Photoluminescence Characteristics of the ZnGa2O4 Phosphor Thin Films as a Function of Post-annealing Temperature

$ZnGa_2O_4$ thin film phosphors have been deposited using a pulsed laser deposition method on Si(100) substrates at a substrate temperature of $550^{\circ}C$ with oxygen pressures of 100mTorr, and subsequently to investigate their photoluminescence characteristics after post-annealed at $600^{\circ}C$ and $700^{\circ}C$. As a result for X-ray diffraction, $Ga_2O_3$ shape appeared with increasing annealing temperature. The luminescent spectra show a broad band extending from 350 to 600nm peaking at 460nm. A post-annealing treatment of $ZnGa_2O_4$ thin films led to the different shape of luminescent intensity and grain size.

후열처리 온도에 따른 ZnGa2O4 형광체 박막의 발광 특성

$ZnGa_2O_4$박막 형광체는 기판 온도 $550^{\circ}C$, 산소 분압 100mTorr에서 Si(100) 기판 위에 펄스레이저 증착법을 이용하여 증착시켰고, 이렇게 증착되어진 박막을 $600^{\circ}C$와 $700^{\circ}C$에서 후 열처리하여 발광 특성을 조사하였다. X-선 회절 실험 결과, 후열처리 온도를 증가시킴에 따라서 $Ga_2O_3$ 상이 나타남을 확인할 수 있었다. 발광 스펙트럼은 460nm에서 최고 피크값을 나타내었으며. 350에서 600nm까지 갖는 넓은 밴드의 발광 특성을 나타내었다. 후열처리에 따른 $ZnGa_2O_4$ 박막은 다른 형태의 발광 강도와 grain 크기를 나타내었다.