Degradation mechanisms of concrete subjected to combined environmental and mechanical actions: a review and perspective

Ye, Hailong (Department of Civil Engineering, The University of Hong Kong)
Jin, Nanguo (Department of Civil and Architectural Engineering, Zhejiang University)

Publication Information

Computers and Concrete / v.23, no.2, 2019 , pp. 107-119 More about this Journal

Abstract

In-service reinforced concrete structures are simultaneously subjected to a combination of multi-deterioration environmental actions and mechanical loads. The combination of two or more deteriorative actions in environments can potentially accelerate the degradation and aging of concrete materials and structures. This paper reviews the coupling and synergistic mechanisms among various deteriorative driving forces (e.g. chloride salts- and carbonation-induced reinforcement corrosion, cyclic freeze-thaw action, alkali-silica reaction, and sulfate attack). In addition, the effects of mechanical loads on detrimental environmental factors are discussed, focusing on the transport properties and damage evolution in concrete. Recommendations for advancing current testing methods and predictive modeling on assessing the long-term durability of concrete with consideration of the coupling effects are provided.

Keywords

concrete; multi-deterioration mechanisms; environmental factors; mechanical loading; durability design;

Citations & Related Records

Times Cited By KSCI : 7 (Citation Analysis)

Reference
Cited By KSCI

1	Ye, H., Fu, C., Jin, N. and Jin, X. (2015), "Influence of flexural loading on chloride ingress in concrete subjected to cyclic drying-wetting condition", Comput. Concrete, 15, 183-198. DOI
2	Ye, H., Fu, C., Jin, N. and Jin, X. (2018), "Performance of reinforced concrete beams corroded under sustained service loads: A comparative study of two accelerated corrosion techniques", Constr. Build. Mater., 162, 286-297. DOI
3	Ye, H., Jin, N., Fu, C. and Jin, X. (2017a), "Rust distribution and corrosion-induced cracking patterns of corner-located rebar in concrete cover", Constr. Build. Mater., 156, 684-691. DOI
4	Ye, H., Jin, N. and Jin, X. (2017b), "An experimental study on relationship among water sorptivity, pore characteristics, and salt concentration in concrete", Periodica Polytechnica Civil Eng., 61, 530-540.
5	Ye, H., Jin, N., Jin, X. and Fu, C. (2012), "Model of chloride penetration into cracked concrete subject to drying-wetting cycles", Constr. Build. Mater., 36, 259-269. DOI
6	Ye, H., Jin, N., Jin, X., Fu, C. and Chen, W. (2016a), "Chloride ingress profiles and binding capacity of mortar in cyclic dryingwetting salt fog environments", Constr. Build. Mater., 127, 733-742. DOI
7	Ye, H., Jin, X., Chen, W., Fu, C. and Jin, N. (2016b), "Prediction of chloride binding isotherms for blended cements", Comput. Concrete, 17, 655-672. DOI
8	Ye, H., Jin, X., Fu, C., Jin, N., Xu, Y. and Huang, T. (2016c), "Chloride penetration in concrete exposed to cyclic dryingwetting and carbonation", Constr. Build. Mater., 112, 457-463. DOI
9	Miao, C., Mu, R., Tian, Q. and Sun, W. (2002), "Effect of sulfate solution on the frost resistance of concrete with and without steel fiber reinforcement", Cement Concrete Res., 32, 31-34. DOI
10	Mien, T.V., Stitmannaithum, B. and Nawa, T. (2009), "Simulation of chloride penetration into concrete structures subjected to both cyclic flexural loads and tidal effects", Comput. Concrete, 6, 421-435. DOI
11	Monette, L., Gardner, N. and Grattan-Bellew, P. (2002), "Residual strength of reinforced concrete beams damaged by alkali-silica reaction-Examination of damage rating index method", Mater. J., 99, 42-50.
