Use of Core-Crosslinked Amphiphilic Polymer Nanoparticles as Templates for Synthesis of Nanostructured Inorganic Materials

In this study, physically and chemically stable core-crosslinked amphiphilic polymer (CCAP) nanoparticles were prepared using amphiphilic reactive precursors via soap-free emulsion process. Obtained CCAP nanoparticles were used as templates for synthesis of nanostructured $TiO_2$ nanoparticles. First, CCAP nanoparticles dispersed aqueous solutions were mixed with titanium isopropoxide to prepare stable organic-inorganic hybrid sols, and then obtained sols were spin coated onto glass substrate to prepare hybrid thin films onto glass, and then hybrid thin films were calcinated at various temperature to remove CCAP. Nanostructure of calcinated thin fims were examined by SEM. To study effect of CCAP nanoparticles on nanostructure of $TiO_2$ nanoparticles, the morphology of $TiO_2$ nanoparticles prepared using various CCAP templates was compared with that of $TiO_2$ nanoparticles prepared using conventional organic template, nonionic surfactant, Triton X-100.

코아 가교 양친성 고분자 나노입자 템플레이트를 이용한 무기물 나노 구조체 합성

본 연구에서는 양친성 반응성 고분자 전구체를 합성하고 이를 사용하여 화학적, 물리적으로 안정한 코아 가교 양친성 고분자(Core-crosslinked Amphiphilic Polymer; 이하 CCAP) 나노입자를 제조하였으며, CCAP 나노입자를 $TiO_2$ 나노입자 제조의 템플레이트로 응용하였다. 먼저 CCAP 나노입자 수용액과 티타늄 이소프로폭사이드(Titanium isopropoxide)를 혼합하여, 매우 안정한 유/무기 나노하이브리드 솔(Sol)을 제조하였으며, 제조된 솔(Sol)은 회전코팅(Spin coating) 기법을 통해 유/무기 하이브리드 박막으로 제조하고, 소결 공정을 통해서 템플레이트인 CCAP를 제거하여 제조된 $TiO_2$ 나노입자의 미세구조를 주사전자현미경(SEM)을 이용하여서 관찰하였다. 다양한 CCAP 나노입자를 템플레이트로 사용하여 제조된 $TiO_2$ 나노입자의 미세구조를 기존 유기물 템플레이트(계면활성제)를 사용하여 제조된 $TiO_2$ 나노입자의 미세구조와 비교하여, CCAP 나노입자가 $TiO_2$ 나노입자 구조에 미치는 영향을 조사하였다.