Effect of Hot-Pressing Time and Temperature on Properties of Bamboo Zephyr Boards

In this research, in order to investigate the effect of hot-pressing condition, properties of bamboo zephyr boards (target density 0.7 g/cm³, 400×400×12 mm) produced by different hot-pressing time and temperature were compared through Korean Standard(KS) F 3104 and F 3113, and the results were summarized as follows: All of the boards had comparatively high values in bending properties (MOR, MOE) irrespective of hot-pressing condition, and the boards hot-pressed by 160℃ and 12 min showed the highest strength in parallel direction of board-surface to span. Internal bond (IB) strength of the boards generally increased with the increase of hot pressing temperature. Boards produced by hot pressing temperature and time of 160℃ and 12 min and 180℃ and 10 min exhibited relatively higher wet-bending strength. Thickness swelling (TS) of all the boards showed good dimensional stability of 6% or less.

대나무 Zephyr 보드의 제조에 있어서 열압시간과 열압온도가 보드성능에 미치는 영향

본 연구에서는 대나무 Zephyr 보드에 있어서 열압조건이 보드의 성능에 미치는 영향을 조사하기 위하여 다양한 열압시간과 열압온도를 적용하여 보드(목표밀도 0.7 g/cm³, 400×400×12 mm)를 제조하고 그 기본적인 물성을 비교, 검토해 보았다. 제조된 보드는 KS F 3104와 KS F 3113에 준하여 성능평가를 하였으며 그 결과는 다음과 같다. 보드의 상태 휨강도는 열압조건에 관계없이 전반적으로 상당히 높은 값을 나타내었으며 그 중 span에 대한 평행 방향에 있어서는 열판온도 160℃에서 12분 동안 열압하여 제조한 보드가 가장 높은 강도를 보였다. 보드의 박리강도 시험에서는 모든 열압시간에서 열압온도가 높을수록 상대적으로 더 높은 값을 나타내었으며, 그 결과 200℃에서 압체된 보드가 가장 높은 강도를 보였다. 보드의 습윤 휨강도 시험에서는 총 열압시간 12분과 10분일 때 각각 160℃와 180℃의 온도에서 제조된 보드가 상대적으로 높은 강도를 나타내었다. 더욱이, 200℃에서 8분 동안 열압하여 제조한 보드의 경우 상태 휨강도에 거의 육박하는 가장 높은 습윤 휨강도를 보였다. 두께 팽창율 시험에서는 모든 보드에서 전반적으로 6% 미만의 낮은 값을 나타내어 높은 치수안정성을 가지는 것을 알 수 있었다.