The Aging Effect of K3B/1M7 Laminates in Water

The Hygrothermal aging of the laminates of $Avimid^(R)$ K3B/IM7 in $80^{\circ}C$ water was studied as a function of immersion time prior to forming microcracks. The factors causing the $80^{\circ}C$ water to degradation of the laminates could be the degradation of the matrix toughness, the change in residual stresses or the interfacial damage between the fiber and the matrix. The times to saturation in $80^{\circ}C$ water for the laminates and for the neat resin were 100 hours and 500 hours. After 500 hours aging of the neat resin, the glass transition temperature was changed less than 1% by DSC test, and the weight gain was 1.55% increase with the diffusion coefficient $7\times10^{-6}m/s^2$ and the fracture toughness was decreased about 41%. After 100 hours fully saturated aging of the ${[+45/0/-45/90]}_s$ K3B/IM7 laminates in $80^{\circ}C$ water, the weight gain was 0.41% increase with the diffusion coefficient $1\times10^{-6}m/s^2$. In 100 hours, the loss of the fracture toughness of the laminates was 43.8% of the original toughness by the microcracking fracture toughness criterion. Therefore, the main factor to degrade the microcracking toughness of the laminates could be the degradation of the matrix fracture toughness.

K3B/IM7 복합재료의 물에서의 노화현상

미세균열이 생기기 전 $80^{\circ}C$ 물속에서 침수시간에 따른 $Avimid^(R)$ K3B/IM7 복합재의 습기노화 현상에 관하여 연구하였다. $80^{\circ}C$ 물속에서 복합재의 파괴인성을 저하시키는 요인으로는 수지 파괴인성의 저하나 잔류응력의 변화 그리고 섬유와 수지 사이의 계면 손상이다. $80^{\circ}C$ 물속에서 수지에 습기가 포화되는 시간은 500 시간이며 K3B/IM7복합재에 습기가 포화되는 시간은 100 시간이다. 수지가 500 시간 가속노화한 후 DSC 시험을 한 결과 $T_g$는 1% 이내 증가하였으며, 무게는 $7\times10^{-6}m/s^2$ 확산속도로 1.55% 증가하였다. K3B/IM7복합재에 관하여 물속에서 100시간 지난 후 무게는 $1\times10^{-6}m/s^2$ 확산속도로 0.41% 증가했다. 500 시간 노화한 후 수지의 파괴인성은 41% 저하하였으며 100 시간 노화한 후 ${[+45/0/-45/90]}_s$ K3B/IM7 복합재의 미세균열 파괴인성은 43.8% 감소하였다. 그러므로 $80^{\circ}C$ 수분노화 시험에서 복합재 적층의 파괴인성을 감소시키는 주요 원인은 수지 파괴인성의 저하라고 할 수 있다.