Influence of mechanical properties with gingival shade composites resin according to the thermocycling treatment  

Im, Yong-Woon (Department of Biomaterials Science, College of Dentistry, Dankook University)
Hwang, Seong-Sig (Department of Dental technology, Kyung-Dong University)
Publication Information
Journal of Technologic Dentistry / v.39, no.2, 2017 , pp. 83-91 More about this Journal
Abstract
Purpose: The objective of this study was to evaluate influence of mechanical properties of gingival shade composite resins(GSCRs) according to thermocycling treatment. Methods: The material utilized in this study was Crea.lign(CGR), Twiny flow(TGF) and Twiny(TGP). Total sixty specimens were fabricated with a dimension of $25{\times}2{\times}2mm$ according to the ISO 4049. After fabrications, specimens of before and after thermocycling(to $55^{\circ}C$ from $5^{\circ}C$) were stored in the distilled water for 24 hours at the $37^{\circ}C$. Three-point flexural test was performed in universal testing machine(Instron 5966, USA) at a crosshead speed of 1 mm/min. Flexural strength, flexural modulus and work of fracture according to the thermocycling were analyzed using a one-way ANOVA analysis. Surface analysis of GSCRs after thermocycling evaluated using the scanning electron microscope. Results: : The highest FS was measured in TGP group of NTC group and lowest in CGR group after TC. After TC, FS and FM decreased in CGR and TGP groups, but TGF increased. There was a statistically significant difference between FS and WOF in GSCRs(p<0.05). But FM did not show any significant difference after TC (p>0.05). The strength of the characteristic exceeded the flexural strength required by ISO 4049(> 80 MPa). Weibull modulus(m) showed the highest reliability in the TGP group (m = 14.22), and the reliability of the TGF and TGP groups after TC decreased. Conclusion: Thermocycling treatment is important factor influence of mechanical properties with gingival shade composite resins. Therefore, we recommended that mechanical properties need to get useful information and accuracy for life-span expectancy according to the thermocycling treatment.
Keywords
Flexural strength; Gingival shade composite resin; Mechanical properties; Thermocycling; Weibull analysis;
Citations & Related Records
Times Cited By KSCI : 3  (Citation Analysis)
연도 인용수 순위
1 Ichiwata T, Ueda K, Takeda T, et al., Research into the colors of denture base resininfluence of differences in shade and thickness. J Nihon Univ Sch Dent, 26, 30-38, 1984.   DOI
2 ISO 4049: Dentistry-polymer-based filling, restorative and luting materials. International organization for standardization, Geneva, Switzerland, 15-17, 2000.
3 Im YW, Hwang SS. Evaluation of flexural Properties of indirect gum-shade composite resin for esthetic improvement. J Dent Hyg Sci, 15(4), 407-412, 2015.   DOI
4 Im YW, Jun SK, Kim SC, Kim DA, Kim GR, Kim NS, Lee HH. Standardized test methods for mechanical properties of dental prosthetic/restorative materials and their applications. Kor J Dent Mater, 42(3), 259-270, 2015.   DOI
5 Janda R, Roulet JF, Latta M. The effects of thermocycling on the flexural strength and flexural modulus of modern resinbased filling materials. Dent Mater, 22(12), 1103-1108, 2006.   DOI
6 Jin SE, Cho IH. The effect of glass fiber reinforcing materials and thermocycling on the transverse strength of denture base resin. J Dent Rehabil Appl Sci, 29(4), 327-336, 2013.   DOI
7 Jun SK, Kim DA, Goo HJ, Lee HH. Investigation of the correlation between the different mechanical properties of resin composites. Dent Mater J, 32, 48-57, 2013.   DOI
8 Lee DS, Lim HS, Lim JH, Cho IH. A study on the effect of thermocycling to the physical properties of denture liners. J Kor Acad Prosthdont, 39, 556-575, 2001
9 Ilie N, Hickel R. Investigations on mechanical behaviour of dental composites. Clin Oral Investig, 13, 427-438, 2009.   DOI
10 Lee DU, Song DB. All of aesthetics denture. Well, 256-262, 2014.
11 Lee HH, Lee CJ, Aaoka K. Correlation in the mechanical properties of acrylic denture base resins. Dent Mat J, 31(1), 157-164, 2012.   DOI
12 Lee JH, Kim S, Jeong TS, Kwon YH. Effect of filler type on microhardness and flexural properties of flowable resins. Kor J Dent Mater, 40(4), 316-320, 2013.
13 Park BW, Kim NJ, Lee JH, Lee HH. Technique for fabricating individualized dentures with a gingiva-shade composite resin. J Prosthet Dent. 115(5), 547-550, 2016.   DOI
14 Park SH, Lim HS, Cho IH. On the fracture strength of the repaired resin according to the type of denture base resin, the type of reinforcing material and thermocycling. J Den Rehabi Appl Sci. 15, 27-37, 1999.
15 Rodrigues SA Jr, Ferracane JL, Della Bona A. Flexural strength and Weibull analysis of a microhybrid and a nanofill composite evaluated by 3- and 4-point bending tests. Dent Mater, 24, 426-431, 2008.   DOI
16 Shimizu H, Kawaguchi T, Mutobe H, Kiyokuni Y, Takahashi K, and Takahashi Y. Bonding of a gingival shade composite to a denture base resin using a chemically activated 4-meta resin. Eur J Prosthodont Restor Dent, 19(1), 7-10, 2011.
17 Yap AUJ, Wang X, Wu X, Chung SM. Comparative hardness and modulus of toothcolored restoratives: a depth-sensing microindentation study. Biomaterials, 25(11), 2179-2185, 2004.   DOI
18 Yim SH, Kim JH. Esthetically improved complete denture by gingival shade alteration: a case report. J Kor Acad Prosthodont. 52, 239-245, 2014.   DOI
19 Zeng K, Oden A, Rowcliffe D. Flexure tests on dental ceramics. Int J Prosthodont 9, 434-439, 1996.
20 Barclay CW, Spence D, Laird WRE. Intra-oral temperatures during function. J Oral Rehabil, 32, 886-94, 2005.   DOI
21 Della Bona A, Anusavice KJ, DeHoff PH. Weibull analysis and flexural strength of hotpressed core and veneered ceramic structure. Dent Mater, 19, 662-669, 2003.   DOI
22 Gale MS, Darvell BW. Thermal cycling procedures for laboratory testing of dental restorations. J Dent, 27(2), 88-99, 1999.
23 Gu HJ, Jun SK, Kim DA, Kim HW, Lee HH. Effect of thermocycling on the mechanical properties of resin composites. J korea research Dent Mater, 35(2), 155-164, 2008.
24 Gohring TN, Gallo L, Luthy H. Effect of water storage, thermocycling, the incorporation and site of placement of glass-fibers on the flexural strength of veneering composite. Dent Mater, 21, 761-772. 2005.   DOI
25 Hadis M, Leprince JG, Shortall AC, Devaux J, Leloup G, Palin WM. High irradiance curing and anomalies of exposure reciprocity law in resin based materials. J Dent, 39, 549-557, 2011.   DOI
26 Haeberle CB, Khan Z. Construction of a custom-shade interim denture using visible-light-cured resin. J Kor Adv Prosthodont, 6, 153-156, 1997.   DOI