Surface Diffusion Coefficients of Adatoms on Strained Overlayers

Adatom kinetics on the surfaces of Co overlayers, prepared on the W(110) surface, was studied with scanning tunneling microscopy. By counting the number-density of the adatom-islands, we estimated the ratio of adatom diffusion coefficients. The ratio $D_{W(110)}:D_{1ML\;Co}:D_{2ML\;Co}$ was measured to be 1 : 125 : 33000 at room temperature, where $D_{W(110)},\;D_{1ML\;Co}$, and $D_{2ML\;Co}$ are the diffusion coefficients on bare W(110) surface, on one-monolayer Co overlayer, and on two-monolayers Co overlayers, respectively. An increased diffusion coefficient on two-ML Co overlayers, relative to that on one-ML Co overlayers, was explained with the heteroepitaxial strain effect.

스트레인을 받고 있는 표면에서의 원자 확산계수

W(110) 표면에 성장한 Co 박막에서 원자 정역학을 주사터널링 현미경으로 연구했다. 원자섬의 개수 밀도를 측정하여 원자 확산 계수의 비를 알 수 있었다. W(110) 표면, Co가 1 원자층 성장된 표면, Co가 2 원자층 성장된 표면의 원자 확산 계수의 비는 상온에서 1:124:33000인 것으로 측정되었다. Co가 2 원자층 성장된 표면의 확산 계수가 Co 가 1 원자층 성장된 표면의 확산 계수보다 큰 것은 이종성장의 스트레인 효과로 인한 것으로 해석되었다.