12	Mori, Y. and Ellingwood, B.R. (1993), "Reliability-based servicelife assessment of aging concrete structures", J. Struct. Eng., 119, 1600-1621. DOI
13	Mu, R., Miao, C., Luo, X. and Sun, W. (2002), "Interaction between loading, freeze-thaw cycles, and chloride salt attack of concrete with and without steel fiber reinforcement", Cement Concrete Res., 32, 1061-1066. DOI
14	Multon, S. and Toutlemonde, F. (2006), "Effect of applied stresses on alkali-silica reaction-induced expansions", Cement Concrete Res., 36, 912-920. DOI
15	Nakhi, A., Xie, Z., Asiz, A., Ababneh, A. and Xi, Y. (2000), "Chloride penetration in concrete under coupled hygromechanical loadings", Condition Monit. Mater. Struct., ASCE, 84-94.
16	Neville, A. (2004), "The confused world of sulfate attack on concrete", Cement Concrete Res., 34, 1275-1296. DOI
17	Ye, H., Tian, Y., Jin, N., Jin, X. and Fu, C. (2013), "Influence of cracking on chloride diffusivity and moisture influential depth in concrete subjected to simulated environmental conditions", Constr. Build. Mater., 47, 66-79. DOI
18	Ngala, V. and Page, C. (1997), "Effects of carbonation on pore structure and diffusional properties of hydrated cement pastes", Cement Concrete Res., 27, 995-1007. DOI
19	Ye, H. and Radlin'ska, A. (2017), "Effect of alkalis on cementitious materials: Understanding the relationship between composition, structure, and volume change mechanism", J. Adv. Concrete Technol., 15, 165-177. DOI
20	Ye, H. and Radlin'ska, A. (2016), "A review and comparative study of existing shrinkage prediction models for portland and nonportland cementitious materials", Adv. Mater. Sci. Eng., 2016, Article ID: 2418219.
21	Yin, G.J., Zuo, X.B., Tang, Y.J., Ayinde, O. and Ding, D.N. (2017), "Modeling of time-varying stress in concrete under axial loading and sulfate attack", Comput. Concrete, 19, 143-152. DOI
22	Yoon, S., Wang, K., Weiss, W.J. and Shah, S.P. (2000), "Interaction between loading, corrosion, and serviceability of reinforced concrete", Mater. J., 97, 637-644.
23	Yuan, J., Lu, H., Yang, Q. and Ling, J. (2017), "Mechanisms on the salt-frost scaling of concrete", J. Mater. Civil Eng., 29, D4015002. DOI
24	Zhao, J., Cai, G., Gao, D. and Zhao, S. (2014), "Influences of freeze-thaw cycle and curing time on chloride ion penetration resistance of Sulphoaluminate cement concrete", Constr. Build. Mater., 53, 305-311. DOI
25	Zuquan, J., Wei, S., Yunsheng, Z., Jinyang, J. and Jianzhong, L. (2007), "Interaction between sulfate and chloride solution attack of concretes with and without fly ash", Cement Concrete Res., 37, 1223-1232. DOI
26	Penttala, V. and Al-Neshawy, F. (2002), "Stress and strain state of concrete during freezing and thawing cycles", Cement Concrete Res., 32, 1407-1420. DOI
27	Nixon, P., Page, C., Canham, I. and Bollinghaus, R. (1988), "Influence of sodium chloride on alkali-silica reaction", Adv. Cement Res., 1, 99-106. DOI
28	Papadakis, V.G., Vayenas, C.G. and Fardis, M.N. (1991), "Physical and chemical characteristics affecting the durability of concrete", Mater. J., 88, 186-196.
29	Penttala, V. (1998), "Freezing-induced strains and pressures in wet porous materials and especially in concrete mortars", Adv. Cement Bas. Mater., 7, 8-19. DOI
30	Pettifer, K. and Nixon, P. (1980), "Alkali metal sulphate-a factor common to both alkali aggregate reaction and sulphate attack on concrete", Cement Concrete Res., 10, 173-181. DOI
31	Pigeon, M. and Pleau, R. (2010), Durability of Concrete in Cold Climates, CRC Press.
32	Powers, T. (1975), "Freezing effects in concrete", ACI Spec. Pub., 47, 1-12
33	Powers, T.C. and Helmuth, R. (1953), "Theory of volume changes in hardened portland-cement paste during freezing", Highway Research Board Proceedings.
