An experimental investigation on the flexural fatigue behavior of a RC bridge slab retrofitted with Carbon Fiber Sheet (CFS) is presented. The test slab was almost identical to the slab of a highway viaduct in terms of the amount of reinforcement, quality of concrete and thickness of the slab, which was 18cm. Repeated load corresponding to 3.0, 4.5 or 6.0 times of the design load was applied to the test slab. Normal type and high-elastic modulus type of CFS were used for strengthening. The test slabs were loaded in dry or wet condition. Two different types of an-choring system were adapted. Some of the test slabs were damaged by the repeated load and retrofitted by CFS, then loaded again to see the improvement of the fatigue life. Infrared Thermography was also performed to investigate the debonding condition of CFS. From the test results, Carbon Fiber Sheet can be applied to the RC bridge slabs as a feasible retrofitting material.

This is the second of two part series on experimental studies of grout type transverse joints. In this paper, grout-type transverse joints between precast concrete slabs are tested to study the fatigue behavior. The tests are per-formed with loading equipment designed and constructed especially in the lab to introduce shear fatigue failures on the joints of the test specimens with repeated loads. Non-prestressed as well as prestressed specimens are selected based on static tests and these specimens are studied to identify the effect of prestress on the fatigue strength of the grout type joint. A comparison between prestressed and non-prestressed specimens indicates that longitudinal prestressing is an effective method to increase fatigue strength of the transverse joints. Based on the fatigue test, a rational estimation of the fatigue strength is proposed to aid design of the grout-type transverse joints.

The role of high volume Class F fly ash in reducing expansion due to Alkali-Silica Reaction (ASR) was investigated. A series of modified ASTM C 1260 tests were performed under three different levels of NaOH normality, extending the test period to 28 days, using high- or low alkali cement, and Class F fly ash up to 58 ％ by mass of cement. A reactive siliceous fine aggregate was used. The test results confirm that HVFA replacement in a cementitious system significantly helps in controlling expansion caused by ASR.

The strength development of concrete is influenced by temperature and cement type which greatly affect hydration degree of cement. There is not pertinent concrete strength management method in korea. There are several methods for estimating the in-place strength of concrete. One such method is the maturity concept. The maturity concept is based on the fact that concrete gains strength gradually as a result of chemical reactions between cement and water; and for a specific concrete mixture, strength at any age and at normal conditions is related to the degree of hydration. The rate of hydration and, therefore, strength development of a given concrete will be a function of its temperature. Thus, strength of concrete depends on its time-temperature history. The goals of the present study are to investigate a relationship between strength of high-strength concrete and maturity that is expressed as a function of an integral of the curing period and temperature and predict strength of concrete.

This paper presents an experimental study to investigate the behavior of mechanical anchorage of reinforcing bars in concrete members. Three kinds of mechanical anchorage which are a kind of headed reinforcements are considered in this study. Total seven specimens were prepared to consider the effects of anchoring methods (Type A, Type B and Type C) and anchorage lengths of the reinforcing bars (14 $d_{b}$, 12 $d_{b}$, 9 $d_{b}$). Pullout tests conforming to ASTM were carried out to assess the effects of several variables on anchoring strength of bars. Based on the test results, it was concluded that the behavior of the specimen anchored by the mechanical anchorage with the anchor-age length of 12 $d_{b}$, is as good as, or better than that of the specimen anchored by 90-degree standard hook.rd hook.