Temperature Dependence of Cr Impurity in La0.6Sr0.4Ti0.3Fe0.7O3-δ Coated Ba0.5Sr0.5Co0.8Fe0.2O3-δ Ion Conducting Membrane for oxygen Separation  

Park, Yu Gang (Department of Chemical and Biochemical Engineering, Dongguk university)
Park, Jung Hoon (Department of Chemical and Biochemical Engineering, Dongguk university)
Publication Information
Korean Chemical Engineering Research / v.57, no.1, 2019 , pp. 11-16 More about this Journal
Abstract
$La_{0.6}Sr_{0.4}Ti_{0.3}Fe_{0.7}O_{3-{\delta}}$(LSTF) coated $Ba_{0.5}Sr_{0.5}Co_{0.8}Fe_{0.2}O_{3-{\delta}}$(BSCF) membranes which has properties of high oxygen permeability and stability to $CO_2$ were applied to a bench scale apparatus to conduct oxygen permeation experiments. Also, the membranes of the laboratory and the bench scale device were divided into three regions according to the temperature gradient in the membrane reactor for comparative analysis. While oxygen permeation experiment were conducted up to $900^{\circ}C$, temperature dependence of Cr deposition was investigated. As a result, it was confirmed that the oxygen permeability was $2.37ml/min{\cdot}cm^2$, which was significantly lower than $3.79ml/min{\cdot}cm^2$ measured in the laboratory apparatus. It was found through XRD and SEM/EDS analysis that the decrease in oxygen permeability was originated from the deposition of gaseous Cr on the membrane surface released from the alloy material of the housing. In particular, a large amount of Cr was found in the medium temperature region.
Keywords
Perovskite; Membrane; Oxygen separation; BSCF; Cr impurity;
Citations & Related Records
Times Cited By KSCI : 1  (Citation Analysis)
연도 인용수 순위
1 Sunarso, J., Baumannn, S., Serra, J. M., Meulenberg, W. A., Liu, S., Lin, Y. S. and Diniz da costa, J. C., "Mixed Ionic-electronic Conducting (MIEC) Ceramic-based Membranes for Oxygen Separation," Journal of Membrane Science, 320, 13-41(2008).   DOI
2 Shao, Z., Yang, W., Cong, Y., Dong, H., Tong, J. and Xiong, G., "Investigation of the Permeation Behavior and Stability of a $Ba_{0.5}Sr_{0.5}Co_{0.8}Fe_{0.2}O_{3-{\delta}}$ Oxygen Membrane," Journal of Membrane Science, 172, 177-188(2000).   DOI
3 Park, J, H., Magnone, E., Kim, J, P. and Choi, S, H., "Oxygen Permeation Performance of $Ba_{0.5}Sr_{0.5}Co_{0.8}Fe_{0.2}O_{3-{\delta}}$ Membrane After Surface Modification," Korean Journal of Chemical Engineering, 29(2), 235-242(2012).   DOI
4 Wang, H., Cong, Y. and Yang, W., "Oxygen Permeation Study in a Tubular $Ba_{0.5}Sr_{0.5}Co_{0.8}Fe_{0.2}O_{3-{\delta}}$ Oxygen Permeable Membrane," Journal of Membrane Science, 210, 259-271(2002).   DOI
5 Kharton, V. V., Yaremchenko, A. A., Kovalevsky, A. V., Viskup, A. P., Naumovich, E. N. and Kerko, P. F., "Perovskite-type Oxides for High-temperature Oxygen Separation Membranes," Journal of Membrane Science, 163, 307-317(1999).   DOI
6 Lee, S. W., Kim, E. J., Lee, H. J. and Park, J. H., "Preparation of the Hollow Fiber Type Perovskite Catalyst for Methane Complete Oxidation," Korean Chemical Engineering Research, 56(3), 297-302(2018).   DOI
7 Gindorf, C., Singheiser, L. and Hilpert, K., "Vaporisation of Chromia in Humid Air," Journal of Physics and Chemistry of Solids, 66, 384-387(2005).   DOI
8 Yang, Z., Harvey, A. S. and Gauckler, L. J., "Influence of $CO_2$ on $Ba_{0.2}Sr_{0.8}Co_{0.8}Fe_{0.2}O_{3-{\delta}}$ at Elevated Temperatures," Scripta Materialia, 61, 1083-1086(2009).   DOI
9 Stanislowski, M., Froitzheim, J., Niewolak, L., Quadakkers, W. J., Hilpert, K., Markus, T. and Singheiser, L., "Reduction of Chromium Vaporization from SOFC Interconnectors by Highly Effective Coatings," Journal of Power Sources, 164, 578-589(2007).   DOI
10 Kim, Y. M., Chen, X., Jiang, S. P. and Bae, J., "Effect of Strontium Content on Chromium Depositin and Poisoning in $Ba_{1-x}Sr_{x-}Co_{0.8}Fe_{0.2}O_{3-{\delta}}$ ($0.3{\leq}x{\leq}0.7$) Cathodes of Solid Oxide Fuel Cells," Journal of The Electrochemical Society, 159, B185-B194(2012).