34	Puatatsananon, W. and Saouma, V. (2005), "Nonlinear coupling of carbonation and chloride diffusion in concrete", J. Mater. Civil Eng., 17, 264-275. DOI
35	Rajabipour, F., Giannini, E., Dunant, C., Ideker, J. H. and Thomas, M.D. (2015), "Alkali-silica reaction: Current understanding of the reaction mechanisms and the knowledge gaps", Cement Concrete Res., 76, 130-146. DOI
36	Scherer, G.W. (1993), "Freezing gels", J. Non-Crystal. Solid., 155, 1-25. DOI
37	Rodriguez, J., Ortega, L. and Casal, J. (1996), "Load bearing capacity of concrete columns with corroded reinforcement", Corrosion of Reinforcement in Concrete Construction Proceedings of Fourth International Symposium, Cambridge, July.
38	Saillio, M., Baroghel-Bouny, V. and Barberon, F. (2014), "Chloride binding in sound and carbonated cementitious materials with various types of binder", Constr. Build. Mater., 68, 82-91. DOI
39	Saito, M. and Ishimori, H. (1995), "Chloride permeability of concrete under static and repeated compressive loading", Cement Concrete Res., 25, 803-808. DOI
40	Shi, X., Fay, L., Peterson, M.M. and Yang, Z. (2010), "Freezethaw damage and chemical change of a portland cement concrete in the presence of diluted deicers", Mater. Struct., 43, 933-946. DOI
41	Skalny, J. and Brown, P. (2002), Sulfate Attack on Concrete, Taylor & Francis.
42	Song, H.W., Lee, C.H. and Ann, K.Y. (2008), "Factors influencing chloride transport in concrete structures exposed to marine environments", Cement Concrete Compos., 30, 113-121. DOI
43	Sotiriadis, K., Nikolopoulou, E. and Tsivilis, S. (2012), "Sulfate resistance of limestone cement concrete exposed to combined chloride and sulfate environment at low temperature", Cement Concrete Compos., 34, 903-910. DOI
44	Spragg, R.P., Castro, J., Li, W., Pour-Ghaz, M., Huang, P.T. and Weiss, J. (2011), "Wetting and drying of concrete using aqueous solutions containing deicing salts", Cement Concrete Compos., 33, 535-542. DOI
45	Gontar, W.A., Martin, J.P. and Popovics, J.S. (2000), "Effects of cyclic loading on chloride permeability of plain concrete", Condition Monit. Mater. Struct., 1, 95-109.
46	Stewart, M.G. and Rosowsky, D.V. (1998), "Structural safety and serviceability of concrete bridges subject to corrosion", J. Infrastr. Syst., 4, 146-155. DOI
47	Fu, C., Ye, H., Jin, X., Yan, D., Jin, N. and Peng, Z. (2016), "Chloride penetration into concrete damaged by uniaxial tensile fatigue loading", Constr. Build. Mater., 125, 714-723. DOI
48	Geng, J., Easterbrook, D., Li, L.Y. and Mo, L.W. (2015), "The stability of bound chlorides in cement paste with sulfate attack", Cement Concrete Res., 68, 211-222. DOI
49	Gerard, B., Pijaudier-Cabot, G. and Laborderie, C. (1998), "Coupled diffusion-damage modelling and the implications on failure due to strain localisation", Int. J. Solid. Struct., 35, 4107-4120. DOI
50	Giorla, A.B., Scrivener, K.L. and Dunant, C.F. (2015), "Influence of visco-elasticity on the stress development induced by alkali-silica reaction", Cement Concrete Res., 70, 1-8. DOI
51	Gowripalan, N., Sirivivatnanon, V. and Lim, C. (2000), "Chloride diffusivity of concrete cracked in flexure", Cement Concrete Res., 30, 725-730. DOI
52	Guoping, L., Fangjian, H. and Yongxian, W. (2011), "Chloride ion penetration in stressed concrete", J. Mater. Civil Eng., 23, 1145-1153. DOI
53	Suryavanshi, A., Scantlebury, J. and Lyon, S. (1996), "Mechanism of Friedel's salt formation in cements rich in tri-calcium aluminate", Cement Concrete Res., 26, 717-727. DOI
54	Stutzman, P. E. (1999) "Deterioration of Iowa Highway concrete pavements: A petrographic study", US Department of Commerce, Technology Administration, National Institute of Standards and Technology.
