Characteristics of Red mud Ceramics according to Sintering Temperature and Contents of Red Mud from Industrial Byproducts

This paper aims to recycle red mud from a byproduct in the alumina industry as an alternative raw material for depleted natural resources. In order to apply red mud as a ceramic material, red mud ceramics were prepared according to mixing and temperature in a laboratory environment. Compared with KS L 4201 in terms of compression ratios and absorptions, it is found that two kinds of conditions for one type and three conditions for two types meet the standard. When red mud is used as a clay brick raw material, the substitution ratio of red mud is 10% or less, and the firing temperature is considered to be appropriate at $1200^{\circ}C$. In order to apply red mud to clay brick raw material in actual field, various samples and firing temperature should be considered in the future.

산업부산물 레드머드 첨가량에 따른 소성온도별 레드머드 세라믹의 특성

본 논문은 고갈되고 있는 천연자원의 대체 원료로서 알루미나 산업에서 부산물로 발생되는 레드머드를 재활용하고자 하였으며, 레드머드를 소성하여 세라믹 소재로 적용하기 위하여 실험실 환경에서 레드머드를 배합 및 온도에 따라 레드머드 세라믹을 제조하여 점토벽돌 제조용 원료로서 기초 특성을 검토하고자 한다. 본 논문의 범위에서는 레드머드 배합조건별 KS L 4201와 압축강도 및 흡수율을 비교하였을 때 1종의 경우 2개의 조건, 2종의 경우가 3개의 조건에서 규격을 만족하는 것으로 나타났으며, 레드머드를 점토벽돌 원료로 활용할 경우 레드머드 첨가량은 10%이하 소성온도는 $1200^{\circ}C$가 적절할 것으로 판단된다. 향후 레드머드를 점토벽돌 원료로서 실제 현장에 적용하기 위해서는 다양한 시료와 소성온도가 검토되어야 할 것으로 판단된다.