Reviews on Very High Cycle Fatigue Behaviors of Structural Metals  

Han, Seung-Wook (Department of Mechanical Engineering, Graduate School, Hanyang University)
Park, Jung-Hoon (Department of Mechanical Engineering, Graduate School, Hanyang University)
Myeong, No-Jun (Department of Mechanical Engineering, Graduate School, Hanyang University)
Choi, Nak-Sam (Department of Mechanical Engineering, Hanyang University)
Publication Information
Transactions of the Korean Society of Automotive Engineers / v.22, no.2, 2014 , pp. 134-140 More about this Journal
Abstract
The paper presents an overview of the present state of study on the fatigue behaviors at very high number of cycles ($N_f$ > $10^7$). A classification of materials with typical S-N curves and influencing factors such as notches, residual stresses, temperatures, corrosion environments and stress ratios are given. The microstructural inhomogeneities of materials and micro-cracks played an important roles in very high cycle fatigue behaviors. The failure mechanisms for the fatigue design of materials and components are mentioned.
Keywords
Very high cycle fatigue; S-N curves; Fatigue strength; Fatigue fracture; Failure mechanism;
Citations & Related Records
Times Cited By KSCI : 1  (Citation Analysis)
연도 인용수 순위
1 Y. S. Pyoun and I. S. Cho, "Application of Ultrasonic Nano Crystal Surface Modification Technology for Increasing the Fatigue Strength, Weight Reduction and Decreasing the Friction Loss," KSAE Fall Conference Proceedings, pp.929-938, 2007.
2 T. Sakai, "Review and Prospects for Current Studies on Very High Cycle Fatigue of Metallic Materials for Machine Structural Use," Journal of Solid Mechanics and Materials Engineering, Vol.3, No.3, pp.425-439, 2009.   DOI
3 Design of Steel Structures, Part 1-9: Fatigue, CEN European Committee for Standardization, Eurocode 3, 1993.
4 A. Amanov, I. S. Cho, J. Y. Lee, C. S. Lee, Y. S. Pyoun and I. G. Park, "Effect of Ultrasonic Nanocrystalline Surface Modification on Very High Numbers of Cycles Fatigue of Al6061-T6 Alloy," Fifth International Conference on Very High Cycle Fatigue, pp.405-410, 2011.
5 H. Mughrabi, "Specific Features and Mechanisms of Fatigue in the Ultrahighcycle Regime," Int. J. Fatigue, Vol.28, No.11, pp.1501-1508, 2006.   DOI
6 H. Mughrabi and S. Stanzl-Tschegg, "Fatigue Damage Evolution in Ductile Singlephase Facecentred Cubic Metals in the UHCF-regime," Proc. VHCF 4. Ann Arbor, pp.75-82, 2007.
7 A. Weidner, D. Amberger, F. Pyczak, B. Schonbauer, S. Stanzl-Tschegg and H. Mughrabi, "Fatigue Damage in Copper Polycrystals Subjected to Ultrahigh-cycle Fatigue Below the PSB Threshold," International Journal of Fatigue, Vol.32, No.6, pp.872-878, 2010.   DOI   ScienceOn
8 T. Sakai, M. Takeda, K. Shiozawa, Y. Ochi, T. Nakajima and N. Oguma, "Experimental Reconfirmation of Characteristic S-N Property for High Carbon Chromium Bearing Steel in Wide Life Region in Rotating Bending," Journal of the Society of Materials Science, Vol.49, No.7, pp.779-785, 2000.   DOI   ScienceOn
9 H. Tian, M. Kirkham, L. Jiang, B. Yang, G. Wang and P. Liaw, "A Review of Failure Mechanisms of Ultra High Cycle Fatigue in Engineering Materials," Proc. VHCF 4. Ann Arbor, pp.437-444, 2007.
10 C. Bathias and P. Paris, Gigacycle Fatigue in Mechanical Practice, CRC Press, USA, 2004.
11 K. Tanaka and T. Mura, "A Theory of Fatigue Crack Initiation at Inclusions," Metall. Trans., Vol.13A, No.1, pp.117-123, 1982.
12 Y. Murakami, T. Nomoto and T. Ueda, "Factors Influencing the Superlong Fatigue Failure in Steels," Fatigue Fract Eng Mater Struct, Vol.22, No.7, pp.581-590, 1999.   DOI
13 T. Sakai, H. Harada and N. Oguma, "Crack Initiation Mechanism of Bearing Steel in Very High Cycle Fatigue," Proceedings of ECF-16, CD-ROM, 2006.
14 Y. Akiniwa, N. Miyamoto, H. Tsuru and K. Tanaka, "Notch Effect on Fatigue Strength Reduction of Bearing Steel in the Very High Cycle Regime," Int. J. Fatigue, Vol.28, No.11, pp.1555-1565, 2006.   DOI
15 I. S. Cho, C. S. Shin, J. Y. Kim and Y. H. Jeon, "Accelerated Ultrasonic Fatigue Testing Applications and Research Trends," Trans. Korean Soc. Mech. Eng. A, Vol.36, Issue. 6, pp.707-712, 2012.   과학기술학회마을   DOI   ScienceOn
16 H. Mughrabi, "On 'Multi-stage' Fatigue Life Diagrams and the Relevant Lifecontrolling Mechanisms in Ultrahigh-cycle Fatigue," Fatigue Fract Eng Mater Struct, Vol.25, No.8, pp.755-764, 2002.   DOI
17 X. Zhu, A. Shyam, J. W. Jones, H. Mayer, J. V. Lasecki and J. E. Allison, "Effects of Microstructure and Temperature on Fatigue Behavior of E319-T7 Cast Aluminum Alloy in Very Long Life Cycles," International Journal of Fatigue, Vol.28, No.11, pp.1566-1571, 2006.   DOI
18 G. M. D. Almaraz, J. L. A. Ambriz and E. C. Calderon, "Fatigue Endurance and Crack Propagation under Rotating Bending Fatigue Tests on Aluminum Alloy AISI 6063-T5 with Controlled Corrosion Attack," Engineering Fracture Mechanics, Vol.93, pp.119-131, 2012.   DOI
19 S. Kovacs, T. Beck and L. Singheiser, "Influence of Mean Stresses on Fatigue Life and Damage of a Turbine Blade Steel in the VHCF-regime," International Journal of Fatigue, Vol.49, pp.90-99, 2013.   DOI