The coating of vitamin C on the surface of polymethylmethacrylate microsphere

This paper was described that the preparation of polymetylmethacrylate (PMMA) microsphere and coating of vitamin C onto surface of the prepared PMMA microsphere for application of cosmetic materials. The PMMA microsphere with various sizes can be obtained by change of reaction condition such as reaction temperature and reaction time. The coating of vitamin C on the surface of PMMA microsphere by using cyclodextrin as binder can be achieved to 30 wt-% in water/ethanol mixture. The vitamin C coated with cyclodextrin was stabilized during 56 days at $40^{\circ}C$. The color of the coated Vitamin C was changed from white to dark yellow after 14 days at $40^{\circ}C$. The vitamin C coated with cyclodextrin on the surface of PMMA microsphere can be sufficiently used for cosmetic materials.

Polymethylmethacrylate 입자에 표면에 비타민 C의 코팅

기능성 화장품 원료로서 관심을 갖는 비타민 C(L-ascobic acid)는 피부에 대한 안전성, 항산화성으로 인해 노화방지 및 미백, 잔주름개선 등의 효능을 갖지만 화학적으로 쉽게 산화된다. 따라서 본 연구에서는 비타민 C의 안정성에 대한 단점을 보완하기 위하여, 에멀젼 중합법으로 다양한 마이크론 크기의 Polymethylmethacrylate(PMMA)입자를 제조하고, 제조된 PMMA의 입자 표면에 코팅용액(물과 에탄올 혼합용매에 cyclodextrin과 비타민 C를 녹인 용액)을 이용하여 비타민 C를 코팅처리 하였다. 코팅처리 후, 실온 및 $40^{\circ}C$에서 시간에 따른 비타민 C의 함량을 조사한 결과, 56일이 경과후에도 비타민 C가 86.4%가 잔존함을 확인 할 수 있었다.