55	Sugiyama, T. (1994) "Permeability of stressed concrete", University of New Brunswick, Canada.
56	Sun, W., Mu, R., Luo, X. and Miao, C. (2002), "Effect of chloride salt, freeze-thaw cycling and externally applied load on the performance of the concrete", Cement Concrete Res., 32, 1859-1864. DOI
57	Suryavanshi, A. and Swamy, R.N. (1996), "Stability of Friedel's salt in carbonated concrete structural elements", Cement Concrete Res., 26, 729-741. DOI
58	Sutter, L., Dam, T.V., Peterson, K.R. and Johnston, D.P. (2006), "Long-term effects of magnesium chloride and other concentrated salt solutions on pavement and structural portland cement concrete: Phase I results", Tran. Res. Record: J. Tran. Res. Board, 1979, 60-68. DOI
59	Swamy, R.N. (2002), The Alkali-Silica Reaction in Concrete, CRC Press.
60	Tang, S.W., Yao, Y., Andrade, C. and Li, Z. (2015), "Recent durability studies on concrete structure", Cement Concrete Res., 78, 143-154. DOI
61	Thomas, M.D. and Bamforth, P.B. (1999), "Modelling chloride diffusion in concrete: effect of fly ash and slag", Cement Concrete Res., 29, 487-495. DOI
62	Guzman, S., Galvez, J.C. and Sancho, J.M. (2011), "Cover cracking of reinforced concrete due to rebar corrosion induced by chloride penetration", Cement Concrete Res., 41, 893-902. DOI
63	Hobbs, D.W. (1988), Alkali-silica Reaction in Concrete, Thomas Telford Publishing.
64	Holt, E., Ferreira, M., Kuosa, H. and Leivo, M. (2015), "Performance and durability of concrete under effect of multideterioration mechanisms", J. Chin. Ceram. Soc., 43, 10.
65	Taylor, H., Famy, C. and Scrivener, K. (2001), "Delayed ettringite formation", Cement Concrete Res., 31, 683-693. DOI
66	Thomas, M. (2001), "The role of calcium hydroxide in alkali recycling in concrete", Mater. Sci. Concrete Spec., 225-236.
67	Al-Amoudi, O.S.B., Maslehuddin, M. and Abdul-Al, Y.A. (1995), "Role of chloride ions on expansion and strength reduction in plain and blended cements in sulfate environments", Constr. Build. Mater., 9, 25-33. DOI
68	Adamson, A.W. and Gast, A.P. (1967), Physical Chemistry of Surfaces, Sixth Edition, Wiley-Interscience.
69	Ahmad, S. (2003), "Reinforcement corrosion in concrete structures, its monitoring and service life prediction-a review", Cement Concrete Compos., 25, 459-471. DOI
70	Ahn, W. and Reddy, D. (2001), "Galvanostatic testing for the durability of marine concrete under fatigue loading", Cement Concrete Res., 31, 343-349. DOI
71	Al-Sulaimani, G., Kaleemullah, M. and Basunbul, I. (1990), "Influence of corrosion and cracking on bond behavior and strength of reinforced concrete members", Struct. J., 87, 220-231.
