Effects of Si Content on the Microstructure and Processing Window of Austempered Ductile Cast Iron

The effects of Si content on the variation of microstructure and processing window of austempered ductile cast iron were investigated. Four different Si contents between 2.42 and 3.37 wt.% were used. The influence of silicon on the microstructure and processing window of these materials were studied. Austenitizing was performed at $900^{\circ}C$ for 60min and austempering temperature were both $340^{\circ}C$ and $360^{\circ}C$ and austempering time were for 4min upto 119min and for 5min upto 160min respectively. After heat treatment, the evolution of stage I and stage II were performed by optical metallography, XRD, hardness test. The results showed that $t_2$ was delayed as Si contents was increased due to the fact that Si retarded the formation of cementite ($Fe_3C$). The high silicon content promoted the stability of the metastable two-phase combination of austenite and ausferrite.

오스템퍼드 구상흑연주철의 미세조직과 프로세싱 윈도우에 미치는 규소 함량의 영향