11 Park, J. H., Kim, J. P. and Son, S. H., "Oxygen Permeation and Stability of $Ba_{0.5}Sr_{0.5}Co_{0.8}Fe_{0.2}O_{3-{\delta}}$ Membrane According to Trace Elements and Oxygen Partial Pressure in Synthetic Air," Energy Procedia, 1, 369-374(2009).   DOI
12 Park, J. H., Kim, K. Y. and Park, S. D., "Oxygen Permeation and Stability of $La_{0.6}Sr_{0.4}TixFe_{1-x}O_{3-{\delta}}$ (x=0.2 and 0.3) Membrane," Desalination, 245, 559-569(2009).   DOI
13 Kim, J. P., Magnone, E., Park, J. H. and Lee, Y., "Oxygen Production of Tubular Module with $La_{0.6}Sr_{0.4}Ti_{0.3}Fe_{0.7}O_{3-{\delta}}$ Coated $Ba_{0.5}Sr_{0.5}$ $Co_{0.8}Fe_{0.2}O_{3-{\delta}}$ Membrane," Journal of Membrane Science, 403, 188-195(2012).   DOI
14 Kim, J. P., Magnone, E., Seo, M. J. and Park, J. H., "Development of Novel Chromium-tolerate Barium-chromium Oxide Coated BSCF Membrane for Oxygen Separation," Materials Letters, 93, 383-385(2013).   DOI
15 Kim, J. P., Park, J. H., Magnone, E. and Lee, Y., "Significant Improvement of the Oxygen Permeation Flux of Tubular $Ba_{0.5}Sr_{0.5}Co_{0.8}Fe_{0.2}O_{3-{\delta}}$ Membrane Covered by a thin $La_{0.6}Sr_{0.4}Ti_{0.3}Fe_{0.7}O_{3-{\delta}}$ Layer," Materials Letters, 65, 2168-2170(2011).   DOI
16 Kim, J. P., Park, J. H., Lee, Y. and Choi, Y. J., "Oxygen Permeation Properties of Tubular $Ba_{0.5}Sr_{0.5}Co_{0.8}Fe_{0.2}O_{3-{\delta}}$ (BSCF) Membranes Under Different Condition of Feed Side and Permeate Side," Membrane Journal, 21, 155-162(2011).
17 Tan, X., Pang, Z. and Li, K., "Oxygen Production Using $La_{0.6}Sr_{0.4}Co_{0.2}Fe_{0.8}O_{3-{\alpha}}$ (LSCF) Perovskite Hollow Fibre Membrane Modules," Journal of Membrane Science, 310, 550-556(2008).   DOI
18 Al-Hajji, L. A., Hasan, M. A. and Zaki, M. I., "Characterization Studies of Physicochemical Modifications Conceded by Equimolar-mixed Chromia and Barium Carbonate Powders as a Function of Temperature," Thermochimica Acta, 483, 8-14(2009).   DOI