Property of the Nano-Thick TiO2 Films Using an ALD at Low Temperature

We fabricated 10 nm-$TiO_2$ thin films for DSSC (dye sensitized solar cell) electrode application using ALD (atomic layer deposition) method at the low temperatures of $150^{\circ}\;and\;250^{\circ}$. We characterized the crosssectional microstructure, phase, chemical binding energy, and absorption of the $TiO_2$ using TEM, HRXRD, XPS, and UV-VIS-NIR, respectively. TEM analysis showed a 10 nm-thick flat and uniform $TiO_2$ thin film regardless of the deposition temperatures. Through XPS analysis, it was found that the stoichiometric $TiO_2$ phase was formed and confirmed by measuring main characteristic peaks of Ti $2p^1$, Ti $2p^3$, and O 1s indicating the binding energy status. Through UV-VIS-NIR analysis, ALD-$TiO_2$ thin films were found to have a band gap of 3.4 eV resulting in the absorption edges at 360 nm, while the conventional $TiO_2$ films had a band gap of 3.0 eV (rutile)${\sim}$3.2 eV (anatase) with the absorption edges at 380 nm and 410 nm. Our results implied that the newly proposed nano-thick $TiO_2$ film using an ALD process at $150^{\circ}$ had almost the same properties as thsose of film at $250^{\circ}$. Therefore, we confirmed that the ALD-processed $TiO_2$ thin film with nano-thickness formed at low temperatures might be suitable for the electrode process of flexible devices.

저온 ALD로 제조된 TiO2 나노 박막 물성 연구