The Effect of Fretting Wear on Fatigue Crack Initiation Site of Press-fitted Shaft  

Lee, Dong-Hyong (한국철도기술연구원, 철도시스템연구본부)
Kwon, Seok-Jin (한국철도기술연구원, 철도시스템연구본부)
Choi, Jae-Boong (성균관대학교, 기계공학부)
Kim, Young-Jin (성균관대학교, 기계공학부)
Publication Information
Journal of the Korean Society for Railway / v.10, no.5, 2007 , pp. 546-553 More about this Journal
Abstract
The objective of the present paper is to evaluate the effect of the evolution of contact surface profile by fretting wear on the contact stress distribution and fatigue crack initiation site of press-fitted shaft by means of an analytical method based on experimental data. A finite element analysis was performed to analyze the stress states of press-fitted shaft, considering the worn contact surface profiles of shaft. The evolutions of contact stress as wearing of contact surface were analyzed by finite element analysis and fatigue crack nucleation sites were evaluated by fretting fatigue damage parameter (FFDP) md multiaxial fatigue criteria. It is found that the stress concentration of a contact edge in press-fitted sha손 decreases rapidly at the initial stage of total fatigue life, and its location shifts from the contact edge to the inside due to fretting wear as increasing of fatigue cycles. Thus the transition of crack nucleation position in press-fitted shaft is mainly caused by stress change of a contact edge due to the evolution of contact surface profile by fretting wear. Therefore, it is suggested that the nucleation of multiple cracks on fretted surface of press fits is strongly related to the evolution of surface profile at the initial stage of total fatigue life.
Keywords
Press-fitted shaft; Fatigue crack; Fretting wear;
Citations & Related Records
Times Cited By KSCI : 1  (Citation Analysis)
연도 인용수 순위
1 O. J. Horger (1956), 'Fatigue of Large Shafts by Fretting Corrosion,' Proc. Int. Conf. Fatigue Metals, pp.352-360
2 ABAQUS (2003), 'ABAQUS user's and theory manual', Version 6.4, Hibbit, Karlson & Sorensen, Inc
3 R. Kühnel (1932), 'Achsbrüche von Eisenbahnfahrzeugen und ihre Ursachen,' Glasers Annln, Gewerbe Bauw., Vol.110, p.39
4 R. B. Waterhouse (1992), 'Fretting fatigue,' International materials reviews, Vol.37, No.2, pp.77-97   DOI
5 機械.構造物の破損事例と解析技術'(1984), 日本機械學會
6 C. D. Lykins, S. Mall, and V. K. Jain (2001), 'Combined experimental-numerical investigation of fretting fatigue crack initiation,' Int. J. Fatigue, Vol.23, pp.703-711   DOI   ScienceOn
7 R. B. Waterhouse and D. E. Taylor (1971), 'The initiation of fatigue cracks in a 0:7% carbon steel by fretting,' Wear 17, pp.139-147   DOI   ScienceOn
8 R. I. Stephens, A. Fatemi, R.R. Stephens and H.O. Fuchs, Metal Fatigue in Engineering-2nd ed.: John Wiley & Sons, 2001
9 W. W. Maxwell, B. R. Dudley, A. B. Cleary, J. Richards, and J. Shaw (1967-68), 'Measures to Counter Fatigue Failure in Railway Axles,' Proc. Inst. Mech. Engrs., Vol.182, Pt.1, No.4, pp.89-99
10 K. Nishioka and K. Komatshu (1967), 'Study on the means for Improvement in Fatigue Strength of press-fitted axles,' Trans. Jpn. Soc. Mech. Eng., Vol.33, No.248, pp.503-511   DOI
11 S. Tanaka, K. Hatsuno, B. Mori, and S. Yaguchi (1975), 'Fretting Corrosion and Fatigue Strength for Wheel-seat of Car-Axle - Test Results of Full Size Wheel Axle Testing Machine - (Report 1),' Railway Technical Research Report, No.955
12 C. D. Lykins, S. Mall, and V. Jain (2000), 'An evaluation of parameters for predicting fretting fatigue crack initiation,' Int. J. Fatigue, Vol.22, pp.703-716   DOI   ScienceOn
13 R. A. Smith and S. Hillmansen (2004), 'A brief historical overview of the fatigue of railway axles,' Proc. Instn Mech. Engrs. Part F: J. Rail and Rapid Transit, Vol.218 No.4 pp.267-278   DOI   ScienceOn
14 D. H. Lee, S. J. Kwon, J. B. Choi, and Y. J. Kim (2006), 'Fatigue Life Evaluation of Press-fitted Shaft considering the Evolution of Contact Stress and Surface profile under Bending Load,' 9th International Fatigue Congress, CD-rom ver
15 K. Hirakawa, K. Toyama and M. Kubota (1998), 'The analysis and prevention of failure in railway axles,' Int. J. Fatigue, Vol.20, No.2, p.135   DOI   ScienceOn
16 A. C. Ugural and S. K. Fenster (1995), Advanced strength and applied elasticity: Prentice-Hall, Inc
17 이동형, 권석진, 최재붕, 김영진 (2007), '압입축에 발생하는 프레팅 피로균열 발생 및 진전특성 실험', 대한기계학회논문집 A권, Vol.31, No.6, pp.701-709   과학기술학회마을   DOI
18 T. Makino and M. Yamamoto and K. Hirakawa (1997), 'Effect of Contact Edge Profile on Fretting Fatigue Crack Initiation Site in Press-Fitted Axle,' Trans. Jpn. Soc. Mech. Eng. (A), Vol.63, No.615, pp.2312-2317   DOI
19 C. Ruiz and P. H. B. B. a. K.C.Chen (1984), 'An investigation of fatigue and fretting in a dovetail joint,' Experimental Mechanics, Vol.24, No.3, pp.208-217   DOI