Influence of heat treatment on the microstructure and the physical and mechanical properties of dental highly translucent zirconia

  • Received : 2022.01.07
  • Accepted : 2022.04.12
  • Published : 2022.04.30

Abstract

PURPOSE. Microstructural and physico-mechanical characterization of highly translucent zirconia, prepared by milling technology (CAD-CAM) and repeated firing cycles, was the main aim of this in vitro study. MATERIALS AND METHODS. Two groups of samples of two commercial highly-translucent yttria-stabilized dental zirconia, VITA YZ-HTWhite (Group A) and Zolid HT + White (Group B), with dimensions according to the ISO 6872 "Dentistry - Ceramic materials", were prepared. The specimens of each group were divided into two subgroups. The specimens of the first subgroups (Group A1 and Group B1) were merely the sintered specimens. The specimens of the second subgroups (Group A2 and Group B2) were subjected to 4 heat treatment cycles. The microstructural features (microstructure, density, grain size, crystalline phases, and crystallite size) and four mechanical properties (flexural strength, modulus of elasticity, Vickers hardness, and fracture toughness) of the subgroups (i.e. before and after heat treatment) were compared. The statistical significance between the subgroups (A1/A2, and B1/B2) was evaluated by the t-test. In all tests, P values smaller than 5% were considered statistically significant. RESULTS. A homogenous microstructure, with no residual porosity and grains sized between 500 and 450 nm for group A and B, respectively, was observed. Crystalline yttria-stabilized tetragonal zirconia was exclusively registered in the X-ray diffractograms. The mechanical properties decreased after the heat treatment procedure, but the differences were not statistically significant. CONCLUSION. The produced zirconia ceramic materials can be safely (i.e., according to the ISO 6872) used in extensive fixed prosthetic restorations, such as substructure ceramics for three-unit prostheses involving the molar restoration and substructure ceramics for prostheses involving four or more units. Consequently, milling technology is an effective manufacturing technology for producing zirconia substructures for dental fixed all-ceramic prosthetic restorations.

Keywords

Acknowledgement

The authors are deeply indebted to Mr Stavros Rontogiannis for designing specimens with Siemens NX 12 software, and to the Dental Laboratory "Laboratory 86" (Nafsikas 12 str., P. Faliro, Athens, Greece) for producing and providing the highly translucent zirconia ceramic specimens exclusively for the needs of this study.

