Transverse cracking based numerical analysis and its effects on cross-ply laminates strength under thermo-mechanical degradation  

Abdelatif, Berriah (Laboratory of Mechanics of Structures and Solids (LMSS), Faculty of Technology -Department of Mechanical Engineering University Djilali Liabes of Sidi Bel Abbes)
Abdelkader, Megueni (Laboratory of Mechanics of Structures and Solids (LMSS), Faculty of Technology -Department of Mechanical Engineering University Djilali Liabes of Sidi Bel Abbes)
Abdelkader, Lousdad (Laboratory of Mechanics of Structures and Solids (LMSS), Faculty of Technology -Department of Mechanical Engineering University Djilali Liabes of Sidi Bel Abbes)
Publication Information
Structural Engineering and Mechanics / v.60, no.6, 2016 , pp. 1063-1077 More about this Journal
Abstract
Components manufactured from composite materials are frequently subjected to superimposed mechanical and thermal loadings during their operating service. Both types of loadings may cause fracture and failure of composite structures. When composite cross-ply laminates of type [$0_m/90_n]_s$ are subjected to uni-axial tensile loading, different types of damage are set-up and developed such as matrix cracking: transverse and longitudinal cracks, delamination between disoriented layers and broken fibers. The development of these modes of damage can be detrimental for the stiffness of the laminates. From the experimental point of view, transverse cracking is known as the first mode of damage. In this regard, the objective of the present paper is to investigate the effect of transverse cracking in cross-ply laminate under thermo-mechanical degradation. A Finite Element (FE) simulation of damage evolution in composite crossply laminates of type [$0_m/90_n]_s$ subjected to uni-axial tensile loading is carried out. The effect of transverse cracking on the cross-ply laminate strength under thermo-mechanical degradation is investigated numerically. The results obtained by prediction of the numerical model developed in this investigation demonstrate the influence of the transverse cracking on the bearing capacity and resistance to damage as well as its effects on the variation of the mechanical properties such as Young's modulus, Poisson's ratio and coefficient of thermal expansion. The results obtained are in good agreement with those predicted by the Shear-lag analytical model as well as with the obtained experimental results available in the literature.
Keywords
cross-ply laminate; thermo-mechanical properties; Shear-lag analysis; transverse cracking; finite element method (FEM);
Citations & Related Records
Times Cited By KSCI : 5  (Citation Analysis)
연도 인용수 순위
1 Ait Yahia, S., Ait Atmane, H., Houari, M.S.A. and Tounsi, A. (2015), "Wave propagation in functionally graded plates with porosities using various higher-order shear deformation plate theories", Struct. Eng. Mech., 53(6), 1143-1165.   DOI
2 Amara, Kh., Tounsi, A., Megueni, A. and Adda-Bedia, E.A. (2006), "Effect of transverse cracks on the mechanical properties of angle-ply composites laminates", Theor. Appl. Fract. Mech., 45(1), 72-78.   DOI
3 Berthelot, J.M. and Le Corre, J.F. (1999), "Modelling the transverse cracking in cross-ply laminates: application to fatigue", Compos. Part B: Eng., 30(6), 569-577.   DOI
4 Berthelot, J.M. and Le Corre, J.F. (2000), "A model for transverse cracking and delamination in cross-ply laminates", Compos. Sci. Tech., 60(7), 1055-1066.   DOI
5 Berthelot, J.M. and Le Corre, J.F. (2001), "Fissuration transverse et delaminage dans les stratifies croises, essais monotones et essais de fatigue", $XV^e$ Congres francais de mecanique, Nancy, Institut d'Acoustique et de Mecanique, Universite du Maine. (in French)
6 Berthelot, J.M., El Mahi, A. and Leblond, P. (1996), "Transverse cracking of cross-ply laminates: Part 2, Progressive widthwise cracking", Compos. Part A: Appl. Sci. Manuf., 27(10), 1003-1010.   DOI
7 Bourada, M., Kaci, A., Houari, M.S.A. and Tounsi, A. (2015), "A new simple shear and normal deformations theory for functionally graded beams", Steel Compos. Struct., 18(2), 409 - 423.   DOI
8 Brighenti, R., Carpinteri, A. and Scorza, D. (2013), "Fracture mechanics approach for a partially debonded cylindrical fiber", Compos. Part B: Eng., 53, 169-178.   DOI
9 Brighenti, R., Carpinteri, A. and Scorza, D. (2013), "Stress-intensity factors at the interface edge of a partially detached fibre", Theoretical and Applied Fracture Mechanics, 67-68, 1-13.   DOI
10 Brighenti, R., Carpinteri, A. and Scorza, D. (2016), "Mechanics of interface debonding in fiber-reinforced materials", J. Compos. Mater., 50(19), 2699-2718.   DOI
11 Brighenti, R., Carpinteri, A. and Scorza, D. (2016), "Micromechanical crack growth-based fatigue damage in fibrous composites", Int. J. Fatig., 82, 98-109.   DOI
