Physical Properties and Flame-Retardant Effects of Polyurethane Coatings Containing Pyrophosphoric Lactone Modified Polyesters

Pyrophosphoric lactone modified polyester (PATT) containing two phosphorous functional groups in one unit structure was synthesized to prepare a non-toxic reactive flame-retardant coatings. Then the PATT was cured at room temperature with isocyanate, toluene diisocyanate-isocyanurate , to get a two-component polyurethane flame-retardant coatings (PIPUC). Comparing physical properties of the films of PIPUC with those of film of non-flame-retardant coatings, there was no deterioration observed in physical properties by the introduction of a flame-retarding component into the resin. We found that the char lengths measured by 45$^{\circ}$ Meckel burner method were 3.1∼4.4 cm and LOI values recorded 27∼30%. These results indicate that the coating prepared in this study is a good flame-retardant. The surface structure of coatings investigated with SEM does not show any defects and phase separation.

파이로포스포릭 락톤 변성 폴리에스터를 함유한 폴리우레탄 도료의 물성 및 난연 효과

무독성의 반응형 난연 도료를 제조할 목적으로 모체수지 1개의 구조단위 속에 2개의 인산기를 보유한 파이로포스포릭 락톤 변성 폴리에스터 (PATT)를 합성하고, PATT에 이소시아네이트인 toluene diisocyanate-isocyanurate를 상온경화시켜 2성분계 폴리우레탄 난연 도료(PIPUC)를 제조하였다. PIPUC로서 도막제작 후 비난연 도료와의 도막물성을 비교한 결과 난연 성분 도입에 따른 난연 도료의 물성이 저하되지 않음을 알았다. 난연성 시험 중 45$^{\circ}$ Meckel burner 법에서는 탄화길이가 3.1~4.4 cm를, LOI법에서는 LOI 27~30%를 각각 나타냄으로써 양호한 난연 효과를 보여주었고, SEM에 의한 표면 도막을 관찰한 결과 도막의 결함이나 상분리 현상이 생기지 않음을 관찰하였다.