References

  1. Tang Z, Zhao X, Wang H, Liu B. Clinical evaluation of monolithic zirconia crowns for posterior teeth restorations. Medicine (Baltimore) 2019;98:e17385. https://doi.org/10.1097/md.0000000000017385
  2. Barao VA, Gennari-Filho H, Goiato MC, dos Santos DM, Pesqueira AA. Factors to achieve aesthetics in all-ceramic restorations. J Craniofac Surg 2010;21:2007-12. https://doi.org/10.1097/SCS.0b013e3181f535d4
  3. Sen N, Isler S. Microstructural, physical, and optical characterization of high-translucency zirconia ceramics. J Prosthet Dent 2020;123:761-8. https://doi.org/10.1016/j.prosdent.2019.05.004
  4. Chevalier J, Gremillard L, Deville S. Low-temperature degradation of zirconia and implications for biomedical implants annual review of materials research. Annu Rev Mater Res 2007;37:1-2. https://doi.org/10.1146/annurev.matsci.37.052506.084250
  5. Scott HG. Phase relationships in the zirconia-yttria system. J Mater Sci 1975;10:1527-35. https://doi.org/10.1007/BF01031853
  6. Saadaldin SA, Dixon SJ, Costa DO, Rizkallaa AS. Synthesis of bioactive and machinable miserite glass-ceramics for dental implant applications. Dent Mater 2013;29:645-55. https://doi.org/10.1016/j.dental.2013.03.013
  7. Al-Amleh B, Lyons K, Swain M. Clinical trials in zirconia: a systematic review. J Oral Rehabil 2010;37:641-52. https://doi.org/10.1111/j.1365-2842.2010.02094.x
  8. Andreiotelli M, Wenz HJ, Kohal RJ. Are ceramic implants a viable alternative to titanium implants? A systematic literature review. Clin Oral Implants Res 2009;20:32-47. https://doi.org/10.1111/j.1600-0501.2009.01785.x
  9. Al Jabbari YS, Barmpagadaki X, Psarris I, Zinelis S. Microstructural, mechanical, ionic release and tarnish resistance characterization of porcelain fused to metal Co-Cr alloys manufactured via casting and three different CAD-CAM techniques. J Prosthodont Res 2019;63:150-6. https://doi.org/10.1016/j.jpor.2018.10.008
  10. Dimitriadis K, Lekatou AG, Sfikas A, Roumpi M, Tsouli S, Galiatsatos A, Agathopoulos S. Influence of heat-treatment cycles on the microstructure, mechanical properties, and corrosion resistance of co-cr dental alloys fabricated by selective laser melting. J Mater Eng and Perform 2021;30:5252-65. https://doi.org/10.1007/s11665-021-05738-9
  11. Kontonasaki E, Rigos AE, Ilia C, Istantsos T. Monolithic zirconia: an update to current knowledge. optical properties, wear, and clinical performance. Dent J (Basel) 2019;7:90. https://doi.org/10.3390/dj7030090
  12. Griffin JD Jr. Tooth in a bag: same-day monolithic zirconia crown. Dent Today 2013;32:124, 126-31.
  13. ISO 6872. Dentistry - Ceramic materials. 3rd ed., International Standards Organization (ISO); Geneva; Switzerland, 2008.
  14. Montazerian M, Zanotto ED. Bioactive and inert dental glass-ceramics. J Biomed Mater Res A 2017;105:619-39. https://doi.org/10.1002/jbm.a.35923
  15. Tong H, Tanaka CB, Kaizer MR, Zhang Y. Characterization of three commercial Y-TZP ceramics produced for their high-translucency, high-strength and high-surface area. Ceram Int 2016;42:1077-85. https://doi.org/10.1016/j.ceramint.2015.09.033
  16. Dimitriadis K, Papadopoulos T, Agathopoulos S. Effect of bonding agent on metal-ceramic bond strength between co-cr fabricated with selective laser melting and dental feldspathic porcelain. J Prosthodont 2019;28:1029-36. https://doi.org/10.1111/jopr.13058
  17. Sakar-Deliormanli A, Guden M. Microhardness and fracture toughness of dental materials by indentation method. J Biomed Mater Res B Appl Biomater 2006;76:257-64. https://doi.org/10.1002/jbm.b.30371
  18. Zmak I, Coric D, Mandic V, Curkovic L. Hardness and indentation fracture toughness of slip cast alumina and alumina-zirconia ceramics. Materials (Basel) 2019;13:122. https://doi.org/10.3390/ma13010122
  19. Holand W, Beal GH. Glass-ceramic technology. 2nd ed., Westerville; American Ceramic Society; 2002. p. 57-72, 194-227, 282-91.
  20. Stawarczyk B, Ozcan M, Hallmann L, Ender A, Mehl A, Hammerlet CH. The effect of zirconia sintering temperature on flexural strength, grain size, and contrast ratio. Clin Oral Investig 2013;17:269-74. https://doi.org/10.1007/s00784-012-0692-6