12 Farahani, H. and Barati, F. (2015), "Vibration of sumberged functionally graded cylindrical shell based on first order shear deformation theory using wave propagation method", Struct. Eng. Mech., 53(3), 575-587.   DOI
13 Groves, S.E., Haris, C.E., Highsmith, A.L., Allen, D.H. and Norvell, R.G. (1987), "An experimental and analytical treatment of matrix cracking in cross-ply lamiantes", Exp. Mech, 27(1), 73-79.   DOI
14 Gu, Q. and Reddy, J.N. (1992), "Non-linear analysis of free-edge effects in composite laminates subjected to axial loads", Int. J. Nonlin. Mech., 27(1), 27-41.   DOI
15 Hashin, Z. (1988), "Thermal expansion coefficients of cracked laminates", Compos. Sci. Tech., 31(4), 247-260.   DOI
16 Henaff-Gardin, C. and Lafarie-Frenot, M.C. (2002), "The use of a characteristic damage variable in the study of transverse cracking development under fatigue loading in cross-ply laminates", Int. J. Fatig., 24(2-4), 389-395.   DOI
17 Henaff-Gardin, C., Lafarie-Frenot, M.C. and Gamby, D. (1996), "Doubly periodic matrix cracking in composite laminates Part 1: General in-plane loading", Compos. Struct., 36(1-2), 113-130.   DOI
18 Henaff-Gardin, C., Lafarie-Frenot, M.C. and Gamby, D. (1996), "Doubly periodic matrix cracking in composite laminates Part 2: Thermal biaxial loading", Compos. Struct., 36(1-2), 131-140.   DOI
19 Joffe, R. and Varna, J. (1999), "Analytical modeling of stiffness reduction in symmetric and balanced laminates due to cracks in $90^{\circ}$ layers", Compos. Sci. Tech., 59(11), 1641-1652.   DOI
20 Joffe, R., Krasnikovs, A. and Varna, J. (2001), "COD-based simulation of transverse cracking and stiffness reduction in $[S/90_n]_s$ laminates", Compos. Sci. Tech., 61(5), 637-656.   DOI
21 Kashtalyan, M. and Soutis, C. (2000), "Stiffness degradation in cross-ply laminates damaged by transverse cracking and splitting", Compos. Part A: Appl. Sci. Manuf., 31(4), 335-351.   DOI
22 Katerlos, D.T.G., Kashtalyan, M., Soutis, C. and Galiotis, C. (2008), "Matrix cracking in polymeric composites laminates: Modelling and experiments", Compos. Sci. Tech., 68(12), 2310-2317.   DOI
23 Leblond, P., El Mahi, A. and Berthelot, J.M. (1996), "2D and 3D numerical models of transverse cracking in cross-ply laminates", Compos. Sci. Tech., 56(7), 793-796.   DOI
24 Li, D.S. and Wisnom, M.R. (1997), "Evaluating weibull parameters for transverse cracking in cross-ply laminates", J. Compos. Mater., 31, 935-951.   DOI
25 Lim, S.G. and Hong, C.S. (1989), "Effect of transverse cracks on the thermomechanical properties of cross-ply laminated composites", Compos. Sci. Tech., 34(2), 145-162.   DOI
26 McCartney, L.N., Schoeppner, G.A. and Becker, W. (2000), "Comparison of models for transverse ply cracks in composite laminates". Compos. Sci. Tech., 60(12-13), 2347-2359.   DOI
27 Nguyen, K.T., Thai, T.H. and Vo, T.P. (2015), "A refined higher-order shear deformation theory for bending, vibration and buckling analysis of functionally graded sandwich plates", Steel Compos. Struct., 18(1), 91-120.   DOI
28 Rebiere, J.L. (2009), "Evolution De L'endommagement Par Fissuration Et Delaminage Dans Des Stratifies Croises A L'aide D'une Approche Variationnelle", Conference: JNC 16- seiziemes journees nationales sur les composites, at Toulouse, Institut d'Acoustique et de mecanique, Universite du Maine. (in French)
29 Rebière, J.L. and Gamby, D. (2008), "A decomposition of the strain energy release rate associated with the initiation of transverse cracking, longitudinal cracking and delamination in cross-ply laminates", Compos. Struct., 84(2), 186-197.   DOI
30 Rebiere, J.L. and Gamby, D. (2004), "A criterion for modelling initiation and propagation of matrix cracking and delamination in cross-ply laminates", Compos. Sci. Tech., 64(13-14), 2239-2250.   DOI
31 Rebiere, J.L., Maatallah, M.N. and Gamby, D. (2001), "Initiation and growth of transverse and longitudinal cracks in composite cross-ply laminates", Compos. Struct., 53(2), 173-187.   DOI
32 Rebiere, J.L., Maatallah, M.N. and Gamby, D. (2002), "Analysis of damage mode transition in a cross-ply laminate under uniaxial loading", Compos. Struct., 55(1), 115-126.   DOI
33 Sayyad, A.S. and Ghugal, Y.M. (2015), "Flexure of cross-ply laminated plates using equivalent single layer trigonometric shear deformation theory", Struct. Eng. Mech., 51(5), 867-891.   DOI
34 Sun, Z., Daniel, I.M. and Luo, J.J. (2003), "Statistical damage analysis of transverse cracking in high temperature composite laminates", Mater. Sci. Eng. A, 341(1), 49-56.   DOI
35 Tounsi, A., Amara, K.H., Benzair, A. and Megueni, A. (2006), "On the transverse cracking and stiffness degradation of aged angle-ply laminates", Mater. Lett., 60(21-22), 2561-2564.   DOI
36 Yang, T., Liu, Y. and Wang, J. (2003), "A study of the propagation of an embedded crack in a composite laminate of finite thickness", Compos. Struct., 59(4), 473-479.   DOI