Power metallization degradation monitoring on power MOSFETs by means of concurrent degradation processes

  • Received : 2022.02.07
  • Accepted : 2022.05.09
  • Published : 2022.09.20
⟨ Previous Next ⟩

Abstract

An on-chip solution for health monitoring of semiconductor power switches subjected to thermo-mechanical metal fatigue degradation is proposed. The fatigue detection relies on the correlation between the progress of the main failure mechanism, which is critical to the functionality of the device, and a parallel degradation of a non-critical sensing structure using a different mechanism. Both mechanisms are driven by the same cyclic thermo-mechanical load. This study specifically develops a sensing structure for detecting power metallization aging through electrically detectable ratcheting behavior in the routing metal layer underneath. Experiments have been carried out on a dedicated test structure with electrical sensing of the health monitoring structure. Meanwhile, the main degradation progress was observed via scanning electron microscopy in regular intervals. Results show that the proposed approach will reliably work only for detecting degradation driven by repeated high overload events.

Keywords

Acknowledgement

This work was funded by the Austrian Research Promotion Agency (FFG, Project Nos. 863947, 874907, and 881110).

References

  1. Springer, M.: Modeling and simulation of fatigue damage in power semiconductors, PhD thesis, T.U. Wien (2017)
  2. Glavanovics, M., Kreuter, H.-P., Sleik, R., Schreiber, C.: Cycle stress test equipment for automated short circuit testing of smart power switches according to the aec q100- 012 standard. In: 2009 13th European Conference on Power Electronics and Applications, pp. 1-7 (2009)
  3. Zhao, S., Chen, S., Yang, F., Ugur, E., Akin, B., Wang, H.: A composite failure precursor for condition monitoring and remaining useful life prediction of discrete power devices. IEEE Trans. Ind. Inf. 17(1), 688-698 (2021) https://doi.org/10.1109/TII.2020.2991454
  4. Patil, N., Das, D., Goebel, K., Pecht, M.: Identification of failure precursor parameters for insulated gate bipolar transistors (IGBTs). In: 2008 International Conference on Prognostics and Health Management, pp. 1-5 (2008)
  5. Dusmez, S., Bhardwaj, M., Sun, L., Akin, B.: In situ condition monitoring of high-voltage discrete power mosfet in boost converter through software frequency response analysis. IEEE Trans. Ind. Electron. 63(12), 7693-7702 (2016) https://doi.org/10.1109/TIE.2016.2595482
  6. Anderson, J.M., Cox, R.W.: On-line condition monitoring for mosfet and IGBT switches in digitally controlled drives. In: IEEE Energy Conversion Congress and Exposition, pp. 3920-3927 (2011)
  7. Chen, Y., Meng F., Zhu, A., Li. W., and He, X.: Chip metallization aging monitoring with induced voltage vee between kelvin and power emitter for high power IGBT modules. In: 2020 IEEE Energy Conversion Congress and Exposition (ECCE), pp. 4012-4016 (2020)
  8. Panchal, P., von Essen, T., Ras, M.A., Grosse, C., May, D., Wunderle, B.: Accurate, versatile and compact transient measurement system for fast thermal package characterization and health monitoring. In: 2018 7th Electronic System-Integration Technology Conference (ESTC), pp. 1-7 (2018)
  9. Pu, S., Ugur, E., Yang, F., Akin, B.: In situ degradation monitoring of SiC MOSFET based on switching transient measurement. IEEE Trans. Ind. Electron. 67(6), 5092-5100 (2020) https://doi.org/10.1109/TIE.2019.2924600
  10. Ritter, M., Pfost, M.: A proposal for early warning indicators to detect impending metallization failure of dmos transistors in cyclic operation. In: Proceedings of the 2015 International Conference on Microelectronic Test Structures, pp. 18-22 (2015)
  11. Ritter, M., Pham, G., Pfost, M.: On-chip sensors to detect impending metallization failure of ldmos transistors under repetitive thermo-mechanical stress. IEEE Trans. Semicond. Manuf. 29(3), 193-200 (2016) https://doi.org/10.1109/TSM.2016.2571842
  12. Ritter, M., Pfost, M.: Resistance change in on-chip aluminum interconnects under cyclic thermo-mechanical stress. Microelectron Reliab 100-101, 113321 (2019) https://doi.org/10.1016/j.microrel.2019.06.013
  13. Durand, C., Klingler, M., Coutellier, D., Naceur, H.: Failure mechanisms in chip-metallization in power applications. In: 15th International Conference on Thermal, Mechanical and Mulit-Physics Simulation and Experiments in Microelectronics and Microsystems (EuroSimE), pp. 1-5 (2014)
  14. Nelhiebel, M., Illing, R., Detzel, T., Wohlert, S., Auer, B., Lanzerstorfer, S., Rogalli, M., Robl, W., Decker, S., Fugger, J., Ladurner, M.: Effective and reliable heat management for power devices exposed to cyclic short overload pulses. Microelectron. Reliab. 53, 1745-1749 (2013) https://doi.org/10.1016/j.microrel.2013.07.123
  15. Zhang, Z., Suo, Z., Liu, Y., Irving, S., Luk, T., Desbiens, D.: Methodology for avoidance of ratcheting-induced stable cracking (RISC) in microelectronic devices. In: 56th Electronic Components and Technology Conference 2006, p. 7 (2006)
  16. Smorodin, T., Wilde, J., Alpern, P., Stecher, M.: A temperaturegradient- induced failure mechanism in metallization under fast thermal cycling. IEEE Trans. Device Mater. Reliab. 8(3), 590-599 (2008) https://doi.org/10.1109/TDMR.2008.2002359
  17. Jacob, P., Nicoletti, G.: Failure causes generating aluminum protrusion/ extrusion. Microelectron. Reliab. 53, 1553-1557 (2013) https://doi.org/10.1016/j.microrel.2013.07.015
  18. Aichinger, T., Nelhiebel, M., Einspieler, S., Grasser, T.: In situ poly heater - a reliable tool for performing fast and defined temperature switches on chip. IEEE Trans. Device Mater. Reliab. 10(1), 3-8 (2010) https://doi.org/10.1109/TDMR.2009.2033467
  19. Suresh, S.: Fatigue of materials, 2nd edn. Cambridge University Press, Cambridge (1998)
  20. https://www.lua.org. Accessed Jan 2022
  21. Schneider, C.A., Rasband, W.S., Eliceiri, K.W.: NIH Image to ImageJ: 25 years of image analysis. Nat. Methods 9(7), 671-675 (2012) https://doi.org/10.1038/nmeth.2089