The Effect of Crystallization of SLS Glass for Bulletproof Materials  

Shim, Gyu-In (Yonsei University)
Kim, Tae-Yoon (Yonsei University)
Choi, Se-Young (Yonsei University)
Publication Information
Journal of the Korea Institute of Military Science and Technology / v.13, no.1, 2010 , pp. 120-125 More about this Journal
Abstract
For application of transparent bulletproof materials, the SLS(soda-lime-silicate) glass was heated by 2-step crystallization. The DTA curve for SLS glass revealed the nucleation and crystal growth temperature at about $575^{\circ}C$ and $675^{\circ}C$, respectively. The crystallized glass was heated at various conditions(temperature, time). As a result, the maximum nucleation and crystal growth rates were $3.8\times10^5/mm^3{\cdot}hr$ at $575^{\circ}C$ and 20.58nm/min at $680^{\circ}C$, respectively. The bending strength, fracture toughness and vickers hardness were 451.7MPa, $0.9388MPa{\cdot}m^{1/2}$, and $693.9H_v$ which were 201%, 31%, and 22% higher than parent glass, respectively. Surface image and transmittance of crystallized SLS glass were analyzed by optical microscopy and UV/VIS/NIR spectrophotometer. Transmittance of crystallized SLS glass at visible-range(200~800nm) was not changed.
Keywords
SLS Glass Crystallization Bulletproof Nucleation; Crystal Growth;
Citations & Related Records
연도 인용수 순위
  • Reference
1 S. Y. Choi, G. H. Frischat, Influence of Crystallization on Some Properties of $ZrF_{4}-BaF_{2}-YF_{3}-AlF_{3}$ Glasses, J. Non-Cryst. Solids, Vol. 129, pp. 133-136, 1991   DOI   ScienceOn
2 H. J. Kim, M. K. Lee, S. Y. Choi, A Study on the Transparent Armor Materials with High Efficiency Nano Ceramics(Contract No. : UD080040GD), 2nd-Year Research Report of Agency for Defense Development, 2009.
3 S. M. Song, S. Y. Choi, Y. K. Lee, Crystallization Property Effects in Ge30Se60Te10 Glass, J. Non-Cryst. Solids, Vol. 217, pp. 79-82, 1997   DOI   ScienceOn
4 S. B. Sohn, Y. K. Lee, S. Y. Choi, Controlled Crystallization and Characterization of Cordierite Glass-Ceramics for Magnetic Memory Disk Substrate, Journal of Materials Science, Vol. 35, pp. 4815-4821, 2000.   DOI   ScienceOn
5 M. Suszy, L. Krajczyk and Z. Mazurkiewicz, TEM Studies of Silver Nanoparticles in Phase-Separated Soda Lime Silicate Glasses, Materials Chemistry and Physsics, Vol. 81, pp. 404-406, 2003.   DOI   ScienceOn
6 S. B. Sohn and S. Y. Choi, Crystallization Behavior in the Glass System $MgO-Al_{2}O_{3}-SiO_{2}$ : Influence of $CeO_{2}$ Addition, Journal of Non-Crystalline Solid, Vol. 282, pp. 221-227, 2001.   DOI   ScienceOn
7 M. Roskosz, M. J. Toplis and P. Richet, Kinetic vs. Thermodynamic Control of Crystal Nucleation and Growth in Molten Silicates, Journal of Non-Crystalline Solid, Vol. 352, pp. 180-184, 2006.   DOI   ScienceOn
8 V. P. Pukh, L. G. Baikova, M. F. Kireenko, L. V. Tikhonova, T. P. Kazannikova, and A. B. Sinani, Atomic Structure and Strength of Inorganic Glasses, Physis of the Solid State, Vol. 47, No. 5, pp. 876-881, 2005.   DOI