Effect of the Low Profile Agent and Release Agent on the Surface Morphology and Property of Bulk Mold Compound

The effect of low profile agent and release agent on the surface and mechanical properties of bulk mold compound were investigated. Atomic content and contact angle of surface were characterized using X-ray photoelectron spectroscopy and contact anglemeter. Surface morphology and surface roughness were obtained using field emission scanning electron microscope and atomic force microscope, respectively. As increasing the low profile agent from 0 to 9.2 wt%, the volume shrinkage and surface roughness decreased from 0.35% to 0.05%, and from $0.27{\mu}m$ to $0.12{\mu}m$, respectively. The increase of release agent from 1.8 wt% to 3.6 wt% resulted in the migration of release agent to sample surface and it increased the surface roughness. The flexural strength and impact strength were decreased approximately 30% as the low profile agent increasing from 5.0 wt% to 9.0 wt%.

저수축제 및 이형제가 벌크몰드컴파운드의 표면형태 및 물성에 미치는 영향

폴리스티렌을 저수축제로 사용하고 Zn-stearate를 이형제로 사용하여 함량변화에 따라 벌크 몰드컴파운드의 표면형태 및 기계적 물성에 미치는 영향을 고찰하였다. XPS, 접촉각 측정기 등을 이용하여 표면과 깊이 방향에 대한 원소함량과 접촉각을 측정하였고, 표면형태는 FESEM을 이용하여 관찰하였으며, 표면조도 측정은 AFM을 이용하였다. 저수축제를 첨가하지 않은 경우에 비교하여 저수축제를 9.0 wt% 첨가하였을 경우에는 체적수축률은 0.35%에서 0.05%로 감소하였으며, 표면조도는 $0.27{\mu}m$에서 $0.12{\mu}m$로 감소하였다. 이형제의 함량을 1.8 wt%에서 3.6 wt%로 증가시켰을 경우에는 이형제가 주로 표면에 존재하고 표면조도를 증가시키는 것을 확인하였다. 저수축제의 함량을 5.0 wt%에서 9.0 wt%로 증가시킴에 따라 굴곡탄성율과 충격강도가 약 30% 감소하였다.