Properties of Static Dissipative Epoxy Composites Loaded with Silane Coupled-ATO Nanoparticles

For purpose of anti-static film remaining unchanged in the condition of $160^{\circ}C$, organic solvent, acid and base solution $0.01\sim0.03{\mu}m$ particles of Sb doped tin oxide(ATO) were grafted by 3-Glycidyloxypropyltrimethoxysilane(GPTS) for improving interfere bonding force between ATO and epoxy resin. The particles were dispersed in 2-methoxyethanol with YD-I28(Bisphenol A type epoxy resin, Kukdo chemical) and 1-imidazole as hardener. The anti-static solutions were coated on PI film as thickness of $0.1{\mu}m$. Surface resistivity of anti-static film containing conductive polymer became $10^{12}\Omega/\Box$ after 32 hours in $160^{\circ}C$. The surface resistivity of ATO grafted by GPTS / Epoxy coating layer remained as $10^{7.6}\Omega/\Box$ in $160^{\circ}C$ for 7 days. ATO grafted by GPTS / Epoxy coating layer coated on PI film was dipped in acetone for 7 days. The surface resistivity remained unchanged as $10^{7.6}\Omega/\Box$. The anti-static layer dipped in water solutions containing each KOH 10 wt % and $H_2SO_4$ 2 wt% was ultra-sonicated for 10 minutes per once until 30th. The surface resistance of anti-static layer containing ATO grafted by GPTS remained unchanged.

Silane Coupling제로 표면 처리된 ATO 나노입자를 이용하여 제조된 대전방지 ATO/EPOXY 복합체의 코팅 물성