72	Aldea, C.M., Shah, S. and Karr, A. (1999a), "Permeability of cracked concrete", Mater. Struct., 32, 370-376. DOI
73	Hoseini, M., Bindiganavile, V. and Banthia, N. (2009), "The effect of mechanical stress on permeability of concrete: a review", Cement Concrete Compos., 31, 213-220. DOI
74	Hou, X., Struble, L.J. and Kirkpatrick, R.J. (2004), "Formation of ASR gel and the roles of CSH and portlandite", Cement Concrete Res., 34, 1683-1696. DOI
75	Huang, Y., Ye, H., Fu, C. and Jin, N. (2017), "Modeling moisture transport at the surface layer of fatigue-damaged concrete", Constru. Build. Mater., 151, 196-207. DOI
76	Kaufmann, J.P. (2004), "Experimental identification of ice formation in small concrete pores", Cement Concrete Res., 34, 1421-1427. DOI
77	Kawamura, M., Takeuchi, K. and Sugiyama, A. (1994), "Mechanisms of expansion of mortars containing reactive aggregate in NaCl solution", Cement Concrete Res., 24, 621-632. DOI
78	Khan, M., Kayali, O. and Troitzsch, U. (2016), "Chloride binding capacity of hydrotalcite and the competition with carbonates in ground granulated blast furnace slag concrete", Mater. Struct., 49(11), 4609-4619.. DOI
79	Vorechovska, D., Somodikova, M., Podrouzeka, J., Lehky, D. and Teply, B. (2017), "Concrete structures under combined mechanical and environmental actions: Modelling of durability and reliability", Comput. Concrete, 20, 99-110. DOI
80	Villani, C., Spragg, R., Pour-Ghaz, M. and Jason Weiss, W. (2014), "The influence of pore solutions properties on drying in cementitious materials", J. Am. Ceramic Soc., 97, 386-393. DOI
81	Vu, K.A.T. and Stewart, M.G. (2000), "Structural reliability of concrete bridges including improved chloride-induced corrosion models", Struct. Saf., 22, 313-333. DOI
82	Wang, H., Lu, C., Jin, W. and Bai, Y. (2011), "Effect of external loads on chloride transport in concrete", J. Mater. Civil Eng., 23, 1043-1049. DOI
83	Wang, K., Jansen, D.C., Shah, S.P. and Karr, A.F. (1997), "Permeability study of cracked concrete", Cement Concrete Res., 27, 381-393. DOI
84	Wang, K., Nelsen, D.E. and Nixon, W. A. (2006), "Damaging effects of deicing chemicals on concrete materials", Cement Concrete Compos., 28, 173-188. DOI
85	Wang, Z., Zeng, Q., Wang, L., Yao, Y. and Li, K. (2014), "Corrosion of rebar in concrete under cyclic freeze-thaw and Chloride salt action", Constr. Build. Mater., 53, 40-47. DOI
86	Wittmann, F., Jiang, F., Wan, X., Zhang, P. and Zhao, T. (2014), "Influence of combined mechanical and environmental loads on service life of reinforced concrete structures", Life-Cycle and Sustainability of Civil Infrastructure Systems: Proceedings of the Third International Symposium on Life-Cycle Civil Engineering (IALCCE'12), Vienna, Austria, October.
87	Yang, K.H., Cheon, J.H. and Kwon, S.J. (2017), "Modeling of chloride diffusion in concrete considering wedge-shaped single crack and steady-state condition", Comput. Concrete, 19, 211-216. DOI
88	Kulakowski, M.P., Pereira, F.M. and Dal Molin, D.C. (2009), "Carbonation-induced reinforcement corrosion in silica fume concrete", Constr. Build. Mater., 23, 1189-1195. DOI
89	Kobayashi, K. and Uno, Y. (1990), "Influence of alkali on carbonation of concrete, part 2-influence of alkali in cement on rate of carbonation of concrete", Cement Concrete Res., 20, 619-622. DOI
90	Konin, A., Francois, R. and Arliguie, G. (1998), "Penetration of chlorides in relation to the microcracking state into reinforced ordinary and high strength concrete", Mater. Struct., 31, 310-316. DOI
91	Ann, K., Ahn, J. and Ryou, J. (2009), "The importance of chloride content at the concrete surface in assessing the time to corrosion of steel in concrete structures", Constr. Build. Mater., 23, 239-245. DOI
92	Aldea, C.M., Ghandehari, M., Shah, S.P. and Karr, A. (2000), "Estimation of water flow through cracked concrete under load", ACI Struct. J., 97, 567-575.
