Structure and Magnetic Properties on Synthesis Route of Co2Z-type Barium Hexaferrite

$Co_2Z$-type barium ferrites ($Ba_3Co_2Fe_{24}O_{41}$) were synthesized using variation method. First, M-type, $Co_2Y$-type and $Co_2Z$-type synthesized by hydrothermal method. Second, M- and Y-type precursors for synthesis of $Co_2Z$ hexaferrite by hydrothermal and ball milling method. the morphology, structure and magnetic properties of the barium ferrite particles were characterized using XRD, FESEM, VSM, impedance. As a result, Single phase of M-type and $Co_2Y$-type were obtained. Manufactured powders of M+Y ball milling, M+Y hydrothermal were similar to single phase of $Co_2Z$-type hexaferrite, all powders were obtained theoretical magnetization (50 emu/g). The largest initial permeability were obtained $Co_2Z$ hexaferrite synthesized by reagent precusor, With increasing calcination temperature was lowered the initial permeability. In another synthesis didn't almost that little change could be found.

Co2Z-type Barium Hexaferrite의 합성방법에 따른 결정구조 및 자기적 특성

$Co_2Z$-type hexaferrite 시편을 다양한 합성법을 이용하여 제조하였다. 수열합성법을 이용하여 M-type, $Co_2Y$-type, $Co_2Z$-type을 제조하였으며, 제조된 M-type과 $Co_2Y$-type을 출발물질로 하여 고상반응법(ball milling)과 수열합성법(hydrothermal)으로 $Co_2Z$-type을 제조하였다. 제조된 시편의 결정구조와 미세구조 자기적 성질은 XRD, FESEM, VSM, impedance analyzer를 이용하여 조사하였다. M-type과 $Co_2Y$-type은 단일상의 결정구조를 얻을 수 있었다. 여러 합성법 중에 M+Y ball milling, M+Y hydrothermal에서 제조한 시편이 $Co_2Z$-type hexaferrite의 단일상과 대체로 일치하는 것을 알 수 있었으며, $Co_2Z$-type의 모든 시편들은 이론적인 포화 자화값(50 emu/g)과 비슷한 값을 나타내었다. 소결한 시편들의 투자율은 시약을 precusor로 하여 제조한 $Co_2Z$-type의 투자율이 가장 높았으며, 열처리 온도가 증가함에 따라 투자율은 낮아졌다. 다른 합성법에서는 열처리 온도에 따른 변화가 거의 나타나지 않는 것을 확인할 수 있었다.