A COMPARATIVE STUDY ON THE PROPERTIES OF FILLER-ADDED METHACRYLATE POLYMERS  

Park Dong-Won (Department of Prosthodontics, Division of Dentistry, Graduate School, Kyung-Hee University)
Choi Boo-Byong (Department of Prosthodontics, Division of Dentistry, Graduate School, Kyung-Hee University)
Kwon Kung-Rock (Department of Prosthodontics, Division of Dentistry, Graduate School, Kyung-Hee University)
Publication Information
The Journal of Korean Academy of Prosthodontics / v.41, no.5, 2003 , pp. 606-616 More about this Journal
Abstract
Purpose : The purpose of this study was to research the properties of some chemically cured methacrylate polymers such as MMA, HEMA, TEG-DMA, bis-GMA, GMA. Material and Method : 5 kinds of methacrylates were selected and added 2% tertiary amine and benzoyl peroxide to make a chemically curable polymer 25 micron crushed silicas which are treated with silane were selected as filler, they were added into methacrylate monomer until the consistency did not changed by the load of 500gram. All of the experimental resins were 5 kinds, and a serial test was done with 3 kinds of items including the filler contents, the tensile strength, and the bond strength. The number of specimen were 10 for each group. Filler contents were obtained by reducing the specimens to ashes at $600^{\circ}C$ for 1 hour. The specimens with the dimension of 6mm in diameter and 3mm thick were immersed in $37{\pm}1^{\circ}C$ distilled water for 24 hours before test, and tensile strength were measured with cross-head speed 1mm/min. Shear bond strength were mea sured on the specimens attached to bovine enamel etched with 37% phosphoric acid for 1 minute. Results : 1. Maximum filler incorporation was the highest as 75.5% on MMA, and the least as 53.4% on bis- GMA(p<0.0001). 2. The tensile stregth were MMA 141.3, GMA 154.3, TEG-DMA 157.4, bis-GMA 161.4 MPa, and HEMA showed the highest value, 226.9MPa(p = 0.0004). 3. The bond strength were GMA 10.1, TEG-DMA 11.7, HEMA 12.2, bis-GMA 13.3 MPa, and MMA showed the highest value, 15.3MPa, however statistical significances were not (p =0.3838), 4. TEG-DMA and HEMA were not different on the aspect of maximum filler contents and shear bond strength(p>0.05). Conclusion : HEMA can be used as an another diluent substituting TEG-DMA with the increased strength and with the constant bond strength and the constant filler contents.
Keywords
Metacrylate polymer; Tensile strength; Bond strength; Filler contents;
Citations & Related Records
연도 인용수 순위
  • Reference
1 Paffenbarger. G. C., Nelsen. R. J ., and Sweeney. W. T. : Direct and indirect fill ing resins a review of some physical and chemical properties. J. Am. Dent. Assoc., 47 : 516-520. 1953
2 Brauer. G.M. Properties of sealants containing Bis-GMA and various diluents. J. Dent.Res., 57:597-601. 1978
3 Gross. M., Douglas. W. H., and Fields, R.P. : The relationship between filler loading and particle size distribution in composite resin technology. J. Dent. Res., 62:850-852. 1983
4 Tani, Y. : Posterior restorative composites-characteristics and clinical considerations. Dent. Outlook. 59: 1319-1328.1982
5 Nakabayashi. N., Watatabe. A., : Dentin adhesion of modified 4-META / MMA-TEB resin : funtion of HEMA. Dent. Master., 8:259-264. 1992
6 Soo-Cheol Kim, Ki-Soo Lee : Effects of phosphoric acid concentration on depth of etoh and shear bond strength of Orthodontic brakets to Bovine enamel. Kyunghee Dental journal. 16:7-22. 1994
7 Kalachadra. S., Pandian. M.S ., Shobha. H. K. . Taylor. D.F. and Mcgrath, J.E. Influence of H-bonding on properties of BISGMA analogs , J.Dent.Res., 75:235-235, 1996. #1741
8 Urabe , H., Wakasa, K., and Yamaki, M. : Optical and thermal properties in exper imental Bis-GMA-based resins influenced by filler characteristics. J Mater. Scien Mater. Medic., 1:55-59, 1990
9 Bowen, R. L. : Properties of a silica reinforced polymer for dental restorations. J. Am. Dent. Assoc., 66 : 57-64, 1963
10 Vanherle. G. Posterior composite resin dental restorative materials. Theory of poly-mer composite , Peter Szulc Publishing Co., pp 95-105. 1985
11 Asmussen. E. : Quantitative analysis of peroxides in restorative resin. Acta Odont. Scand., 38 : 269-272. 1980
12 Bowen. R. L., and Washing. D. C : Dental filling material comprising vinyl silane treated fused silica and a binder consisting of the reaction product of bisphenol and glycidyl acrylate. US-Patent. 3 : 66-112. 1962
13 Asmussen. E. : A qualitative and quantitative analysis of tertiary amines in restorative resins. Acta Odont. Scand., 38 : 95-99. 1980   DOI   PUBMED   ScienceOn
