Study on Fabrication and Photoluminescent Properties of Fine Phosphor Film for Application of Radiation Image Sensor

In this paper, the fabrication and feasibility study of clinical application with euripium doped gadollium oxide ($Gd_2O_3$:Eu) nano phosphor derived by low-temperature solution combustion method. From the fabricated phosphor, the photoluminescent characteristic and linearity as a function of phosphor film thickness were investigated to evaluate x-ray converstion properties. From the experimental results, the luminescent intensity was $2945pC/cm^2$-mR at $270{\mu}m$ $Gd_2O_3$:Eu film and this value is higher 1.2 time the conventional bulk phosphor, which is possible to imaging acquisition. And good linearity was shown at x-ray exposure range for clinical diagnostic application.

방사선 영상센서 적용을 위한 미세 발광체 필름 제조 및 광학적 특성에 관한 연구

본 연구에서는 고해상도 영상획득을 위해 저온액상법을 이용하여 Europium doped gadollium oxide($Gd_2O_3$:Eu) 미세 형광체를 제조하여 입자의 형상 및 구조를 분석하였으며, 발광체 필름에 대한 방사선에 대한 광학적 반응특성 실험을 통해 고해상도 영상검출기 적용 가능성을 확인하였다. 제조된 형광체 필름 두께에 따른 광량 및 선량에 따른 발광의 선형성을 조사하였다. 측정결과, $270{\mu}m$ 두께의 $Gd_2O_3$:Eu에서 $2945pC/cm^2/mR$의 발광 강도로 이 값은 벌크 형광체 필름의 발광 강도보다 약 1.2배 높은 영상 획득을 위한 충분한 신호임을 확인할 수 있었다. 또한, 임상 진단 영역의 X선 조사선량 범위에서 대체로 좋은 선형적 특성을 보였다.