DOI
24 Topcu, I.B. and Canbaz, M. (2004), "Properties of concrete containing waste glass", Cement Concrete Res., 34, 267-274. https://doi.org/10.1016/j.cemconres.2003.07.003.   DOI
25 Wang, H.Y. (2009), "A study of the effects of LCD glass sand on the properties of concrete", Waste Mange., 29(1), 335-341. https://doi.org/10.1016/j.wasman.2008.03.005.   DOI
26 Wang, C.C. (2016), "Modelling of the compressive strength development of cement mortar with furnace slag and desulfurization slag from the early strength", Constr. Build. Mater., 128, 108-117. https://doi.org/10.1016/j.conbuildmat.2016.10.083.   DOI
27 Wang, C.C., Chen, T.T., Wang, H.Y. and Huang, C. (2014a), "A predictive model for compressive strength of waste LCD glass concrete by nonlinear-multivariate regression", Comput. Concrete, 13(4), 531-545. https://doi.org/10.12989/cac.2014.13.4.531.   DOI
28 Wang, C.C., Wang, H.Y. and Huang, C. (2014b), "Predictive models of hardened mechanical properties of waste LCD glass concrete", Comput. Concrete, 14(5), 577-597. https://doi.org/10.12989/cac.2014.14.5.577.   DOI
29 Wang, H.Y. and Huang, W.L. (2010), "A study on the properties of fresh self-consolidating glass concrete (SCGC)", Constr. Build. Mater., 24, 619-624. https://doi.org/10.1016/j.conbuildmat.2009.08.047.   DOI
30 Wang, H.Y., Chen, J.S., Wang, S.Y., Chen, Z.C. and Chen, F.L. (2007), "A study on the mix proportion and properties of wasted LCD glass applied to controlled low strength materials concrete (CLSM)", TCI 2007 Concrete Technology Conference and Exhibition, Taiwan Concrete Institute.