93	Andrade, C. and Page, C. (1986), "Pore solution chemistry and corrosion in hydrated cement systems containing chloride salts: a study of cation specific effects", Brit. Corr. J., 21, 49-54. DOI
94	Angst, U., Elsener, B., Larsen, C.K. and Vennesland, O . (2009), "Critical chloride content in reinforced concrete-a review", Cement Concrete Res., 39, 1122-1138. DOI
95	Backus, J., McPolin, D., Basheer, M., Long, A. and Holmes, N. (2013), "Exposure of mortars to cyclic chloride ingress and carbonation", Adv. Cement Res., 25(1), 3-11. DOI
96	Bary, B., Leterrier, N., Deville, E. and Le Bescop, P. (2014), "Coupled chemo-transport-mechanical modelling and numerical simulation of external sulfate attack in mortar", Cement Concrete Compos., 49, 70-83. DOI
97	Ballim, Y. and Reid, J. (2003), "Reinforcement corrosion and the deflection of RC beams-an experimental critique of current test methods", Cement Concrete Compos., 25, 625-632. DOI
98	Balonis, M., Lothenbach, B., Le Saout, G. and Glasser, F.P. (2010), "Impact of chloride on the mineralogy of hydrated Portland cement systems", Cement Concrete Res., 40, 1009-1022. DOI
99	Banthia, N., Biparva, A. and Mindess, S. (2005), "Permeability of concrete under stress", Cement Concrete Res., 35, 1651-1655. DOI
100	Aldea, C.M., Shah, S.P. and Karr, A. (1999b), "Effect of cracking on water and chloride permeability of concrete", J. Mater. Civil Eng., 11, 181-187. DOI
101	Lee, M.K., Jung, S.H. and Oh, B.H. (2013), "Effects of carbonation on chloride penetration in concrete", ACI Mater. J., 110, 458-459.
102	Li, W., Pour-Ghaz, M., Castro, J. and Weiss, J. (2011a), "Water absorption and critical degree of saturation relating to freezethaw damage in concrete pavement joints", J. Mater. Civil Eng., 24, 299-307. DOI
103	Li, W., Sun, W. and Jiang, J. (2011b), "Damage of concrete experiencing flexural fatigue load and closed freeze/thaw cycles simultaneously", Constr. Build. Mater., 25, 2604-2610. DOI
104	Lim, C., Gowripalan, N. and Sirivivatnanon, V. (2000), "Microcracking and chloride permeability of concrete under uniaxial compression", Cement Concrete Compos., 22, 353-360. DOI
105	Malheiro, R., Camoes, A., Ferreira, R.M., Meira, G. and Amorim, M. (2014), "Effect of carbonation on the chloride diffusion of mortar specimens exposed to cyclic wetting and drying", XIII DBMC, International Conference on Durability of Building Materials and Components, 482-489.
106	Liu, R., Jiang, L., Huang, G., Zhu, Y., Liu, X., Chu, H. and Xiong, C. (2016), "The effect of carbonate and sulfate ions on chloride threshold level of reinforcement corrosion in mortar with/without fly ash", Constr. Build. Mater., 113, 90-95. DOI
107	Lodeiro, I.G., Macphee, D., Palomo, A. and Fernandez-Jimenez, A. (2009), "Effect of alkalis on fresh C-S-H gels. FTIR analysis", Cement Concrete Res., 39, 147-153. DOI
108	Maes, M. and De Belie, N. (2014), "Resistance of concrete and mortar against combined attack of chloride and sodium sulphate", Cement Concrete Compos., 53, 59-72. DOI
109	Kuosa, H., Ferreira, R., Holt, E., Leivo, M. and Vesikari, E. (2014), "Effect of coupled deterioration by freeze-thaw, carbonation and chlorides on concrete service life", Cement Concrete Compos., 47, 32-40. DOI
110	Cheung, M.M., Zhao, J. and Chan, Y.B. (2009), "Service life prediction of RC bridge structures exposed to chloride environments", J. Bridge Eng., 14, 164-178. DOI
111	Chung, C.W., Shon, C.S. and Kim, Y.S. (2010), "Chloride ion diffusivity of fly ash and silica fume concretes exposed to freeze-thaw cycles", Constr. Build. Mater., 24, 1739-1745. DOI
112	Fagerlund, G. (1977), "The critical degree of saturation method of assessing the freeze/thaw resistance of concrete", Mater. Struct., 10, 217-229.
