The Effect of Die Cooling on the Surface Defects of the Aluminum 7075 Extrudates

알루미늄 7075 합금의 압출에서 금형 냉각이 압출재의 표면 결함에 미치는 영향

  • S.Y., Lee (Dept. of Advanced Materials Engineering, Andong National University)
  • 이상용 (국립안동대학교 공과대학 반도체.에너지신소재공학부)
  • Received : 2022.11.07
  • Accepted : 2022.11.22
  • Published : 2022.11.30
Download PDF
⟨ Previous Next ⟩

Abstract

Direct extrusions of an aluminum 7075 alloy were carried out using 1500 ton machine with and without die cooling system. Cooling of extrusion die has been performed by the flow of liquid nitrogen and controlled by laser thermometer. Billet was 180 mm in diameter and 500 mm in length. The preheating temperatures of billet, container and die were 390℃, 400℃ and 450℃, respectively. Ram speed was kept with 1.25 mm/sec first. The change of ram speed was carried out during extrusion according to the observation of surface defects such as crack or tearing. Extrudates of 8.3 m in length, 100 mm in width and 15 mm in thickness were obtained to observe and analyze surface defects by optical microscopy and EBSD (Electron BackScattered Diffraction). In case of extrusion without die cooling cracks on the surface and tearing in the corner of extrudate occurred in the middle stage and developed in size and frequency during the late stage of extrusion. At the extrusion with die cooling the occurrence of defects could be suppressed on the most part of extrudate. EBSD micrographs showed that cracks and tearings have been resulted from the same origin. Surface defects were generated at the boundaries of grains formed by secondary recrystallization due to surface overheating during extrusion.

Keywords

Acknowledgement

이 논문은 안동대학교 기본연구지원사업에 의하여 연구되었습니다.

References

  1. T. Sheppard : Extrusion of Aluminum Alloys, Kluwer Academic Publishers, Dordrecht (1999).
  2. J. Hirsch : Trans. Nonferrous Met. Soc. China, 24 (2014) 1995.
  3. N. Hashimoto : Kobelco Technology Review, 35 (2017) 69.
  4. K. E. Nilsen : PhD Thesis, Bournemouth University (2014).
  5. A. Guzel : PhD Thesis, TU Dortmund (2014).
  6. F. Parvizian, T Kayser, C. Hortig, and B. Svendsen : J. of Mat. Process. Tech. 209 (2009) 876.
  7. V. V. Zakharov : Advanced Performance Materials, 2 (1995) 51.
  8. S. Ngerbamrung, Y. Suzuki, N. Takatsuji, and K. Dohda : Procedia Manufacturing, 15 (2018) 217.
  9. L. Li, J. Zhou, and J. Duszczyk : J. of Mat. Process. Tech. 146 (2004) 203.
  10. S. G. Seong, H. J. Kang, and S. Y. Lee : J. Kor. Soc. Heat Treat. 34 (2021) 186.
  11. S. Y. Lee and Y. H. Woo : J. Kor. Soc. Heat Treat. 31 (2018) 307.
  12. S. Y. Lee : J. Kor. Soc. Heat Treat. 33 (2020) 232.