Preparation and Electromagnetic Properties of Ni-Zn Ferrite by Wet Method

Ni-Zn ferrite powder was synthesized from metal nitrates, Fe(N $O_3$)$_3$$.$9 $H_2$O, Ni(N $O_3$)$_2$$.$6 $H_2$O, Zn(N $O_3$)$_2$$.$6 $H_2$O by wet direct process to make high permeability material. The composition of the ferrite powder is (N $i_{0.284}$F $e_{0.053}$Z $n_{0.663}$)F $e_2$ $O_4$. Ni-Zn ferrite powder is compounded by precipitating metal nitrates with NaOH in vessel at 90$^{\circ}C$ synthetic temperature for 8 hours. Calcination temperature and sintering temperature were 700$^{\circ}C$ and 1150$^{\circ}C$-1250$^{\circ}C$ respectively for 2 hours. The same compound powder was extracted from metal oxide by wet ballmilling. We compared the properties of powder and the electromagnetic characteristics of the sintered cores obtained from the two different processes. Wet direct process produces smaller particle size with narrower distribution and higher purified ferrite which cores has high permeability and high magnetization.

습식합성법을 이용한 Ni-Zn Ferrite의 제조 및 전자기적 특성연구

Fe(N $O_3$)$_3$$.$9$H_2O$, Ni(N $O_3$)$_2$.6$H_2O$, Zn(N $O_3$)$_2$$.$6$H_2O$와 같은 질산금속염들을 습식법의 일종인 습식 직접 합성법을 이용하여 Ni-Zn ferrite 분말로 합성하였다. 분말의 화학조성은(N $i_{0.284}$F $e_{0.053}$Z $n_{0.663}$)F $e_2$ $O_4$로 하였으며, 고투자율 재료의 영역에 목표를 두었다. 습식 직접 합성법으로 시편을 제조하기 위하여 측량된 질산금속염들을 반응 용기 내에서 NaOH로 침전시키면서 9$0^{\circ}C$의 합성온도로 8시간 동안 교반.합성하였다. 가소 온도는 $700^{\circ}C$로 하여 2시간 유지시켰고, 소결온도는 11$50^{\circ}C$-12$50^{\circ}C$의 범위에서 각각 2시간 유지시켰다. 또 금속산화물을 출발물질로 하여 동일한 조성을 가지는 분말을 습식볼밀링하여 제조하였으며, 두 가지의 공정으로 합성된 분말의 특성과 소결체의 전자기적 특성을 비교.연구하였다. 동일 조건일 경우, 습식 직접 합성법으로 제조하면 입도분포가 좁고, 고순도이며, 미분말인 페라이트 분말을 얻을 수 있었으며 소결체의 특성 또한 비교적 높은 투자율과 자화 값을 나타내었다.