  21. Sakaguchi RL, Powers JM. Craig's restorative dental materials. 13th ed., St. Louis; Elsevier; 2012. p. 253-70.
  22. Amat NF, Muchtara A, Amril MS, Ghazali MJ, Yahaya N. Effect of sintering temperature on the aging resistance and mechanical properties of monolithic zirconia. J Mater Res Technol 2019;8:1092-101. https://doi.org/10.1016/j.jmrt.2018.07.017
  23. De Souza GM, Zykus A, Ghahnavyeh RR, Lawrence SK, Bahr DF. Effect of accelerated aging on dental zirconia-based materials. J Mech Behav Biomed Mater 2017;65:256-63. https://doi.org/10.1016/j.jmbbm.2016.08.023
  24. Lucas TJ, Lawson NC, Janowski GM, Burgess JO. Effect of grain size on the monoclinic transformation, hardness, roughness, and modulus of aged partially stabilized zirconia. Dent Mater 2015;31:1487-92. https://doi.org/10.1016/j.dental.2015.09.014
  25. Pekkan G, Saridag S, Pekkan K, Helvacioglu DY. Comparative radiopacity of conventional and full-contour Y-TZP ceramics. Dent Mater J 2016;35:257-63. https://doi.org/10.4012/dmj.2015-194
  26. El-Meliegy E, van Noort R. Glasses and glass ceramics for medical applications. 1st ed., New York; Springer; 2012. p. 109-31.
  27. Baino F, Tomalino M, Tulyaganov D. Ceramics, glass and glass-ceramics. 1st ed., New York; Springer; 2021. p. 153-200.
  28. Denry I, Kelly JR. State of the art of zirconia for dental applications. Dent Mater 2008;24:299-307. https://doi.org/10.1016/j.dental.2007.05.007
  29. Natali AN. Dental biomechanics. 1st ed., London; CRC Press; 2003. p. 50-250.
  30. Lin PJ, Su KC. Biomechanical design application on the effect of different occlusion conditions on dental implants with different positions-a finite element analysis. Appl Sci 2020;10:5826. https://doi.org/10.3390/app10175826
  31. Montazerian M, Dutra Zanotto E. History and trends of bioactive glass-ceramics. J Biomed Mater Res A 2016;104:1231-49. https://doi.org/10.1002/jbm.a.35639
  32. Zhang YR, Du W, Zhou XD, Yu HY. Review of research on the mechanical properties of the human tooth. Int J Oral Sci 2014;6:61-9. https://doi.org/10.1038/ijos.2014.21
  33. Kinney JH, Marshall SJ, Marshall GW. The mechanical properties of human dentin: a critical review and re-evaluation of the dental literature. Crit Rev Oral Biol Med 2003;14:13-29. https://doi.org/10.1177/154411130301400103
  34. Sakaguchi RL, Ferracane J, Powers JM. Craig's restorative dental materials. 14th ed., Philadelphia; Elsevier; 2018. p. 69-80.
  35. Mahoney EK, Rohanizadeh R, Ismail FS, Kilpatrick NM, Swain MV. Mechanical properties and microstructure of hypomineralised enamel of permanent teeth. Biomaterials 2004;25:5091-100. https://doi.org/10.1016/j.biomaterials.2004.02.044
  36. Sola-Ruiz MF, Baima-Moscardo A, Selva-Otaolaurruchi E, Montiel-Company JM, Agustin-Panadero R, FonsBadal C, Fernandez-Estevan L. Wear in antagonist teeth produced by monolithic zirconia crowns: a systematic review and meta-analysis. J Clin Med 2020;9:997. https://doi.org/10.3390/jcm9040997
  37. Esquivel-Upshaw JF, Kim MJ, Hsu SM, Abdulhameed N, Jenkins R, Neal D, Ren F, Clark AE. Randomized clinical study of wear of enamel antagonists against polished monolithic zirconia crowns. J Dent 2018;68:19-27. https://doi.org/10.1016/j.jdent.2017.10.005
  38. Mundhe K, Jain V, Pruthi G, Shah N. Clinical study to evaluate the wear of natural enamel antagonist to zirconia and metal ceramic crowns. J Prosthet Dent 2015;114:358-63. https://doi.org/10.1016/j.prosdent.2015.03.001
  39. Deval P, Tembhurne J, Gangurde A, Chauhan M, Jaiswal N, Tiwari DK. A clinical comparative evaluation of the wear of enamel antagonist to monolithic zirconia and metal-ceramic crowns. Int J Prosthodont 2021;34:744-51. https://doi.org/10.11607/ijp.6598
  40. Fischer H, Marx R. Fracture toughness of dental ceramics: comparison of bending and indentation method. Dent Mater 2002;18:12-9. https://doi.org/10.1016/S0109-5641(01)00005-7
  41. Dimitriadis K, Moschovas, Tulyaganov DU, Agathopoulos S. Glass-ceramics in the CaO-MgO-Al2O3-SiO2 system as potential dental restorative materials. Int J Appl Ceram Technol 2021;18:1938-49. https://doi.org/10.1111/ijac.13836