Property Studies of PAN/PVdF Composite Nanofiber Manufactured from Electrospinning

In this paper, manufactured composite nanofiber by electrospinning that make spinning solvent according to weight of PAN/PVdF. PVdF content of composite nanofiber decreases, diameter of fiber decreased. Result that measure contact angle to confirm hydrophile property of PAN/PVdF composite nanofiber, PVdF content increases, could confirm that contact angle with water increases. After leave filter measurement sample for 25 hours in temperature of $40^{\circ}C$, humidity of 85%, result PAN/PVdF composite nanofiber that estimate efficiency could confirm that display performance of HEPA more than 99.95% and ULPA more than 99.999%. And fiber diameter is small, could confirm that filter performance increases. Tensile strength of bulk of PAN/PVdF composite nanofiber was 5-8MPa, expansion 100-300%. And strength and expansion could know that increase according as PVdF's content increases. Tensile strength was 3-8MPa degree after annealing PAN/PVdF composite nanofiber during 2 hours in 120t. Tensile strength was no change almost by annealing, and expansion could know that decrease.

전기방사법으로 제조된 PAN/PVdF 복합나노섬유의 특성연구

본 논문에서는 PAN/PVdF의 중량비에 따라 방사용액을 제조한 후 고전압으로 전기방사법에 의해 복합나노섬유를 제조하였다. 제조된 복합나노섬유는 PVdF의 함량이 감소할수록 섬유경이 감소하는 경향을 나타냈다. PAN/PVdF 복합나노섬유의 친수성 정도를 확인하기 위하여 접촉각을 측정한 결과 친유성인 PVdF의 함량이 증가할수록 물과의 접촉각이 증가하는 것을 확인할 수 있었다. 필터측정용 샘플을 $40^{\circ}C$의 온도, 85%의 습도에서 25시간 동안 방치한 후 성능을 평가한 결과 PAN/PVdF 복합나노섬유의 경우 99.95% 이상의 혜파(HEPA)급 및 99.999% 이상의 울파(ULPA)급 성능을 나타냄을 확인할 수 있었으며, 섬유경이 작을수록 필터 성능이 증가하는 것을 확인할 수 있었다. PAN/PVdF 복합나노섬유의 벌크 인장강도는 5-8MPa, 신도는 10-300% 범위였으며, PVdF의 함량이 증가할수록 강도와 신도가 동시에 증가하는 것을 알 수 있었다. PAN/PVdF 복합나노섬유를 $120^{\circ}C$에서 2시간 열처리한 시료의 인장강도는 3-8MPa정도였다. 인장강도의 경우는 열처리에 의해 거의 변화가 없었으며, 신도는 감소함을 알 수 있었다.