113	Bentz, D.P., Jones, S.Z., Peltz, M.A. and Stutzman, P.E., "Influence of internal curing on properties and performance of cement-based repair materials", http://dx.doi.org/10.6028/NIST.IR.8076.
114	Berube, M.A., Chouinard, D., Pigeon, M., Frenette, J., Boisvert, L. and Rivest, M. (2002), "Effectiveness of sealers in counteracting alkali-silica reaction in plain and air-entrained laboratory concretes exposed to wetting and drying, freezing and thawing, and salt water", Can. J. Civil Eng., 29, 289-300. DOI
115	Clifton, J.R. (1993), "Predicting the service life of concrete", ACI Mater. J., 90, 611-611.
116	Collepardi, M., Marcialis, A. and Turriziani, R. (1972), "Penetration of chloride ions into cement pastes and concretes", J. Am. Ceramic Soc., 55, 534-535. DOI
117	Dow, C. and Glasser, F. (2003), "Calcium carbonate efflorescence on Portland cement and building materials", Cement Concrete Res., 33, 147-154. DOI
118	Farnam, Y., Bentz, D., Hampton, A. and Weiss, W. (2014), "Acoustic emission and low-temperature calorimetry study of freeze and thaw behavior in cementitious materials exposed to sodium chloride salt", Tran. Res. Record: J. Tran. Res. Board, 2441, 81-90.. DOI
119	Fu, C., Jin, N., Ye, H., Jin, X. and Dai, W. (2017), "Corrosion characteristics of a 4-year naturally corroded reinforced concrete beam with load-induced transverse cracks", Corr. Sci., 117, 11-23.. DOI
120	Fu, C., Jin, X., Ye, H. and Jin, N. (2015a), "Theoretical and experimental investigation of loading effects on chloride diffusion in saturated concrete", J. Adv. Concrete Technol., 13, 30-43. DOI
121	Fu, C., Ye, H., Jin, X., Jin, N. and Gong, L. (2015b), "A reactiondiffusion modeling of carbonation process in self-compacting concrete", Comput. Concrete, 15, 847-864. DOI
122	Ye, H. (2015), "Creep mechanisms of Calcium-Silicate-Hydrate: An overview of recent advances and challenges", Int. J. Concrete Struct. Mater., 9, 453-462. DOI
123	Castel, A., Francois, R. and Arliguie, G. (1999), "Effect of loading on carbonation penetration in reinforced concrete elements", Cement Concrete Res., 29, 561-565. DOI
124	Birnin-Yauri, U. and Glasser, F. (1998), "Friedel's salt, Ca 2 Al (OH) 6 (Cl, OH). 2H 2 O: its solid solutions and their role in chloride binding", Cement Concrete Res., 28, 1713-1723. DOI
125	Broomfield, J.P. (2002), Corrosion of Steel in Concrete: Understanding, Investigation And repair, CRC Press.
126	Brown, P. and Bothe, Jr. J. (1993), "The stability of ettringite", Adv. Cement Res., 5, 47-63. DOI
127	Chang, H., Mu, S. and Feng, P. (2018), "Influence of carbonation on "maximum phenomenon" in surface layer of specimens subjected to cyclic drying-wetting condition", Cement Concrete Res., 103, 95-109. DOI
128	Chatterji, S. (1978), "An accelerated method for the detection of alkali-aggregate reactivities of aggregates", Cement Concrete Res., 8, 647-649. DOI
129	Chatterji, S. (1979), "The role of Ca (OH) 2 in the breakdown of portland cement concrete due to alkali-silica reaction", Cement Concrete Res., 9, 185-188. DOI
130	Chen, J., Zhang, W. and Gu, X. (2018), "Mesoscale model for cracking of concrete cover induced by reinforcement corrosion", Comput. Concrete, 22, 53-62. DOI
131	Maslehuddin, M., Page, C. and Rasheeduzzafar, (1996), "Effect of temperature and salt contamination on carbonation of cements", J. Mater. Civil Eng., 8, 63-69. DOI
132	Mehta, P.K. (1986), "Concrete. Structure, properties and materials".