14 Erik. A. Setting time of composite restorative resins vs. content of amine. peroxide. and inhibitor. Act Odontol. Scand., 39:291-294. 1981
15 Attal. J-P., Asmussen. E., and Degrange. M. : Efect of surface treatment on the free surface energy of dentin. Dent. Mater., 10:259- 264 .1994
16 Cobb. D.S ., Reinhardt. J.W., and Vargas. M. A., Effect of HEMA-conataining dentin desesitizers on shear bond strength of a resin cement. Am. J. Dent., 10:62-65,1997
17 Bowen. R. L. Method of preparing a monomer having phenoxy and methacrylate groups linked by hydroxy glycerol groups. US Patent. 3 : 179-623. 1965
18 Bowen. R. L., and Reed. L. E. : Semiporous reinforcing fillers for composite resins II. Heat treatments and etching characteristics. J. Dent. Res ., 55 : 748-750. 1976
19 Bowen. R.L. Use of epoxy resins in restorative materials. J. Dent. Res. 35:360-369, 1956   DOI   PUBMED   ScienceOn
20 Bowen. R. L. : Effect of particle shape and size distribution in a reinforced polymer. J. Am. Dent. Assoc., 69: 481-485.1964
21 Dulik. D., Bernier. R., and Brauer. G.M. : Effect of diluent monomer on the physical properties of BIS-GMA based composites. J. Dent.Res ., 60:983-989. 1981
22 Nakabayashi. N., Takarada. K : Effect of HEMA on bonding to dentin. Dent. Master., 8:125-130.1992
23 Bowen. R. L., and Rodriguez. M. S. Tensile strength and modulus of elasticity of tooth structure and several restorative materials. J. Am. Dent. Assoc., 64 : 378-384. 1962
24 Munksgaard. E. C., Asmussen. E. : Adhesion of restorative resins to dentinal tissues. Netherlands. Peter Szulc Publishing Co., 1985
25 Bowen. R. L. Dental filling material comprising vinyl silane treated fused silica and a bonder consisting of the reaction product of bis phenol and glycidyl acrylate. US Patent. 3 : 066-112. 1962
26 Tani. Y. : A new composite resin Palfique-Characteristics and clinical use. Dental Outlook.62:887-896.1983
27 Asmussen. E. : Restorative resin hardeness and strength vs quantity of remaining double bonds. Scand. J. Dent. Res., 90 : 484-489. 1982
28 Krause, W.R., Park. S.H. . and Straup , R.A. : : Mechanical properties of BIS-GMA resin short glass fiber composites, J. Biomed. Mater. Res., 23: 1195-1211. 1989
29 Nakabayashi. N., Watanabe : Effect of HEMA on bonding to dentin. Dent. Master., 8: 125-130.1992
30 Sumiya Hobo. Young-Hwan Cho : Esthetic Adhesive Dentistry. Koonja publishing. 3-4. 1993
31 Terashita. M., Keida, Y., Ooki. T., Okamoto, S., Nomiyama, S., and Nagano. M. : A study on water-settable polycarboxylate cement; Part 3 Ability to isolate Bis-GMA and some physical properties. Japan. J.Conserv.Dent. , 23: 131-137, 1980
32 Scumacher. G.E. , Eichmiller. F. C., and Antonicci. J.M. : Effects of surface active resins on dentin / composite bonds. Dent. Mater., 8:278-282,1992
33 Paffenbarger, G. C., Nelsen. R. J ., and Sweeney. W. T. : Direct and indirect filling resins a review of some physical and chemical properties. J. Am. Dent. Assoc., 47: 516-520. 1953
34 Tani. Y. : Marginal fracture toughness of composite resins. Dent. Master. J., 1:22-32.1982
35 Malpuarti. G., Berruet. R. G., and bois. D : Prosthetic use of carbon fiberreinforced epoxy resin for esthetic crowns and fixed partial dentures. J. Prosthet. Dent ., 63: 251-257. 1990
36 Bowen. R. L. : Synthesis of a silica-resin direct filling materials. J. dent. Res. 37 : 90-91. 1957
37 Bowen, R. L., and Reed, L. E. : Semiporous reinforcing fillers for composite resins : I. preparation of provisional glass for mulation. J. Dent. Res., 55 738-747. 1976   DOI   ScienceOn
38 Bowen. R. 1. Silica-resin direct filling mate- rial and method of preparation. US Patent. 3-194-784. 1965
39 Wu, W., and Mckinney. J. E. : Influence of chemicals on wear of dental composites. J. Dent. Res ., 61 : 1180-1183. 1982
40 Newman , B.V. : Epoxy adhesives for orthodontic attachments an progress report. Am. J. Orthod., 57:901-912. 1965
41 Ho-Nam Lim. Young-Guk Park. Ki-Soo Lee : : Efficancy of Pyruvic acid as dental etchant. The journal of Korea Research Society of Dental Material. 29(1). 47-55. 196
42 Bum-SoonLim, Cheal-We Kim : Effect of curing efficiency and aging on the physical properties of dental composite resin , The Journal of the Korea Research Society for Dental Materials. 24:227-245. 1997
43 Bowen. R. 1. Compatibility of various mate- rials with oral tissues I. The component in composite restorations. J. Dent. Res., 58 : 1493-1498. 1979
44 Finger. W.J., Fritz. U.B. : Resin bonding to enamel and dentin with one-component UDMA / HEMA adhesives. Eur. J. oral. Sci., 105:183-186.1997
45 Coy. H. D. : Direct filling resins. J. Am. Dent. Assoc., 47:532-537. 1953