Strength and Durability of Polymer Modified Mortar according to Monomer Ratio of Methyl Methacrylate and Butyl Acrylate

The purpose of this study is to clarify the effect of the monomer ratio on properties of the polymer-modified mortars using methyl methacrylate-butyl acrylate (MMA/BA) latexes, and to obtain basic data necessary to develop appropriate latexes for cement modifiers. From the test results, the total pore volume of polymer-modified mortars using MMA/BA latexes is linearly reduced with an increase in the bound MMA content and increased in the polymer-cement ratio. In general, the superior flexural and compressive strength of polymer-modified mortars using MMA/BA latexes is obtained at a bound MMA content of 70 or 80 percent and a polymer-cement ratio of 15%. And, the water absorption and chloride ion penetration depth are greatly affected by the polymer-cement ratio rather than the bound MMA content.

MMA/BA의 단량체 비에 따른 폴리머 시멘트 모르타르의 강도 및 내구성

본 연구에서는 MMA(methyl methacrylate)와 BA(buthyl acrylate)를 단량체로 이용한 폴리머 시멘트 모르타르의 단량체 비에 따른 성질을 파악하고 시멘트 혼화용 폴리머로 활용하기 위한 기초적 자료를 얻고자 하였다. 본 연구결과 MMA/BA를 이용한 폴리머 시멘트 모르타르의 전 세공용적은 MMA/BA의 단량체 비가 증가할수록 감소하는 것으로 나타났다. 강도특성에서는 전체적으로 MMA/BA의 단량체 비가 70 : 30, 그리고 80 : 20일 때, 폴리머 시멘트 비가 15%일 때 가장 우수한 증진효과를 나타냈다. 폴리머 시멘트 모르타르의 내구성을 측정하는 흡수율, 염화물 이온 침투 저항성, 중성화 저항성에서는 단량체 비에 따른 개선보다는 폴리머 시멘트 비에 따른 개선효과가 더 큰 것으로 나타났다.