A Study on the Properties of Fire Endurance and Spalling of High Performance RC Column with the Finishing and Covering Material

High performance concrete(HPC) has been widely used in high-rise building. The HPC has several benefits including high strength, high fluidity and high durability. However, spalling is susceptible to occur in HPC and HPC also tends to be deteriorated in the side of fire resistance performance at fire. This paper investigated the spalling prevention of high performance RC column. Control concrete showed severe failure and a case of concrete with fire enduring spraying material exhibited more severe spalling failure than even control concrete. In addition, concrete with fire enduring paint reported the most favorable spalling resistance effect for preventing spall, compared with other concrete covered with finishing materials, such as fire enduring spraying material, gypsum board, marble board and fire enduring PC board. Meanwhile, concrete adding 0.1% of PP fiber demonstrated spalling resistance performance after 3hours load bearing test.

고성능 RC 기둥의 마감재 변화에 따른 폭열 및 내화특성에 관한 연구

건축물의 초고층화에 따라 최근 고성능 콘크리트의 사용이 증가하고 있다. 이러한 고성능 콘크리트는 고강도, 고유동, 고내구성 등 다양한 성능을 발휘하지만, 화재시 폭열에는 약한 것으로 알려져 있다. 본 연구는 PP섬유 혼입 및 마감재 변화에 따른 고성능 RC 기둥의 폭열방지 성능을 검토한 것이다. 실험결과 내화시험 후 폭열특성으로, 먼저 플레인의 경우 심한 파괴 폭열과 함께 철근이 노출됐고 내화뿜칠로 마감한 고성능 콘크리트는 내부 수분의 영향으로 플레인보다 더욱 심한 폭열을 나타냈다. 또한, 마감재 변화에 따른 시험체의 폭열특성으로는 내화도료로 마감한 경우가 가장 우수한 폭열방지 효과를 나타냈으며 폴리프로필렌 섬유를 0.1%혼입한 콘크리트는 3시간 가력 내화시험 후 가장 안전한 폭열방지 성능을 입증하였다.