Synthesis and luminescent properties of a new green long persistent phosphors

Novel green long persistent phosphors of $CaZrO_3$ : $HO_{3+}$ have been synthesized at high temperature with weak reduction atmosphere by traditional solid state reaction method. The role of $H_3BO_3$ as flux and the suitable concentration of Ho as activator on the $CaZrO_3$ : $HO_{3+}$ long persistent phosphors has been investigated. Crystals of $HO_{3+}$ doped $CaZrO_3$ long persistent phosphores were characterized by fluorescence spectrophotometer and photoluminescence (PL). The main emission spectra of 546 nm peak was revealed through synthesizing at high temperature in $N_2$ gas atmosphere. The after glow emission spectra of $CaZrO_3$ : $HO_{3+}$ long persistent phosphores arise at 546 nm peak of narrow range. because that revealed pure green color. Green long persistent phosphors have been observed in the system for over 5 h after UV irradiation (254 nm). The main emission peak was ascribed to $HO_{3+}$ ions transition from $^5F_4$, $^5S_2{\to}^5I_3$, and the after glow may be ascribed to the trap centers in the $CaZrO_3$ host lattice.

녹색 발광의 축광성 형광체의 합성 및 발광 특성

새로운 녹색의 $CaZrO_3$ : $HO_{3+}$ 축광성 형광체를 고온의 약한 환원 분위기에서 전통적인 고상 반응법으로 합성하였다. $CaZrO_3$ : $HO_{3+}$ 축광성 형광체에 첨가 된 융제 $H_3BO_3$의 역할과 부활제의 적정농도에 대하여 연구하였으며, 합성한 축광성 형광체의 형광 분석 및 광 발광 분석을 행하였다. 고온의 질소 분위기에서 합성한 $CaZrO_3$ : $HO_{3+}$ 축광성 형광체는 546nm의 발광 피크가 나타남을 확인 하였으며, 장잔광 스펙트럼 또한 폭이 좁은 546 nm의 발광 피크가 나타남에 따라 순수한 녹색의 발광색을 띄고 있음을 확인하였다 녹색의 $CaZrO_3$ : $HO_{3+}$ 축광성 형광체의 발광 지속시간은 254 nm UV lamp로 여기 시킨 후 어두운 곳에서 5시간 이상 발광이 유지되었다. 발광 피크는 $HO_{3+}$ 이온의 $^5F_4$, $^5S_2{\to}^5I_3$ 전이에 의한 것이며, 잔광 특성은 $CaZrO_3$ 격자 내에 trap center가 생성됨 의하여 발생되는 것으로 판단된다.